Chloride-induced reinforcement corrosion and concrete cracking simulation

Cement and Concrete Composites

Volumn 30, Issue 3, 2008, Pages 227-238

  Chen, Dong ^a   Mahadevan, Sankaran ^a  

^a VANDERBILT UNIVERSITY   (United States)

Author keywords

Chloride penetration; Cracking; Durability; Reinforcement corrosion; Rust expansion; Service life

Indexed keywords

COMPUTER SIMULATION; CRACK INITIATION; DURABILITY; FINITE ELEMENT METHOD; REINFORCEMENT; SERVICE LIFE;

CHLORIDE PENETRATION; REINFORCEMENT CORROSION; RUST EXPANSION;

STRESS CORROSION CRACKING;

EID: 38149088814     PISSN: 09589465     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.cemconcomp.2006.10.007     Document Type: Article

References (46)

1. Page C.L., and Treadaway K.W.J. Aspects of electrochemistry of steel in concrete. Nature 297 (1982) 109-115
2. Townsend H.E., Cleary H.J., and Allegra L. Breakdown of oxide films in steel exposure to chloride solutions. NACE Corros 37 (1981) 384-391
3. Verbeck G.J. Mechanism of corrosion in concrete. Corrosion of metals in concrete (1975), ACI SP-49
4. Mehta P.K. Concrete structure properties and materials (1993), Prentice-Hall, Inc.
5. Liu Y., and Weyers R.E. Modeling the time-to-corrosion cracking in chloride contaminated reinforced concrete structures. ACI Mater J 95 6 (1998) 675-681
6. Tuutti K. Corrosion of steel in concrete (1982), Swedish Cement and Concrete Research Institute, Stochkolm, Sweden
7. Cady P.D., and Weyers R.E. Chloride penetration and the deterioration of concrete bridge decks. Cement Concr Aggr 5 2 (1983) 81-87
8. Bazant Z.P. Physical model for steel corrosion in sea structures - theory. J Struct Div June (1979) 1137-1153
9. Bazant Z.P. Physical model for steel corrosion in sea structures - applications. J Struct Div June (1979) 1153-1166
10. Morinaga S. Prediction of service lives of reinforced concrete buildings based on rate of corrosion of reinforcing steel. In: Proceedings of building materials and components, Brighton, UK; 1990. p. 5-16.
11. Xi Y., and Bazant Z.P. Modeling chloride penetration in saturated concrete. J Mater Civil Eng 11 1 (1999) 58-65
12. Martin-Perez B., Zibara H., Hooton R.D., and Thomas M.D.A. A study of the effect of chloride binding on service life prediction. Cement Concr Res 30 8 (2000) 1215-1223
13. Nilsson L.O., Massat M., and Tang L. Chloride binding capacity and binding isotherms of OPC pastes and mortars. Cement Concr Res 23 2 (1993) 247-253
14. Onyejekwe O.O., and Reddy N. A numerical approach to the study of chloride ion penetration into concrete. Mag Concr Res 52 4 (2000) 243-250
15. Snyder KA. Validation and modification of the 4SIGHT Computer Program. NISTIR 6747; 2001.
16. Martin-Perez B., Pantazopoulou S.J., and Thomas M.D.A. Numerical solution of mass transport equations in concrete structures. Comput Struct 79 13 (2001) 1251-1264
17. Kong J.S., Ababneh A.N., Frangopol D.M., and Xi Y. Reliability analysis of chloride penetration in saturated concrete. Probabilist Eng Mech 17 3 (2002) 305-315
18. Schiessl P. Corrosion of steel in concrete. RILEM Technical Committee 60-CSC (1988), Chapman and Hall, New York
19. Elsener B. Corrosion of steel in concrete. In: Schutze M. (Ed). Corrosion and environmental degradation vol. II (2000), Wiley-VCH Weinheim 389-436
20. Pantazopoulou S.J., and Papoulia K.D. Modeling cover-cracking due to reinforcement corrosion in RC structures. J Eng Mech 127 4 (2001) 342-351
21. Thoft-Christensen P. Stochastic modeling of the crack initiation time for reinforced concrete structures. In: Proceedings of 2000 ASCE structures congress, Philadelphia, USA; 2000.
22. Jung W.Y., Yoon Y.S., and Sohn Y.M. Predicting the remaining service life of land concrete by steel corrosion. Cement Concr Res 33 5 (2003) 663-677
23. Andrade C., Alonso C., and Molina F.J. Covering cracking as a function of rebar corrosion: Part I - experimental test. Mater Struct 26 (1993) 453-464
24. Hansen EJ, Saouma VE. Numerical simulation of reinforced concrete deterioration: Part II - steel corrosion and concrete cracking. ACI Mater J, Title no. 96-M41, 1999;331-7.
