Mesoporous polymer nanofibers by infiltration of block copolymers with sacrificial domains into porous alumina

Chemistry of Materials

Volumn 20, Issue 2, 2008, Pages 379-381

  Wang, Yong ^a   Gösele, Ulrich ^a   Steinhart, Martin ^a  

^a MAX PLANCK INSTITUTE OF MICROSTRUCTURE PHYSICS   (Germany)

Author keywords

[No Author keywords available]

Indexed keywords

COPOLYMERS; INFILTRATION; IRRADIATION; MESOPOROUS MATERIALS; SCAFFOLDS;

MICROPHASE-SEPERATED BLOCK COPOLYMERS (BCPS); POLYMERIC SCAFFOLD; POROUS ALUMINA;

NANOFIBERS;

EID: 38949151561     PISSN: 08974756     EISSN: None     Source Type: Journal    
DOI: 10.1021/cm703126r     Document Type: Article

References (37)

1. Yang, Z.; Niu, Z.; Cao, X.; Yang, Z.; Lu, Y.; Hu, Z.; Han, C. C. Angew. Chem., Int. Ed. 2003, 42, 4201-4203.
2. Lu, Q.; Gao, F.; Komarneni, S.; Chan, M.; Mallouk, T. E. J. Am. Chem. Soc. 2004, 126, 8650-8651.
3. Wu, Y.; Cheng, G.; Katsov, K.; Sides, S. W.; Wang, J.; Tang, J.; Fredrickson, G. H.; Moskovits, M.; Stocky, G. D. Nat. Mater. 2004, 3, 816-822.
4. Chen, X.; Steinhart, M.; Hess, C.; Gösele, U. Adv. Mater. 2006, 18, 2153-2156.
5. Chen, X.; Knez, M.; Berger, A.; Nielsch, K.; Gösele, U.; Steinhart, M Angew. Chem., Int. Ed. 2007, 46, 6829-6832.
6. Steinhart, M.; Liang, C. D.; Lynn, G. W.; Gösele, U.; Dai, S. Chem. Mater. 2007, 19, 2383.
7. Xiang, H. Q.; Shin, K.; Kim, T.; Moon, S. I.; McCarthy, T. J.; Russell, T. P. Macromolecules 2004, 37, 5660.
8. Sun, Y.; Steinhart, M.; Zschech, D.; Adhikari, R.; Michler, G. H.; Gösele, U. Macromol. Rapid Commun. 2005, 26, 369.
9. Masuda, H.; Fukuda, K. Science 1995, 268, 1466-1468.
10. Masuda, H.; Yada, K.; Osaka, A. Jpn. J. Appl. Phys., Part 2 1998, 37, L1340-L1342.
11. Stewart, S.; Liu, G. Angew. Chem., Int. Ed. 2000, 39, 340-344.
12. Shimizu, T.; Masuda, M.; Minamikawa, H. Chem. Rev. 2005, 105, 1401-1443.
13. Thurn-Albrecht, T.; Steiner, R.; DeRouchey, J.; Stafford, C. M.; Huang, E.; Bal, M.; Tuominen, M.; Hawker, C. J.; Russell, T. P. Adv. Mater. 2000, 12, 787-791.
14. Bohlen, J.; Kirchheim, R. Macromolecules 2001, 34, 4210-4215.
15. Kim, E.; Xia, Y.; Whitesides, G. M. Nature 1995, 376, 581.
16. Kriha, O.; Zhao, L.; Pippel, E.; Gösele, U.; Wehrspohn, R. B.; Wendorff, J. H.; Steinhart, M.; Greiner, A. Adv. Funt. Mater. 2007, 17, 1327-1332.
17. The sample shown in Figure 2f had been kept for 24 h at 220°C before it was cooled to room temperature. However, we could not substantiate a systematic dependence of the morphology type on the annealing time that was varied between 10 and 48 h.
18. The samples were irradiated with UV light for 30 min, using a 254 nm UV bench lamp (XX-15S, UVP, Inc; only one of the two available tubes was used to reduce the irradiation strength). Typically, the samples were then kept in acetic acid for 12 h.
19. Hajduk, D.; Harper, P.; Gruner, S.; Honeker, C.; Kim, G.; Thomas, E.; Fetters, L. Macromolecules 1994, 27, 4063-4075.
20. Förster, S.; Khandpur, A. K.; Zhao, J.; Bates, F. S.; Hamley, I. W.; Ryan, A. J.; Bras, W. Macromolecules 1994, 27, 6922-6935.
21. The samples were coated with a thin layer of Au/Pd alloy and probed with a JEOL JSM 6340F SEM operated at 10 keV.
22. Suspensions of released nanofibers were dropped onto TEM grids coated with a holey carbon film and probed with a JEOL 1010 TEM operated at 100 keV.
23. Fredrickson, G. H. Macromolecules 1987, 20, 2535-2542.
24. Henkee, C. S.; Thomas, E. L.; Fetters, L. J. J. Mater. Sci. 1988, 23, 1685-1694.
25. Coulon, G.; Russell, T. P.; Deline, V. R.; Green, P. F. Macromolecules 1989, 22, 2581-2589.
26. Turner, M.; Rubinstein, M.; Marques, C. Macromolecules 1994, 27, 4986-4992.
27. Hamley, I. W.; Koppi, K. A.; Rosedale, J. H.; Bates, F. S.; Almdal, K.; Mortensen, K. Macromolecules 1993, 26, 5959-5970.
28. Hajduk, D. A.; Takenouchi, H.; Hillmyer, M. A.; Bates, F. S.; Vigild, M. E.; Almdal, K. Macromolecules 1997, 30, 3788-3795.
29. Hajduk, D. A.; Ho, R. M.; Hillmyer, M. A.; Bates, F. S.; Almdal, K. J. Phys. Chem. B 1998, 102, 1356-1363.
30. Vigild, M. E.; Almdal, K.; Mortensen, K.; Hamley, I. W.; Fairclough, J. P. A.; Ryan, A. J. Macromolecules 1998, 31, 5702-5716.
31. Park, I.; Park, S.; Park, H. W.; Chang, T.; Yang, H. C.; Ryu, C. Y. Macromolecules 2006, 39, 315-318.
32. Shin, K.; Xiang, H. Q.; Moon, S. I.; Kim, T.; McCarthy, T. J.; Russell, T. P. Science 2004, 306, 76.
33. Xiang, H.; Shin, K.; Kim, T.; Moon, S. I.; McCarthy, T. J.; Russell, T. P. Macromolecules 2005, 38, 1055-1056.
34. Yu, B.; Sun, P.; Chen, T.; Jin, Q.; Ding, D.; Li, B. Phys. Rev. Lett. 2006, 96, 138306.
35. Li, W.; Wickham, R. A.; Garbary, R. A. Macromolecules 2006, 39, 806-811.
36. Chen, P.; Liang, H.; Shi, A.-C. Macromolecules 2007, 40, 7329-7335.
37. Zalusky, A. S.; Olayo-Valles, R.; Wolf, J. H.; Hillmyer, M. A. J. Am. Chem. Soc. 2002, 124, 12761-12773.