Effects of loading rate on damage and fracture behavior of TiAl alloys

Materials Science and Engineering: A

Volumn 465, Issue 1-2, 2007, Pages 183-193

  Cao, R ^a   Lei, M X ^a   Chen, J H ^a   Zhang, J ^b  

^a LANZHOU UNIVERSITY OF TECHNOLOGY   (China)

^b CENTRAL IRON AND STEEL RESEARCH INSTITUTE   (China)

Author keywords

Damage; Fracture mechanisms; Fracture toughness; Loading rate; TiAl alloys

Indexed keywords

CRACK INITIATION; CRACK PROPAGATION; FRACTURE TOUGHNESS; LOADS (FORCES); TENSILE STRENGTH;

GRIFFITHS CRACK; INTERLAMELLAR CRACKS; LOADING RATE;

TITANIUM ALLOYS;

CRACK INITIATION; CRACK PROPAGATION; FRACTURE TOUGHNESS; LOADS (FORCES); TENSILE STRENGTH; TITANIUM ALLOYS;

EID: 34250818809     PISSN: 09215093     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.msea.2007.02.026     Document Type: Article

References (13)

1. Kim Y.-W., and Dimiduk D.M. In: Chan K.S. (Ed). Proceeding of George R. Irwin Symposium on Cleavage Fracture (1997), The Minerals, Metals & Materials Society 305-317
2. Chan K.S., Onsttot J., and Kumar K.S. Metall. Mater. Trans. 31A (2000) 71-80
3. Inui H., Oh M.H., Nakamura A., and Yamakuchi M. Acta Mater. 40 (1992) 3095-3104
4. Akiyama, Yokoshima S., Johnson D.R., Kishida K., and Yamakuchi M. In: Chan K.S. (Ed). Proceeding of George R. Irwin Symposium on Cleavage Fracture (1997), The Minerals, Metals & Materials Society 293-303
5. Chen J.H., Cao R., Zhang J., and Wang G.Z. Metall. Mater. Trans. 35A (2004) 439-457
6. Hazzledine P.M., and Kad B.K. Mater. Sci. Eng. A 192-193 (1995) 340-346
7. Chan K.S., and Kim Y.W. Metall. Trans. A 23A (1992) 1663-1677
8. Chen J.H., Cao R., Zhang J., and Wang G.Z. Mater. Sci. Tech. 21 (2005) 507-516
9. Zheng R.T., Zhang Y.G., and Chen C.Q. J. Mater. Sci. 39 (2004) 1721-1724
10. Bartels A., Clemens H., and Dehm G. Z. Metallkd. 92 (2002) 180-185
11. Zhou Y., and Xia Y. J. Mater. Sci. 34 (2000) 925-929
12. R. Cao, Doctorate dissertation, Lanzhou University of Technology, 2006.
13. Kim Y.W. Mater. Sci. Eng. A192-A193 (1995) 519-533