Effects of silica fume addition and water to cement ratio on the properties of high-strength concrete after exposure to high temperatures

Cement and Concrete Composites

Volumn 30, Issue 2, 2008, Pages 106-112

  Behnood, Ali ^a   Ziari, Hasan ^a  

^a IRAN UNIVERSITY OF SCIENCE AND TECHNOLOGY   (Iran)

Author keywords

Compressive strength; High temperature; High strength concrete; Mixture proportioning; Silica fume

Indexed keywords

CEMENTS; COMPRESSIVE STRENGTH; CONCRETES; HIGH TEMPERATURE EFFECTS; WATER;

HIGH STRENGTH CONCRETES; MIXTURE PROPORTIONING;

SILICA FUME;

EID: 37448998625     PISSN: 09589465     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.cemconcomp.2007.06.003     Document Type: Article

References (18)

1. ACI committee 363. State-of-the-art report on high-strength concrete (1993), American Concrete Institute, Detroit
2. ACI committee 363. Guide for the use of silica fume in concrete (1994), American Concrete Institute, Detroit
3. Malhotra V.M. Fly ash, slag, silica fume, and rice-husk ash in concrete: a review. Concrete Int 15 (1993) 23-28
4. Hertz K.D. Danish investigations on silica fume concretes at elevated temperatures. ACI Mater J 89 4 (1992) 345-347
5. Hertz KD. Heat-induced explosion of dense concretes. Report No. 166, Institute of Building Design, Technical University of Denmark, Lyngby; 1984.
6. Phan L.T., and Carino N.J. Effects of test conditions and mixture proportions on behaviour of high-strength concrete exposed to high temperatures. ACI Mater J 99 1 (2002) 54-66
7. Sarshar R., and Khoury G.A. Material and environmental factors influencing the compressive strength of unsealed cement paste and concrete at high temperatures. Mag Concrete Res 45 162 (1993) 51-61
8. Poon C., Azhar S., Anson M., and Wong Y. Comparison of the strength and durability performance of normal and high-strength pozzolanic concretes at elevated temperatures. Cement Concrete Res 31 (2001) 1291-1300
9. Hammer TA. High strength concrete phase 3. compressive strength and e-modulus at elevated temperatures, SP 6 Fire Resistance, Report 6.1, SINTEF Structures and concretes, STF 70 A95023; 1995.
10. Felicetti R., and Gambarova P.G. Effects of high temperature on the residual compressive strength of high-strength siliceous concretes. ACI Mater J 95 4 (1998) 395-406
11. Chan S.Y.N., Peng G.F., and Anson M. Fire behaviour of high-performance concrete made with silica fume at various moisture contents. ACI Mater J 96 3 (1999) 405-411
12. Parrott L.J. Production and properties of high-strength concrete. Concrete 3 11 (1969) 443-448
13. Hoff G., Bilodeau A., and Malhotra V.M. Elevated temperature effects on HSC residual strength. Concrete Int 22 4 (2000) 41-47
14. Janotka I., and Bagel L. Pore structures, permeabilities, and compressive strength of concrete at temperatures up to 800 °C. ACI Mater J 99 2 (2002) 196-200
15. Lawson J.R., Phan L.T., and Davis F. Mechanical properties of high-performance concrete after exposure to elevated temperatures (2000), Building and Fire Research Laboratory, National Institute of Standards and Technology, Maryland
16. Bartlett FM, MacGregor JG. Assessment of concrete strength in existing structures. Structural Engineering Report No.198, University of Alberta, Edmonton, Canada; 1994.
17. Castillo C., and Durrani A.J. Effect of transient high temperature on high-strength concrete. ACI Mater J 87 1 (1990) 47-53
18. Sanjayan G., and Stocks L.J. Spalling of high-strength silica fume concrete in fire. ACI Mater J 90 2 (1993) 170-173