SCC of commercial steels exposed to high hydrogen fugacity

Engineering Failure Analysis

Volumn 15, Issue 6, 2008, Pages 617-641

  Villalba, E ^a   Atrens, A ^a,b  

^a UNIVERSITY OF QUEENSLAND   (Australia)

^b SWISS FEDERAL LABORATORIES FOR MATERIALS SCIENCE AND TECHNOLOGY   (Switzerland)

Author keywords

Commercial steel; Hydrogen embrittlement; Linearly increasing stress test; Stress corrosion cracking

Indexed keywords

HYDROGEN EMBRITTLEMENT; PH EFFECTS; STEEL;

COMMERCIAL STEEL; HYDROGEN FUGACITY; STRESS TEST;

STRESS CORROSION CRACKING;

HYDROGEN EMBRITTLEMENT; PH EFFECTS; STEEL; STRESS CORROSION CRACKING;

EID: 40849097706     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfailanal.2007.10.004     Document Type: Article

References (25)

1. Villalba E., and Atrens A. An evaluation of steel subjected to rock bolt SCC conditions. Eng Fail Anal 14 (2007) 1351-1393
2. Gamboa E., and Atrens A. Environmental influence on the stress corrosion cracking of rock bolts. Eng Fail Anal 10 (2003) 521-558
3. Gamboa E., and Atrens A. Stress corrosion cracking fracture mechanisms in rock bolts. J Mater Sci 38 (2003) 3813-3829
4. Gamboa E., and Atrens A. Material influence on the stress corrosion cracking of rock bolts. Eng Fail Anal 12 (2005) 201-225
5. Atrens A., Brosnan C., Ramamurthy S., Oehler A., and Smith I. Linearly increasing stress test (LIST) for SCC research. Meas Sci Technol 4 (1993) 1281-1292
6. Carter T.J., and Cornish L.A. Hydrogen in metals. Eng Fail Anal 8 (2001) 113-121
7. ASTM E 647. Standard test method for measurement of fatigue crack growth rates. ASTM International.
8. Wang J.Q., and Atrens A. Analysis of service stress corrosion cracking in a natural gas transmission pipeline, active or dormant?. Eng Fail Anal 11 (2004) 3-18
9. Wang J., and Atrens A. SCC initiation for X65 pipeline steel in "high" pH carbonate/bicarbonate solution. Corros Sci 45 (2003) 2199-2217
10. Williams J.G., Killmore C.R., Barbaro F.J., Piper J., and Fletcher L. Mater Forum 20 (1996) 13
11. Wang J., and Atrens A. Microstructure and grain boundary microanalysis of X70 pipeline steel. J Mater Sci 38 (2003) 323-330
12. Atrens A., Wang J.Q., Stiller K., and Andren H.O. Atom probe field ion microscope measurements of carbon segregation at an α:α grain boundary and service failures by intergranular stress corrosion cracking. Corros Sci 48 (2006) 79-92
13. Wang J.Q., Atrens A., and Cousens D.R. Boundary characterisation of X65 pipeline steel using analytical electron microscopy. J Mater Sci 34 (1999) 1711-1719
14. Wang J.Q., Atrens A., Cousens D.R., and Kinaev N. Microstructure of X52 and X65 pipeline steels. J Mater Sci 34 (1999) 1721-1728
15. Wang J.Q., Atrens A., Cousens D.R., Kelly P.M., Nockolds C., and Bulcock S. Measurement of grain boundary composition for X52 pipeline steel. Acta Mater 46 (1998) 5677-5687
16. Gamboa E, Villalba E, Atrens A. Stress corrosion cracking of rock bolts. In: Atrens A, Boland JN, Clegg R, Griffiths JR, Australian Fracture Group, editors. Proceedings of an International Conference, Structural integrity fracture, SIF 2004. Brisbane, Australia; 2004. P.127-34. Available from: http://eprint.uq.edu.au/archive/00000836.
17. Winzer N, Atrens A, Dietzel W, Song G, Kainer KU. Comparison of the linearly increasing stress test and the constant extension rate test in the evaluation of transgranular stress corrosion cracking of magnesium. Mater Sci Eng A 2007; doi:10.1016/j.msea.2007.03.021.
18. Oehlert A., and Atrens A. SCC propagation in Aermet 100. J Mater Sci 33 (1998) 775-781
19. Oehlert A., and Atrens A. Environmental assisted fracture for 4340 steel in water and air of various humidities. J Mater Sci 32 (1997) 6519-6523
20. Oehlert A., and Atrens A. Initiation and propagation of stress corrosion cracking in AISI 4340 and 3.5NiCrMoV rotor steel in constant load tests. Corros Sci 38 (1996) 1159-1170
21. 3 and in Bayer liquor. J Mater Sci 33 (1998) 783-788
22. Oehlert A., and Atrens A. Overview No 114 room temperature creep of high strength steels. Acta Metall Mater 42 (1994) 1493-1508
23. Wang Z.F., and Atrens A. Initiation of stress corrosion cracking for pipeline steels in a carbonate-bicarbonate solution. Metall Mater Trans 27A (1996) 2686-2691
24. Ramamurthy S., and Atrens A. The stress corrosion cracking of as-quenched 4340 and 3.5NiCrMoV steels under stress rate control in distilled water at 90 °C. Corros Sci 34 (1993) 1385-1402
25. Salmond J., and Atrens A. SCC of copper using the linearly increasing stress test. Scripta Metall Mater 26 (1992) 1447-1450