Experimental characterization of concrete-epoxy interfaces

Journal of Materials in Civil Engineering

Volumn 20, Issue 4, 2008, Pages 303-312

  Coronado, Carlos A ^a,b   Lopez, Maria A ^b  

^a BECHTEL CORPORATION   (United States)

^b The Pennsylvania State University   (United States)

Author keywords

Bonding; Composite materials; Concrete; Cracking; Damage; Interfaces

Indexed keywords

BENDING (DEFORMATION); BONDING; CHARACTERIZATION; CONCRETES; EPOXY RESINS; FIBER REINFORCED PLASTICS; FRACTURE ENERGY; INTERFACES (MATERIALS); TENSILE STRENGTH;

CONCRETE-EPOXY INTERFACE; FIBER REINFORCED POLYMERIC LAMINATES;

LAMINATED COMPOSITES;

CONCRETE; CRACKING; DAMAGE MECHANICS; EXPERIMENTAL STUDY; INSTALLATION; POLYMER;

EID: 41049118139     PISSN: 08991561     EISSN: None     Source Type: Journal    
DOI: 10.1061/(ASCE)0899-1561(2008)20:4(303)     Document Type: Article

References (36)

1. ACI. (2002). "Guide for the design and construction of externally bonded FRP systems for strengthening concrete structures." ACI No. 440.2R-02, American Concrete Institute, 45.
2. ACI. (2007). "Fracture toughness testing of concrete, reported by ACI Committee 446." ACI No. 446.XR, American Concrete Institute (draft report).
3. ASTM. (2005a). "Standard test method for splitting tensile strength of cylindrical concrete specimens." Annual book of ASTM standards, C496/C496M, Vol. 04.02.
4. ASTM. (2005b). "Standard test method for tensile properties of plastics." Annual book of ASTM standards, D638, Vol. 08.01.
5. Bažant, Z. P., and Oh., B. H. (1983). "Crack band theory for fracture of concrete." Mater. Constr. (Paris) MCMSBP0025-543210.1007/BF02486267, 16(3), 155-177.
6. Bažant, Z. P., and Planas, J. (1998). Fracture and size effect in concrete and other quasibrittle materials, CRC, Boca Raton, Fla.
7. Bažant, Z. P., Yu, Q., and Zi, G. (2002). "Choice of standard fracture test for concrete and its statistical evaluation." Int. J. Fract. IJFRAP0376-942910.1023/A:1023399125413, 118(4), 303-337.
8. Bizindavyi, L., and Neale, K. W. (1999). "Transfer lengths and bond strengths for composites bonded to concrete." J. Compos. Constr. JCCOF21090-026810.1061/(ASCE)1090-0268(1999)3:4(153), 3(4), 153-160.
9. Boyajian, D. M., Davalos, J. F., and Ray, I. (2005). "Appraisal of the novel single contoured-cantilever beam." Mater. Struct. MASTED1359-599710.1007/BF02480569, 38(275), 11-16.
10. Buyukozturk, O., Gunes, O., and Karaca, E. (2004). "Progress on understanding debonding problems in reinforced concrete and steel members strengthened using FRP composites." Constr. Build. Mater. CBVME20950-061810.1016/S0950-0618(03)00094-1, 18(1), 9-19..
11. Chajes, M. J., Finch, W. W. J., Januszka, T. F., and Thomson, T. A. J. (1996). "Bond and force transfer of composite material plates bonded to concrete." ACI Struct. J. ASTJEG0889-3241, 93(2), 208-217.
12. Chen, J. F., and Teng, J. G. (2001). "Anchorage strength models for FRP and steel plates bonded to concrete." J. Struct. Eng. JSENDH0733-944510.1061/(ASCE)0733-9445(2001)127:7(784), 127(7), 784-791.
13. Coronado, C. A. (2006). "Characterization, modeling and size effect of concrete-epoxy interfaces." Ph.D. thesis, Pennsylvania State Univ., University Park, Pa.
14. Coronado, C. A., and Lopez, M. M. (2005). "Modeling of FRP-concrete bond using nonlinear damage mechanics." Proc., FRPRCS-7 7th Int. Symp. on Fiber Reinforced Polymer Reinforcement for Reinforced Concrete Structures, Vol. 2, SP-230, American Concrete Institute, Farmington Hills, Mich., 373-390.
15. Coronado, C. A., and Lopez, M. M. (2006). "Sensitivity analysis of reinforced concrete beams strengthened with FRP laminates." Cem. Concr. Compos. CCOCEG0958-946510.1016/j.cemconcomp.2005.07.005, 28(1), 102-114.
16. De Lorenzis, L., Miller, B., and Nanni, A. (2001). "Bond of fiber-reinforced polymer laminates to concrete." ACI Mater. J. AMAJEF0889-325X, 98(3), 256-264.
17. Elices, M., Guinea, G. V., Gomez, J., and Planas, J. (2002). "The cohesive zone model: Advantages, limitations and challenges." Eng. Fract. Mech. EFMEAH0013-794410.1016/S0013-7944(01)00083-2, 69(2), 137-163.
