Analysis of endurance limits under very high cycle fatigue using a unified damage approach

International Journal of Fatigue

Volumn 29, Issue 9-11, 2007, Pages 2060-2071

  Sadananda, K ^a   Vasudevan, A K ^b   Phan, N ^c  

^a Technical Data Analysis Inc   (United States)

^b OFFICE OF NAVAL RESEARCH   (United States)

^c NAVAL AIR SYSTEMS COMMAND   (United States)

Author keywords

Crack nucleation; Crack propagation; Dual stage fatigue; Endurance limits; Fatigue thresholds; Giga cycle fatigue; The unified approach; Very high cycle fatigue

Indexed keywords

CRACK PROPAGATION; NUCLEATION; RESIDUAL STRESSES; STRESS CONCENTRATION; SURFACE ANALYSIS;

CRACK NUCLEATION; DUAL-STAGE FATIGUE; ENDURANCE LIMITS; FATIGUE THRESHOLDS; GIGA-CYCLE FATIGUE; VERY HIGH CYCLE FATIGUE;

FATIGUE OF MATERIALS;

EID: 34548140126     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2007.02.028     Document Type: Article

References (46)

1. Bathias C, editor. Fatigue life in the giga cycle regime. EUROMECH 382, Paris, France, June 29-July 1, 1998.
2. In: Stanzl-Tschegg S., and Mayer H. (Eds). Fatigue in the very high cycle regime (2001), BOKU, Vienna, Austria
3. Murakami Y. Special sessions: giga-cycle fatigue. In: Bloom A.F. (Ed). FATIGUE 2002 (2002), EMAS 2927-2987
4. Sakai T, Ochi Y, editors. Very high cycle fatigue. Kusatsu, Japan, September 16-19, 2004.
5. Murakami Y. Metal fatigue: effects of small defects and nonmetallic inclusions (2002), Elsevier
6. Bathias C., and Paris P.C. Giga cycle fatigue in mechanical practice (2005), Marcel Dekker, New York
7. Mughrabi H. Fatigue Fract Eng Mater Struct 22 (2002) 755-764
8. Murakami Y. Mechanism of fatigue failure in ultra long life regime. In: Stanzl-Tschegg S., and Mayer H. (Eds). Fatigue in the very high cycle regime (2001), Institute of Meteorology and Physics, Austria
9. Tanaka K., and Akiniwa Y. Fatigue crack propagation behavior derived from S-N data in very high cycle regime. In: Stanzl-Tschegg S., and Mayer H. (Eds). Fatigue in the very high cycle regime (2001), BOKU, Austria 61-72
10. Sakai T., Sato Y., and Oguma N. Characteristic S-N property of high carbon chromium bearing steel under axial loading in long life fatigue. In: Stanzl-Tschegg S., and Mayer H. (Eds). Fatigue in the very high cycle regime (2001), BOKU, Austria 51-57
11. Vasudevan A.K., Sadananda K., and Louat N. Mater Sci Eng A188 (1994) 1-22
12. Sadananda K, Vasudevan AK. Short crack growth behavior. In: Piascik RS, editor. Fatigue and fracture mechanics, ASTM-STP 1296; 1997. p. 301-16.
13. Sadananda K., and Vasudevan A.K. Int J Fatigue 25 (2003) 899-914
14. Sadananda K., and Vasudevan A.K. Acta Mater 52 (2004) 4239-4249
15. Suresh S. Fatigue of materials. 2nd ed. (1998), Cambridge, New York
16. Kitagawa H., and Takahashi S. Symposium on second international conference on mechanical behavior of materials (1976), American Society of Metals, Metals Park p. 627-31
17. Feltner C.E., and Laird C. Acta Metall 15 (1967) 1621-1633
18. Usami S. In: Blacklund I., Bloom A., and Beevers C.J. (Eds). Symposium on fatigue threshold (1981), EMAS, Stockholm, Sweden 205-238
19. Basinski Z.S., and Basinski S.J. Progr Mater Sci 36 (1992) 89-148
20. Lynch S.P. Acta Metall 20 (1988) 2639-2661
21. Birnbaum H.K., Robertson I.M., Sofronis P., and Teter D. In: Magnin T. (Ed). Corrosion deformation interactions (1997), Institute of Materials, UK 172-195
22. Noroozi A.H., Glinka G., and Lambert S. Int J Fatigue 27 (2005) 1277-1296
23. Vasudevan A.K., Sadananda K., and Glinka G. Int J Fatigue 23 (2001) S39-S53
24. Vasudevan A.K., and Sadananda K. Int J Fatigue 23 (2001) S365-S374
25. Sadananda k., Vasudevan A.K., Holtz R.L., and Lee E.U. Int J Fatigue 21 (1999) S233-S246
26. Vasudevan A.K., Sadananda K., and Holtz R.L. Int J Fatigue 27 (2005) 1519-1529
27. Murakami Y., and Endo M. Eng Fract Mech 17 (1983) 1
28. Tanaka K., and Nakai Y. Fatigue Eng Mater Struct 6 (1985) 315
29. Kujawski D. Estimation of stress intensity factors for small cracks at notches. Fatigue Fract Eng Struct 14 (1991) 953-964
