The stress intensity factor of an edge dislocation near an elliptically blunted crack tip

International Journal of Fracture

Volumn 144, Issue 1, 2007, Pages 45-52

  Li, Tianlei ^a   Li, Zhonghua ^a  

^a SHANGHAI JIAO TONG UNIVERSITY   (China)

Author keywords

Blunt crack; Edge dislocation; Stress intensity factor

Indexed keywords

CRACK INITIATION; CRACK TIPS; CRACKS; FRACTURE MECHANICS;

BLUNT CRACK; EDGE DISLOCATION;

STRESS INTENSITY FACTORS;

EID: 34250818147     PISSN: 03769429     EISSN: 15732673     Source Type: Journal    
DOI: 10.1007/s10704-007-9074-5     Document Type: Article

References (13)

1. Creager M., Paris P.C. (1967). Elastic field equations for blunt cracks with reference to stress corrosion cracking. Int. J. Fract. 3: 247-251
2. Fischer L.L., Beltz G.E. (2001). The effect of crack blunting on the competition between dislocation nucleation and cleavage. J. Mech. Phys. Solids 49: 635-654
3. Huang P., Li Z., Sun J. (2001). Finite element analysis of the splitting and cylinderization processes of damage microcracks. Modell. Simul. Mater. Sci. Eng. 9: 193-206
4. Lakshmanan V., Li J.C.M. (1988). Edge dislocation emitted along inclined planes from a mode I crack. Mater. Sci. Eng. A104: 95-104
5. Majumdar B.S., Burns S.J. (1981). Crack tip shielding - An elastic theory of dislocations and dislocation arrays near a sharp crack. Acta Metall. 29: 579-588
6. Muskhelishvili N.I. (1975). Some Basic Problems in Mathematical Theory of Elasticity. Noordhoff, Leyden
7. Shiue S.T., Lee S. (1988). The elastic interaction between screw dislocations and cracks emanating from an elliptic hole. J. Appl Phys. 64: 129-139
8. Vitek V. (1975). Yielding from a crack with finite root-radius loaded in uniform tension. J. Mech. Phys. Solids 24: 67-76
9. Wang H., Li Z. (2003). Diffusive shrinkage of a void within a grain of a stressed polycrystal. J. Mech. Phys. Solids 51: 961-976
10. Weertman, J. (1996). Dislocation Based Fracture Mechanics. Word Scientific.
11. Zhang T.Y., Tong P. (1995). Interaction of an edge dislocation with a wedge crack. J Appl Phys. 78: 4873-4880
12. Zhang T.Y., Li J.C.M. (1991a). Image forces and shielding effects of a screw dislocation near a finite-length crack. Mater. Sci. Eng. A142: 35-39
13. Zhang T.Y., Li J.C.M. (1991b). Image forces and shielding effects of an edge dislocation near a finite length crack. Acta Metal. Mater. 39: 2739-2744