Erosion-oxidation behaviour of pack-aluminized 9% chromium steel under fluidized-bed conditions at elevated temperature

Corrosion Science

Volumn 49, Issue 7, 2007, Pages 2844-2865

  Huttunen Saarivirta, E ^a   Stott, F H ^a   Rohr, V ^b   Schutze M ^b  

^a UNIVERSITY OF MANCHESTER   (United Kingdom)

^b KARL WINNACKER INSTITUT   (Germany)

Author keywords

A. Aluminium; A. Metal coatings; A. Steel; B. Erosion; C. Oxidation

Indexed keywords

ALUMINUM; EROSION; FLUIDIZED BEDS; HIGH TEMPERATURE EFFECTS; OXIDATION; SCANNING ELECTRON MICROSCOPY;

ANGLE IMPACTS; BRITTLE EROSION; METAL COATINGS;

STEEL;

ALUMINUM; EROSION; FLUIDIZED BEDS; HIGH TEMPERATURE EFFECTS; OXIDATION; SCANNING ELECTRON MICROSCOPY; STEEL;

EID: 34248574817     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.corsci.2006.12.024     Document Type: Article

References (44)

1. Eyre B.L. Materials technology challenges for power generation in the 21st century. Prog. Mater. Sci. 42 (1997) 23-37
2. Natesan K. Applications of coatings in coal-fired energy systems. Surf. Coat. Technol. 56 (1993) 185-197
3. Wright I.G. A review of experience of wastage in fluidized-bed boilers. Mater. High Temp. 14 (1997) 277-288
4. Stringer J. Practical experience with wastage at elevated temperatures in coal combustion systems. Wear 186-187 (1995) 11-27
5. R. Viswanathan, W.T. Bakker, Materials for boilers in ultra supercritical power plants, in: Proceedings of International Joint Power Generation Conference 2000, Miami Beach, Florida, USA, American Society of Mechanical Engineers, New York, USA, Paper 15049, 2000.
6. Levy A., and Man Y.-F. Elevated temperature erosion-corrosion of 9Cr-1Mo steel. Wear 111 (1986) 135-159
7. Levy A., and Man Y.-F. The effect of temperature on the erosion-corrosion of 9Cr-1Mo steel. Wear 111 (1986) 161-172
8. Sethi V.K., and Corey R.G. High temperature erosion of alloys in oxidizing environments. Proceedings of 7th International Conference on Erosion by Liquid and Solid Impact (1987), Cavendish Laboratory, Cambridge, United Kingdom
9. Levy A.V., Wang B.Q., Man Y.-F., and Jee N. Erosion-corrosion of steels in simulated and actual fluidized bed combustor environments. Wear 131 (1989) 85-103
10. Rao M., Keiser J., Levy A.V., and Wang B.-Q. Mechanical behaviour of erosion-corrosion scales on steels as characterized by single-particle impacts. Wear 150 (1991) 135-152
11. Norling R., and Olefjord I. Erosion-corrosion of Fe- and Ni-based alloys at 550 °C. Wear 254 (2003) 173-184
12. Wang B.Q., Geng G.Q., and Levy A.V. The relationship between erosion-corrosion metal wastage and temperature. Wear 159 (1992) 233-239
13. Stott F.H., Green S.W., and Wood G.C. The influence of temperature on the erosion oxidation of steels in a fluidized-bed environment. Mater. Sci. Eng. A 121 (1989) 611-617
14. Hutchings I.M., Little J.A., and Ninham A.J. Low velocity erosion-corrosion of steels in a fluidized bed. Proceedings of 4th Berkeley Conference on Corrosion-Erosion-Wear of Materials at Elevated Temperatures (1990), National Association of Corrosion Engineers, Houston, USA
15. Hall D.J., and Saunders S.R.J. Corrosion-erosion of alloys exposed in fluidized bed combustors. Proceedings of High Temperature Materials for Power Engineering Conference 1990, Liege, Belgium (1990), Kluwer, Dordrecht, The Netherlands
16. Lamarre L. Solutions for solid-particle erosion. Electric Power Res. Inst. J. 15 (1990) 31-37
17. Stephenson D.J., Nicholls J.R., and Hancock P. Particle-surface interactions during the erosion of aluminide-coated MarM002. Wear 111 (1986) 31-39
18. Hogmark S., Hammarsten A., and Söderberg S. On the combined effects of corrosion and erosion. Proceedings of 6th International Conference on Erosion by Liquid and Solid Impact (1983), Cavendish Laboratory, Cambridge, United Kingdom
19. Kang C.T., Pettit F.S., and Birks N. Mechanisms in the simultaneous erosion-oxidation attack of nickel and cobalt at high temperature. Metall. Trans. 18A (1987) 1785-1803
