Engineering Fracture Mechanics

Volumn 75, Issue 9, 2008, Pages 2695-2706

Deformation behaviour of elastomeric matrix composites under static loading conditions

(3) Bayraktar, E a Bessri, K a Bathias, C a

a ITMA School of Mechanical and Manufacturing Engineering (France)

Author keywords

Damage mechanism; Fracture of elastomeric composites; Pancake specimen; SEM; X ray computed tomography

Indexed keywords

CONTINUUM DAMAGE MECHANICS; CRACK INITIATION; CRACK PROPAGATION; DEFECTS; DEFORMATION; ELASTOMERS; FAILURE ANALYSIS; FRACTURE MECHANICS; LOADS (FORCES);

ELASTOMERIC MATRIX COMPOSITES; STATIC LOAD;

POLYMER MATRIX COMPOSITES;

CONTINUUM DAMAGE MECHANICS; CRACK INITIATION; CRACK PROPAGATION; DEFECTS; DEFORMATION; ELASTOMERS; FAILURE ANALYSIS; FRACTURE MECHANICS; LOADS (FORCES); POLYMER MATRIX COMPOSITES;

EID: 40649111147 PISSN: 00137944 EISSN: None Source Type: Journal
DOI: 10.1016/j.engfracmech.2007.03.016 Document Type: Article

Times cited : (28)

References (9)

1
- 0001441436
- Rupture of rubber. I. Characteristics energy for tearing
- Rivlin R.S., and Thomas A.G. Rupture of rubber. I. Characteristics energy for tearing. J Polym Sci 10 (1953) 291-318
- (1953) J Polym Sci , vol.10 , pp. 291-318
- Rivlin, R.S.¹ Thomas, A.G.²

2
- 0035870540
- Cavitation instability in rubber with consideration of failure
- Chang W.J., and Pan J. Cavitation instability in rubber with consideration of failure. J Mater Sci 36 (2001) 1901-1909
- (2001) J Mater Sci , vol.36 , pp. 1901-1909
- Chang, W.J.¹ Pan, J.²

3
- 0343992507
- Effects of hydrostatic pressure on crack growth in elastomers
- Lake G.J., Thomas A.G., and Lawrence C.C. Effects of hydrostatic pressure on crack growth in elastomers. Polymer 33 19 (1992) 4069-4074
- (1992) Polymer , vol.33 , Issue.19 , pp. 4069-4074
- Lake, G.J.¹ Thomas, A.G.² Lawrence, C.C.³

4
- 33745938736
- Multiscale observation of fatigue behaviour of elastomeric matrix and metal matrix composites by X-ray tomography
- Bayraktar E., Antolovich S., and Bathias C. Multiscale observation of fatigue behaviour of elastomeric matrix and metal matrix composites by X-ray tomography. Int J Fatigue 28 10 (2006) 1322-1333
- (2006) Int J Fatigue , vol.28 , Issue.10 , pp. 1322-1333
- Bayraktar, E.¹ Antolovich, S.² Bathias, C.³

5
- 40649111324
- Piras R. Mechanical test of elastomeric materials. MSc - ITMA, Supmeca/LISMMA Paris; 2003. p. 15-21.
- Piras R. Mechanical test of elastomeric materials. MSc - ITMA, Supmeca/LISMMA Paris; 2003. p. 15-21.

6
- 40649091799
- Luong R. Damage mechanism in elastomeric composites. MSc, ITMA, Supmeca/LISMMA Paris; 2004. p. 40-52.
- Luong R. Damage mechanism in elastomeric composites. MSc, ITMA, Supmeca/LISMMA Paris; 2004. p. 40-52.

7
- 4344713142
- Determination of critical tearing energy of tire rubber
- Gdoutos E.E., Schubel P.M., and Daniel I.M. Determination of critical tearing energy of tire rubber. Strain 40 (2004) 119-125
- (2004) Strain , vol.40 , pp. 119-125
- Gdoutos, E.E.¹ Schubel, P.M.² Daniel, I.M.³

8
- 0000380706
- Failure mechanics in elastomeric toughened polypropylene
- Jancar J., Dianselmo A., and Dibenedetto A.T. Failure mechanics in elastomeric toughened polypropylene. Polymer 34 8 (1993) 1684-1694
- (1993) Polymer , vol.34 , Issue.8 , pp. 1684-1694
- Jancar, J.¹ Dianselmo, A.² Dibenedetto, A.T.³

9
- 16644367293
- Multiscale observation of polymer materials in order to explain mechanical behaviour and damage mechanism by X-ray computed tomography
- Bayraktar E., Montembault F., and Bathias C. Multiscale observation of polymer materials in order to explain mechanical behaviour and damage mechanism by X-ray computed tomography. J Mater Sci Technol 20 1 (2004) 27-31
- (2004) J Mater Sci Technol , vol.20 , Issue.1 , pp. 27-31
- Bayraktar, E.¹ Montembault, F.² Bathias, C.³

* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.