18. Fyfe Co. LLC. (2005-2006). "Fyfe Co. LLC products-Tyfo®Epoxies-Tyfo S, saturant epoxy." 〈http//www.fyfeco.com/products/epoxies/pdf/s.pdf〉 (January 2006).
19. Giurgiutiu, V., Lyons, J., Petrou, M., Laub, D., and Whitley, S. (2001). "Fracture mechanics testing of the bond between composite overlays and a concrete substrate." J. Adhes. Sci. Technol. JATEE80169-424310.1163/15685610152599386, 15(11), 1351-1371.
20. Granju, J.-L., Sabathier, V., Turatsinze, A., and Toumi, A. (2004). "Interface between an old concrete and a bonded overlay: Debonding mechanism." Interface Sci. INSCE90927-705610.1023/ B:INTS.0000042336.03156.cb, 12(4), 381-388.
21. Hillerborg, A. (1985). "Results of three comparative test series for determining the fracture energy GF of concrete." Mater. Struct. MASTED1359-599710.1007/BF02472416, 18(107), 407-413.
22. Hillerborg, A., Modeer, M., and Petersson, P. (1976). "Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements." Cem. Concr. Res. CCNRAI0008-884610.1016/0008-8846(76)90007-7, 6(6), 773-782.
23. Karbhari, V. M., and Engineer, M. (1996). "Investigation of bond between concrete and composites: Use of a peel test." J. Reinf. Plast. Compos. JRPCDW0731-6844, 15(2), 208-227.
24. Lu, X., Teng, J., Ye, L., and Jiang, J. (2005). "Bond-slip models for FRP sheets/plates bonded to concrete." Eng. Struct. ENSTDF0141-029610.1016/j.engstruct.2005.01.014, 27(6), 920-937.
25. Lubliner, J., Oliver, J., Oller, S., and Onate, E. (1989). "Plastic-damage model for concrete." Int. J. Solids Struct. IJSOAD0020-768310.1016/0020-7683(89)90050-4, 25(3), 299-326.
26. McSweeney, B. M., and Lopez, M. M. (2005). "FRP-concrete bond behavior: A parametric study through pull-off testing." Proc., 7th Int. Symp. on Non-Metallic Fiber Reinforced Polymer Composite Reinforcement for Concrete Structures, FRPRCS-7, Vol. 2, SP-230, American Concrete Institute, Farmington Hills, Mich., 441-460.
27. Mukhopadhyaya, P., Swamy, R. N., and Lynsdale, C. J. (1998). "Influence of aggressive exposure conditions on the behaviour of adhesive bonded concrete-GFRP joints." Constr. Build. Mater. CBVME20950-061810.1016/S0950-0618(98)00030-0, 12(8), 427-446.
28. Petersson, P. E. (1981). "Crack growth and development of fracture zones in plain concrete and similar materials." Rep. No. TVBM-1006, Division of Building Materials, Lund Institute of Technology, Lund, Sweden.
29. Planas, J., and Elices, M. (1990). "Fracture criteria for concrete. Mathematical approximations and experimental validation." Proc., Engineering Fracture Mechanics Int. Conf. on Fracture and Damage of Concrete and Rock and Special Seminar on Large Concrete Dam Structures, Pergamon Press, Elmsford, N.Y., Vol. 35(1-3), 87-94.
30. Planas, J., Guinea, G. V., and Elices, M. (1999). "Size effect and inverse analysis in concrete fracture." Int. J. Fract. IJFRAP0376-942910.1023/A:1018681124551, 95(1-4), 367-378.
31. Qiao, P., and Xu, Y. (2004). "Evaluation of fracture energy of composite-concrete bonded interfaces using three-point bend tests." J. Compos. Constr. JCCOF21090-026810.1061/(ASCE)1090-0268(2004)8:4(352), 8(4), 352-359.
32. Rocco, C., Guinea, G. V., Planas, J., and Elices, M. (1999). "Mechanisms of rupture in splitting tests." ACI Mater. J. AMAJEF0889-325X, 96(1), 52-60.
33. Rocco, C., Guinea, G. V., Planas, J., and Elices, M. (2001). "Review of the splitting-test standards from a fracture mechanics point of view." Cem. Concr. Res. CCNRAI0008-884610.1016/ S0008-8846(00)00425-7, 31(1), 73-82.
34. Taljsten, B. (1996). "Strengthening of concrete prisms using the plate-bonding technique." Int. J. Fract. IJFRAP0376-942910.1007/ BF00013161, 82, 253-266.
35. Yao, J., Teng, J. G., and Chen, J. F. (2005). "Experimental study on FRP-to-concrete bonded joints." Composites, Part B CPBEFF1359-836810.1016/j.compositesb.2004.06.001, 36(2), 99-113.
36. Yuan, H., Teng, J. G., Seracino, R., Wu, Z. S., and Yao, J. (2004). "Full-range behavior of FRP-to-concrete bonded joints." Eng. Struct. ENSTDF0141-029610.1016/j.engstruct.2003.11.006, 26(5), 553-565.