20. Rishel D.M., Pettit F.S., and Birks N. Some principal mechanisms in the simultaneous erosion and corrosion attack of metals at high temperatures. Mater. Sci. Eng. A 143 (1991) 197-211
21. Sundararajan G. An analysis of the erosion-oxidation interaction mechanisms. Wear 145 (1991) 251-282
22. Stack M.M., Stott F.H., and Wood G.C. Review of mechanisms of erosion-corrosion of alloys at elevated temperatures. Wear 162-164 (1993) 706-712
23. Stack M.M., Lekatos S., and Stott F.H. Erosion-corrosion regimes: number, nomenclature and justification?. Tribol. Int. 28 (1995) 445-451
24. Wright I.G., Sethi V.K., and Markworth A.J. A generalized description of the simultaneous processes of scale growth by high temperature oxidation and removal by erosive impact. Wear 186-187 (1995) 230-237
25. Wellman R.G., and Nicholls J.R. High temperature erosion-oxidation mechanisms, maps and models. Wear 256 (2004) 907-917
26. Huttunen-Saarivirta E., Kalidakis S., Stott F.H., Rohr V., and Schütze M. The erosion-corrosion resistance of uncoated and aluminized 12% chromium ferritic steels under fluidized-bed conditions at elevated temperature. Mater. Corros. 56 (2005) 897-906
27. Huttunen-Saarivirta E., Stott F.H., Rohr V., and Schütze M. Degradation mechanisms of aluminium diffusion coatings on 12% chromium steels under elevated temperature erosion-oxidation conditions. Mater. High Temp. 23 (2006) 1-11
28. Rohr V., and Schütze M. Novel low temperature diffusion coatings for heat exchanger materials. Mater. Sci. Forum 461 (2004) 401-408
29. Xiang Z.D., and Datta P.K. Effects of pack composition on the formation of aluminide coatings on alloy steels at 650 °C. J. Mater. Sci. 40 (2005) 1959-1966
30. Finnie I. The mechanisms of erosive wear in ductile metals. In: Natesan K. (Ed). Corrosion-Erosion of Materials (1980), American Institute of Mining, Metallurgical and Petroleum Engineers, New York, USA
31. 5 intermetallic compound. Intermetallics 11 (2003) 633-642
32. Huttunen-Saarivirta E., Stott F.H., Rohr V., and Schütze M. Particle angularity effects on the elevated-temperature erosion-oxidation behaviour of aluminium diffusion coatings on 9% Cr steel. Wear 261 (2006) 746-759
33. Tortorelli P.F., and Natesan K. Critical factors affecting the high-temperature corrosion performance of iron aluminides. Mater. Sci. Eng. A 258 (1998) 115-125
34. Natesan K. Corrosion performance of iron aluminides in mixed-oxidant environments. Mater. Sci. Eng. A 258 (1998) 126-134
35. Agüero A., Muelas R., Pastor A., and Osgerby S. Long exposure steam oxidation testing and mechanical properties of slurry aluminide coatings for steam turbine components. Surf. Coat. Tech. 200 (2005) 1219-1224
36. Norling R., and Nylund A. The influence of temperature on oxide-scale formation during erosion-corrosion. Oxid. Met. 63 (2005) 87-111
37. Palm M. The Al-Cr-Fe system - phases and phase equilibria in the Al-rich corner. J. Alloys Compd. 252 (1997) 192-200
38. Deevi S.C., and Sikka V.K. Nickel and iron aluminides: an overview on properties, processing and applications. Intermetallics 4 (1996) 357-375
39. Jun J.H., Jun J.H., and Kim K.Y. Degradation behaviour of Al-Fe Coatings in wet-seal area of molten carbonate fuel cells. J. Power Sources 112 (2002) 153-161
40. Agüero A., and Muelas R. Steam oxidation of slurry aluminide coatings on ferritic steels for advanced coal-fired steam power plants. Mater. Sci. Forum 461 (2004) 957-964
41. 5 formed on MANET II steel by aluminizing. J. Nucl. Mater. 249 (1997) 33-38
42. Paul A., van Dal M.J.H., Kodentsov A.A., and van Loo F.J.J. The Kirkendall effect in multiphase diffusion. Acta Mater. 52 (2004) 623-630
43. Nakamura R., Fujita K., Iijima Y., and Okada M. Diffusion mechanisms in B2 NiAl phase studied by experiments on Kirkendall effect and interdiffusion under high pressures. Acta Mater. 51 (2003) 3861-3870
44. Angenete J., and Stiller K. Oxidation of simple and Pt-modified aluminide diffusion coatings on Ni-base superalloys-II. Oxide scale failure. Oxid. Met. 60 (2003) 83-101