Near-neutral pH SCC of two line pipe steels under quasi-static stressing conditions

Proceedings of the Biennial International Pipeline Conference, IPC

Volumn 2, Issue , 2007, Pages 95-105

  Zheng, W ^a   Bibby, D ^a   Li, J ^a   Bowker, J T ^a   Gianetto, J A ^a   Revie, R W ^a   Williams, G ^a  

^a CANMET MATERIALS TECHNOLOGY LABORATORY   (Canada)

Author keywords

[No Author keywords available]

Indexed keywords

CRACK PROPAGATION RATE; LINE PIPE STEELS; PH SOLUTIONS; PRESSURE FLUCTUATIONS;

CRACK PROPAGATION; CYCLIC LOADS; GAS MIXTURES; PH; STRESS CORROSION CRACKING; YIELD STRESS;

STEEL PIPE;

EID: 34547532552     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1115/IPC2006-10084     Document Type: Conference Paper

References (11)

1. W. Zheng, F. A. MacLeod, R. W. Revie, W. R. Tyson, G. Shen, D. Kiff, M. Skaff, and E-W Wong, 1997, "Recent progress in the study of transgranular SCC in line pipe steels", Second International Conference on Corrosion-Deformation Interactions. CDI '96; Nice; France; 24-26 Sept. 1996. pp. 282-292.
2. R. N. Parkins, W. K Blanchard and B. S. Delanty, 1994, "Transgranular stress corrosion cracking of high-pressure pipelines in contact with solutions of near-neutral pH", Corrosion, Vol. 50 No.5, pp 394-408.
3. th EPRG-PRCI Joint Technical Meeting on Pipeline Research, Orlando, U.S.A..
4. T. Kushida, K. Nose, H. Asahi, M. Kimura, Y. Yamane, S. Endo, H. T. Kawano, 2001, "Effects of metallurgical factors and test conditions on near-neutral pH SCC of pipeline steels," Paper No. 01213, NACE Corrosion.
5. B. Fang, M. Elboujdaini, W. Zheng, J. Li, W. Revie, and E-H. Han, "Stress-corrosion crack initiation of high-strength pipeline steel", 2005, "Materials Degradation: Innovation, Inspection, Control", Annual Conference of Metallurgists of CIM, COM2005, p. 27-40.
6. W. Zheng, R. Sutherby, R.W. Revie, W.R. Tyson and G. Shen, 2000, "The roles of stress in SCC of linepipe steels in near-neutral pH environment", Environmentally Induced Cracking of Metals - the 39th Annual Conference of Metallurgists of CIM, COM2000, Ottawa, Ontario; Canada; pp. 93-102.
7. J. Li, 2006 "The focused-ion-beam microscope- More than a precision ion milling machine," JOM, pp. 27-31.
8. J. A. Gianetto, J. E.M. Braid and J. T. Bowker, 1992, "Microstructural characterization of hydrogen cracks in HAZ of selected pipeline steels", MTL Report 92-06 (TR), International Institute of Welding Doc. No. IX-1696-92
9. E. Bayraktar and D. Kaplan, 2004, "Mechanical and metallurgical investigation of martensite-austenite constituents in simulated welding conditions", J of Mat. Proc. Technology, 153-154 (2004), pp. 87-92.
10. W. Zheng, W.R. Tyson, G. Shen, R.W. Revie, G. Williams and D. Bibby, 2005, "Effects of Operating Practices on Crack Dormancy and Growth", GRI Report, GRI-04/0121.
11. J. A. Beavers, J. T Johnson, and R.L. Sutherby, 2000, "Material factors influencing the initiation of near-neutral pH SCC on underground pipelines," ASME International, OMAE Division (Calgary Chapter), Int. Pipeline Conf. (IPC 2000), Calgary, Alberta, Canada, October 1-5, 2000, ASME Paper No. 1PC 0047.