C0 plate element based on strain energy updating and spline interpolation, for analysis of impact damage in laminated composites

International Journal of Impact Engineering

Volumn 34, Issue 11, 2007, Pages 1835-1868

  Icardi, U ^a  

^a POLITECNICO DI TORINO   (Italy)

Author keywords

Delamination analysis; Design of composites; Impact induced damage; Nondestructive testing

Indexed keywords

ALGORITHMS; BOUNDARY CONDITIONS; IMPACT TESTING; MATHEMATICAL MODELS; NONDESTRUCTIVE EXAMINATION; STRAIN RATE;

DESIGN OF COMPOSITES; IMPACT DAMAGE; SMEARED LAMINATES; STRESS CONTACT CONDITIONS;

DELAMINATION;

EID: 34249980360     PISSN: 0734743X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijimpeng.2006.10.006     Document Type: Article

References (65)

1. Abrate S. Impact on composite structures (1998), Cambridge University Press, Cambridge
2. Abrate S. Impact on laminated composite materials. Appl Mech Rev 44 4 (1991) 155-190
3. Abrate S. Modeling of impacts on composite structures. Compos Struct 51 (2001) 129-138
4. Abrate S. Impact on laminated composites: recent advances. Appl Mech Rev 47 11 (1994) 517-544
5. Bolotin V.V. Delaminations in composite structures: its origin, growth and stability. Compos: Part B 27 (1996) 129-145
6. Rowlands RE. Strength (failure) theories and their experimental correlations. Handbook of Composites, vol. 3. Amsterdam: Elsevier; 1985. p. 71-125.
7. Nahas M.N. Survey of failure and post-failure theories of laminated fibre reinforced composites. J Compos Technol. Res. 8 (1986) 138-153
8. Echaabi J.F., and Trochu F. Review of failure criteria of fibrous composite materials. Polym Compos 17 (1996) 786-798
9. Paris F. A study of failure criteria of fibrous composite materials. NASA/CR-2001-210661, 2001.
10. Tennyson RC, Wharam GE. Evaluation of failure criterion for graphite-epoxy. NASA CR-172547, 1985.
11. Icardi U, Locatto S, Longo A. Assessment of recent theories for predicting failure of composite laminates. Appl Mech Rev, in press.
12. Bathe KJ. On reliability in the simulation of structural and fluid flow response. Advances in computational methods for simulation. Civil-Comp Press; 1996. p. 1-7.
13. Noor AK. Computational structures technology-leap frogging into the twenty-first century. Advances in computational structures technology, Civil-Comp Press; 1996. p. 1-18.
14. Noor A.K., Burton W.S., and Bert C.W. Computational models for sandwich panels and shells. Appl Mech Rev 49 3 (1996) 155-199
15. Reddy J.N. Mechanics of laminated composite plates and shells: theory and analysis. 2nd ed (2003), CRC Press, Boca Raton, FL
16. Tenek L.T., and Argyris J. Finite element analysis for composite structures (1998), Kluwer Academic Publishers, Dordrecht
17. Averill R.C., and Yip Y.C. An efficient thick beam theory and finite element model with zig-zag sublaminates approximations. AIAA J 34 8 (1996) 1626-1632
18. Cho Y.B., and Averill R.C. An improved theory and finite element model for laminated composite and sandwich beams using first-order zig-zag sublaminate approximations. Compos Struct 37 3/4 (1997) 281-298
19. Cho Y.B., and Averill R.C. First-order zig-zag sublaminate plate theory and finite element model for laminated composite and sandwich panels. Compos Struct 50 (2000) 1-15
20. 0 zig-zag kinematic displacement models for the analysis of laminated composites. Mech Compos Mater Struct 6 1 (1999) 31-56
21. 0 zig-zag finite element for analysis of laminated composites beams. J Eng Mech 125 3 (1999) 323-330
22. Icardi U. Higher-order zig-zag model for analysis of thick composite beams with inclusion of transverse normal stress and sublaminates approximations. Compos: Part B 32 (2001) 343-354
23. Icardi U. Applications of zig-zag theories to sandwich beams. Mech Adv Mater Struct 10 1 (2002) 77-97
24. Wang C.Y., and Yew C.H. Impact damage in composite laminates. Comput Struct 37 (1990) 967-982
25. 0 plate element for delamination damage analysis, based on a zig-zag model and strain energy updating. Int J Impact Eng 31 (2005) 579-606
26. 0 plate element for global/local analysis of multilayered composites, based on a 3D zig-zag model and strain energy updating. Int J Mech Sci 47 (2005) 1561-1594
27. Rolfes R., and Rohwer K. Improved transverse shear stress in composite finite elements based on first order shear deformation theory. Int J Numer Meth Eng 40 (1997) 51-60
28. Rolfes R. Efficient linear transverse normal stress analysis of layered composite plates. Comput Struct 68 (1998) 643-652
29. Rolfes R., and Rohwer K. Calculating three dimensional stresses in layered composite plates and shells. Mech Compos Mater 34 4 (1998) 491-500
30. Icardi U. Layer-wise mixed element with sub-laminates approximation and 3D zig-zag field, for analysis of local effects in laminated and sandwich composites, Int J Numer Meth Eng, in press.