25. Hong H.P. Assessment of reliability of aging reinforced concrete structures. ASCE J Struct Eng 126 12 (2000) 1458-1465
26. Stewart M.G., and Rosowsky D.V. Time-dependent reliability of deteriorating reinforced concrete bridge decks. Struct Safety 20 1 (1998) 91-109
27. Liu Y., and Weyers R.E. Modeling the dynamic corrosion process in chloride contaminated concrete structures. Cement Concr Res 28 3 (1998) 365-379
28. Liu Y. Modeling the time-to-corrosion cracking of the cover concrete in chloride contaminated reinforced concrete structures. Ph.D. dissertation, Virginia Polytechnic Institute; 1996.
29. Thoft-Christensen P. Estimation of the service life time of concrete bridges. In: Proceedings of ASCE structures congress XV, Portland OR, USA; 1997.
30. Thoft-Christensen P. Corrosion crack based assessment of the life-cycle reliability of concrete structures. In: Proceedings of ICOSSAR'01, Newport Beach, CA, USA; 2001.
31. Thoft-Christensen P. What happens with reinforced concrete structures when the reinforcement corrodes? In: Proceedings of the 2nd international workshop on "Life-cycle cost analysis and design of civil infrastructure systems", Ube, Yamaguchi, Japan; 2001. p. 35-46.
32. Shah S.P., Swartz S.E., and Ouyang C. Fracture mechanics of concrete (1995), Wiley, New York
33. Bazant Z.P., and Planas J. Fracture and size-effect in concrete and quasi-brittle materials (1998), CRC Press, Boca Raton and London
34. Darwin D. Reinforced concrete. Finite element analysis of reinforced-concrete. Structures vol. II: Proceedings of the international workshop (1993), ASCE, New York 203-232
35. Mandke JS, Smalley AJ. Parameter studies for enhanced integrity of reciprocating compressor foundation blocks. Mechanical and fluids engineering division, Southwest Research Institute. Technical Report No. TA 94-1; 1994.
36. Kachlakev D, Miller T, Yim S. Finite element modeling of reinforced concrete structures strengthened with FRP laminates. Final Report SPR 316 for Oregon Department of Transportation and Federal Highway Administration; 2001.
37. Saouma V.E., and Chang S.-Y. Numerical simulation of reinforced concrete deterioration due to steel corrosion, freezing-thawing and mechanical load effects. In: Frangopol D.M., Bruhwiler E., Faber M.H., and Adey B. (Eds). Life-cycle performance of deteriorating structures: assessment, design and management (2003), ASCE
38. ANSYS. ANSYS 7.0 Help, ANSYS Inc., Canonsburg, PA; 2002.
39. Desayi P., and Krishnan S. Equation for stress strain curve of concrete. J Am Concr Instit 61 (1964) 345-350
40. Hognestad EA. A study of combined bending and axial load in reinforced concrete members. Bulletin No. 399, Engineering Experiment Station, University of Illinois, Urbana, IL, vol. 49 (22); 1951.
41. Willam K.J., and Warnke E.P. Constitutive model for the triaxial behavior of concrete. Proceedings international association for bridge and structural engineering vol. 19 (1975), ISMES, Bergamo Italy 174
42. Schiessl P., and Raupach M. Influence of concrete composition and microclimate on the critical chloride content in concrete. In: Page C.L., Threadaway K.W.J., and Bamforth P.B. (Eds). Corrosion of Reinforcement in Concrete (1990), Society of Chemical Industry, Elsevier Applied Science, London 49-58
43. Hansson C.M., and Sorensen B. Threshold concentration of chloride in concrete for the initiation of reinforcement corrosion. In: Berke N.S., Chaker V., and Whiting D. (Eds). Corrosion rates of steel in concrete. ASTM STP 1065 (1990), American Society for Testing and Materials, Philadelphia, PA 3-16
44. Berman H.A. Sodium chloride corrosion of reinforcing steel and the pH of calcium hydroxides solution. ACI J (1975) 587-598
45. Clear KC. Chloride at the threshold. Report of Kenneth C. Clear Inc.; 1983. p. 1011.
46. Dagher HJ, Kulendran S. Finite element modeling of corrosion damage in concrete structures. ACI Struct J, Title no. 89-S67, 1992;699-708.