Bulk glass formation in ternary Cu-Zr-Ti system

Journal of University of Science and Technology Beijing: Mineral Metallurgy Materials (Eng Ed)

Volumn 14, Issue SUPPL. 1, 2007, Pages 19-22

  Men, Hua ^a   Fu, Junying ^a   Ma, Chaoli ^a   Pang, Shujie ^a   Zhang, Too ^a  

^a BEIHANG UNIVERSITY   (China)

Author keywords

bulk metallic glass; eutectics; glass forming ability; Laves phase

Indexed keywords

EUTECTICS; METAL MOLDING; METALLIC GLASS; NUCLEATION; PHASE DIAGRAMS; TERNARY ALLOYS; UNDERCOOLING;

GLASS FORMING ABILITY; LAVES PHASE; MOLD CASTING METHOD; UNDERCOOLED LIQUID;

COPPER ALLOYS;

EID: 36148941019     PISSN: 10058850     EISSN: None     Source Type: Journal    
DOI: 10.1016/S1005-8850(07)60100-5     Document Type: Article

References (10)

1. Tumbull D. Under what conditions can a glass be formed. Contemp. Phys. 10 (1969) 473
2. Inoue A., Kato A., Zhang T., Kim S.G., and Masumoto T. Mg-Cu-Y amorphous alloys with high mechanical strengths produced by a metallic mold casting method. Mater. Trans., JIM 32 7 (1991) 609
3. 10 bulk metallic glass forming liquid. J. Appl. Phys. 83 8 (1998) 4134
4. Nishiyama N., and Inoue A. Stability and nucleation behavior of glass-forming Pd-Cu-Ni-P alloy with a critical cooling rate of 0.067 K/s. Intermetallics 10 11-12 (2002) 1141
5. Zhang T., and Inoue A. Bulk glassy alloys with low liquidus temperature in Pt-Cu-P system. Mater. Trans. 44 6 (2003) 1143
6. Xu D.H., Duan G., and Johnson W.L. Unusual glass-forming ability of bulk amorphous alloys based on ordinary metal copper. Phys. Rev. Lett. 92 24 (2004) 245504
7. Lu Z.P., Liu C.T., Thompson J.R., and Porter W.D. Structural amorphous steels. Phys. Rev. Lett. 92 24 (2004) 245503
8. Inoue A., Zhang W., Zhang T., and Kurosaka K. Thermal and mechanical properties of Cu-based Cu-Zr-Ti bulk glassy alloys. Mater. Trans. 42 6 (2001) 1149
9. Inoue A., Zhang W., Zhang T., and Kurosaka K. High-strength Cu-based bulk glassy alloys in Cu-Zr-Ti and Cu-Hf-Ti ternary systems. Acta Mater. 49 5 (2001) 2645
10. x alloys. Mater. Sci. Eng., A 408 1-2 (2005) 326