31. Prathap G. The displacement-type finite element approach-from art to science. Prog Aerosp Sci 10 (1994) 295-405
32. Yong-Woo K., and Oak-Key M. Optimal strain location of two-dimensional continuum elements in terms of field-consistency. Comput Struct 59 6 (1996) 1121-1138
33. Barlow J. More on optimal stress points reduced integration, element distorsions and error estimation. Int J Numer Meth Eng 28 (1989) 1486-1504
34. Barlow J. Optimal stress location in finite element models. Int J Numer Meth Eng 10 (1976) 243-251
35. de Boor C. A practical guide to splines (1987), Springer, Berlin
36. Tan T.M., and Sun C.T. Use of statical indentation laws in the impact analysis of laminated composite plates. Trans ASME 52 (1985) 6-12
37. Chao C.C., and Tu C.Y. Three-dimensional contact dynamics of laminated plates: part1 normal impact. Compos: Part B 30 (1999) 9-22
38. Heitzer J. Dynamic interaction of a plate and an impactor. Comput Struct 60 5 (1996) 837-848
39. Hashin Z., and Rotem A. A fatigue failure criterion for fiber reinforced materials. J Compos Mater 7 (1973) 448-464
40. Hashin Z. Failure criteria for unidirectional fiber composites. J Appl Mech 47 (1980) 329-334
41. Hashin Z. Analysis of orthogonally craked laminates under tension. J Appl Mech 54 (1987) 872-879
42. Chang F.K., and Chen M.H. The in situ ply shear strength distributions in graphite/epoxy laminated composites. J Compos Mater 21 (1987) 708-733
43. Puck A. Festigkeitsanalyse von faser-matrix-laminaten-Modelle fur die praxis (1995), Carl Hanser, Munich
44. Puck A. Festigkeitsberechnung an glassfaser/kunstoff laminates bei zusammengesetzeter beanspruchung. Kunststoffe 59 (1969) 780-787
45. Puck A. Calculating the strength of glass-fibre/plastic laminates under combined load. Kunststoffe, German Plast 55 (1969) 18-19
46. Puck A. Failure criterion shows the direction. Kunststoffe, German Plast 82 (1992) 29-32
47. Puck A. Fracture criteria for higly stressed fibre-plastic composites which meet requirements of design practice. Kunststoffe, German Plast 82 (1992) 34-38
48. Puck A., and Shurmann H. Failure analysis of FRP laminates by means of physically based phenomenological models. Compos Sci Technol 58 (1998) 1045-1067
49. Davila CG, Camanho PP. Failure criteria for FRP laminates in plane stress. NASA/TM-2003-212663, 2003.
50. Choi H.Y., and Chang F.K. A model for predicting damage in graphite/epoxy laminated composites resulting from low-velocity point impact. J Compos Mater 26 (1992) 2134-2169
51. Hou J.P., Petrinic N., Ruiz C., and Hallet S.R. Prediction of impact damage in composite plates. Compos Sci Technol 60 (2000) 273-281
52. Chang F.K., and Lessard H. Damage tolerance of laminated composites containing an open hole and subjected to compressive loadings: part I-analysis. J Compos Mater 25 1 (1991) 2-43
53. Choi H.Y., and Chang F.K. A model for predicting damage in graphite/epoxy laminated composites resulting from low velocity point impact. J Compos Mater 26 14 (1992) 2134-2169
54. Hou J.P., Petrinic N., and Ruiz C. A delamination criterion for laminated composites under low velocity impact. Compos Sci Technol 61 (2001) 2069-2074
55. Chang F.K., and Chang K.Y. Post failure analysis of bolted composite joints in tension or shear-out mode failure. J Compos Mater 21 (1987) 803-833
56. Chang F.K., and Chang K.Y. A progressive damage model for laminated composites containing stress concentrations. J Compos Mater 21 (1987) 834-855
57. Brewer J.C., and Lagace P.A. Quadratic stress criterion for initiation of delamination. J Compos Mater 22 (1988) 1141-1155
58. Whitney J.N., and Nuismer R.J. Stress failure criteria for laminated composites containing stress concentrations. J Compos Mater 8 (1974) 253-265
59. Chang F.K., and Springer G.S. The strengths of fiber reinforced composite bends. J Compos Mater 20 (1986) 30-47
60. Luo R.K., Green E.R., and Morrison C.J. An approach to evaluate the impact damage initiation and propagation in composite laminates. Compos PartB: Eng 32B (2001) 513-520
61. Pagano N.J. Exact solutions for composite laminates in cylindrical bending. J Compos Mater 3 (1969) 398-411
62. Alfano G., Auricchio E., Rosati L., and Sacco E. MITC finite elements for laminated composite plates. Int J Numer Meth Eng 50 (2001) 707-738
63. Swanson S.R. Impact response of fiber composite structures. Appl Mech Rev 44 11 (1991) 256-263
64. Prasad C.B., Damodar R.A., and Starnes H.J. Response of laminated composite plates to low-speed impact by different impactors. AIAA J 32 6 (1994) 1270-1277
65. Christoforou A.P., and Yigit A.S. Charaterization of impact in composite plates. Compos Struct 43 (1998) 15-24