30. El Hadad MH, Smith KN, Topper TH. In: Fracture mechanics. ASTM STP-668, 1979. p. 703-19.
31. Yamabe J., Kobayashi M., and Nakajima N. VHCF-3, Proceedings of the 3rd international conference on very high cycle fatigue. In: Sakai T., and Ochi Y. (Eds) (2004), Society of Material Science, Japan 40-147
32. Mughrabi H. Specific features and mechanisms of fatigue in the ultrahigh cycle regime. In: Sakai T., and Ochi Y. (Eds). VHCF-3 Proceedings of the 3rd international conference on very high cycle fatigue (2004), Society of Material Science, Japan 14-23
33. Tao H., and Xue H. Very high cycle properties for Al-alloys. In: Sakai T., and Ochi Y. (Eds). VHCF-3, Proceedings of the 3rd international conference on very high cycle fatigue (2004), Society of Material Science, Japan 413-419
34. Ueda T., Mohri M., and Suzuki A. Very high cycle fatigue behavior of smooth and notched specimen for low alloy steel. In: Sakai T., and Ochi Y. (Eds). VHCF-3, Proceedings of the 3rd international conference on very high cycle fatigue (2004), Society of Material Science, Japan 427-433
35. Morrissey R., and Nicholas T. Staircase testing of a titanium alloy in the giga cycle regime. In: Sakai T., and Ochi Y. (Eds). VHCF-3, Proceedings of the 3rd international conference on very high cycle fatigue (2004), Society of Material Science, Japan 156-162
36. 2 + γ) Ti-Al alloy. In: Sakai T., and Ochi Y. (Eds). VHCF-3, Proceedings of the 3rd international conference on very high cycle fatigue (2004), Society of Material Science, Japan 440-447
37. Nakamura T., Oguma H., Yokomaya S., and Noguchi T. Characteristics of initial fatigue crack propagation process in Ti-6Al-4V in very high cycle fatigue. In: Sakai T., and Ochi Y. (Eds). VHCF-3, Proceedings of the 3rd international conference on very high cycle fatigue (2004), Society of Material Science, Japan 201-208
38. Jha S.K., and Ravi Chandran K.S. Scripta Mater 48 (2003) 1207-1212
39. Sakai T., Sato Y., and Nagano Y. Fatigue Fract Eng Mater Struct 25 (2002) 765-773
40. Sakai T., Sato Y., Nagano Y., and Oguma N. Effect of stress ratio on long life fatigue behavior of high carbon chromium bearing steels under axial loading. In: Sakai T., and Ochi Y. (Eds). VHCF-3, Proceedings of the 3rd international conference on very high cycle fatigue (2004), Society of Material Science, Japan 209-216
41. Shiozawa K., Nishino S., and Morii Y. Subsurface crack initiation and propagation mechanism of high-strength steel in very high cycle fatigue regime. In: Sakai T., and Ochi Y. (Eds). VHCF-3, Proceedings of the 3rd international conference on very high cycle fatigue (2004), Society of Material Science, Japan 85-92
42. Harada H., Oguma N., and Sakai T. Formation mechanism of fine granular area around inclusions for bearing steel in rotating bending. In: Sakai T., and Ochi Y. (Eds). VHCF-3, Proceedings of the 3rd international conference on very high cycle fatigue (2004), Society of Material Science, Japan 101-107
43. Lu L., and Shiozawa K. Effect of two-step load variation on giga-cycle fatigue and internal crack growth behavior of high carbon-chromium bearing steel. In: Sakai T., and Ochi Y. (Eds). VHCF-3, Proceedings of the 3rd international conference on very high cycle fatigue (2004), Society of Material Science, Japan 185-192
44. Sugeta A., Uematsu Y., and Jono M. An effect of load variation on high-cycle fatigue behavior of high strength steel. In: Sakai T., and Ochi Y. (Eds). VHCF-3, Proceedings of the 3rd international conference on very high cycle fatigue (2004), Society of Material Science, Japan 177-184
45. Ohtsuka N., Shindo Y., Mashiro T., and Hayashi T. Study on fracture surfaces of high strength steel subjected to very high cycle fatigue. In: Sakai T., and Ochi Y. (Eds). VHCF-3, Proceedings of the 3rd international conference on very high cycle fatigue (2004), Society of Material Science, Japan 93-100
46. Nakajima M., Toakaji M., Itoga H., and Ko H.-N. In: Stanzl-Tschegg S., and Mayer H. (Eds). Proceedings of the international conference on fatigue in the very high cycle regime (2001), BOKU, University of Agricultural Sciences, Austria 181-188