Cuspal movement and microleakage in premolar teeth restored with resin-based filling materials cured using a 'soft-start' polymerisation protocol

Dental Materials

Volumn 23, Issue 5, 2007, Pages 637-643

  Fleming, G J P ^a   Cara, R R ^b   Palin, W M ^b   Burke, F J T ^c  

^a TRINITY COLLEGE DUBLIN   (Ireland)

^b IULIU HATIEGANU UNIVERSITY OF MEDICINE AND PHARMACY   (Romania)

^c UNIVERSITY OF BIRMINGHAM   (United Kingdom)

Author keywords

Cuspal movement; Gingival microleakage; Ormocer; Resin based composite; Soft start polymerisation

Indexed keywords

CHEMICAL BONDS; DENTAL PROSTHESES; FOURIER TRANSFORM INFRARED SPECTROSCOPY; POLYMERIC GLASS; RESINS;

CUSPAL MOVEMENTS; GINGIVAL MICROLEAKAGE; RESIN-BASED COMPOSITE; SOFT-START POLYMERIZATION;

DENTAL COMPOSITES;

ADMIRA; BIOMEDICAL AND DENTAL MATERIALS; COLORING AGENT; DIAGNOSTIC AGENT; FILTEK Z250; FUCHSINE; METHACRYLIC ACID DERIVATIVE; POLYMER; RESIN; SILICON DIOXIDE; SILOXANE; UNCLASSIFIED DRUG; Z100 COMPOSITE RESIN; ZIRCONIUM;

ARTICLE; CHEMISTRY; CLASSIFICATION; COMPARATIVE STUDY; DENTAL BONDING; DENTAL SURGERY; DENTIN; ENAMEL; HUMAN; INFRARED SPECTROSCOPY; MATERIALS TESTING; METHODOLOGY; PREMOLAR TOOTH; TEMPERATURE; TIME; TOOTH CERVIX; TOOTH CROWN; TOOTH DISEASE; ULTRASTRUCTURE;

BICUSPID; COLORING AGENTS; COMPOSITE RESINS; DENTAL BONDING; DENTAL ENAMEL; DENTAL LEAKAGE; DENTAL MATERIALS; DENTAL RESTORATION, PERMANENT; DENTIN; HUMANS; MATERIALS TESTING; METHACRYLATES; POLYMERS; ROSANILINE DYES; SILICON DIOXIDE; SILOXANES; SPECTROSCOPY, FOURIER TRANSFORM INFRARED; TEMPERATURE; TIME FACTORS; TOOTH CERVIX; TOOTH CROWN; ZIRCONIUM;

EID: 33947238872     PISSN: 01095641     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.dental.2006.06.002     Document Type: Article

References (27)

1. Bowen R.L. Synthesis of a silica-resin direct filling material: progress report. J Dent Res 37 (1958) 90
2. Bowen RL. Dental filling materials comprising of vinyl-silane treated fused silica and binder consisting of the reaction product of bisphenol-A and glycidyl methacrylate. US Patent 3,066,112 (1962).
3. Davidson C.L., DeGee A.J., and Feilzer A.J. The competition between the composite-dentin bond strength and the polymerisation contraction stress. J Dent Res 63 (1984) 1396-1399
4. Davidson C.L., and Feilzer A.J. Polymerisation shrinkage and polymerisation shrinkage stress in polymer-based restoratives. J Dentistry 25 (1997) 435-440
5. Abbas G., Fleming G.J.P., Harrington E., Shortall A.C.C., and Burke F.J.T. Cuspal movement in premolar teeth restored with a packable composite cured in bulk or incrementally. J Dentistry 31 (2003) 437-444
6. Fleming G.J.P., Hall D., Shortall A.C.C., and Burke F.J.T. Cuspal movement and microleakage in premolar teeth restored with posterior filling materials of varying reported volumetric shrinkage values. J Dentistry 33 (2005) 139-146
7. Palin W.M., Fleming G.J.P., Nathwani H., Burke F.J.T., and Randall R.C. In vitro cuspal deflection and microleakage of maxillary premolars restored with novel low-shrink dental composites. Dent Mater 21 (2005) 324-335
8. Gonzalez-Lopez S., Lucena-Martin C., de Haro-Gasquet F., Vilchez-Diaz M.A., and Haro-Munoz C. Influence of different composite restoration techniques on cuspal deflection: an in vitro study. Operative Dentistry 29 (2004) 600-656
9. Sulimann A.A., Boyer D.B., and Lakes R.S. Cusp movemnet in premolars resulting from composite polymerization shrinkage. Dent Mater 9 (1993) 6-10
10. Causton B.E., Miller B., and Sefton J. The deformation of cusps by bonded posterior composite restorations: an in vitro study. Br Dent J 159 (1985) 397-400
11. Lutz F., Kreici I., and Barbakow F. Quality and durability of marginal adaptation in bonded composite restorations. Dent Mater 7 (1991) 107-113
12. Uno S., and Asmussen E. Marginal adaptation of a restorative resin polymerized at reduced rate. Scand J Dent Res 99 (1991) 440-444
13. Mehl A., Hickel R., and Kunzelmann K.-H. Physical properties and gap formation of light-cured composites with and without 'soft-start polymerization'. J Dentistry 25 (1997) 321-330
14. Hofmann N., Denner W., Hugo B., and Klaiber B. The influence of plasma arc vs. halogen standard or soft-start irradiation on polymerization shrinkage kinetics of polymer matrix composites. J Dentistry 31 (2003) 383-393
15. Sakaguchi R.L., and Berge H.X. Reduced light energy density decreases post-gel contraction while maintaining degree of conversion in composites. J Dentistry 26 (1998) 695-700
16. Sahafi A., Peutzfeldt A., and Asmussen E. Soft-start polymerisation and marginal gap formation in vitro. Am J Dentistry 24 (2001) 145-147
17. Miyazaki M., Oshida Y., Moore B.K., and Onose H. Effects of light exposures on fracture toughness and flexural strength of light-cured composites. Dent Mater 12 (1996) 328-332
18. Wolter H., Storch W., and Ott H. Dental filling materials (posterior composites) based on inorganic/organic copolymers (ORMOCERs). Macro Akron (1994) 503
19. Data Sheet for Scotch bond 1 supplied by 3M ESPE (St. Paul, MN, USA).
20. Data Sheet for Admira supplied by VOCO (GmbH, Germany).
21. Palmer D.S., Barco M.T., and Billy E.J. Temperature extremes produced orally by hot and cold liquids. J Prosthetic Dentistry 67 (1992) 325-327
22. Spierings T.M., Peters M.B., Bosman F., and Plasschaert A.M. Verification of theoretical modelling of heat transmission in teeth by in vivo experiments. J Dent Res 66 (1987) 1336-1339
23. Palin W.M., Fleming G.J.P., Burke F.J.T., Marquis P.M., and Randall R.C. Monomer conversion versus flexural strength of a novel dental composite. J Dentistry 31 (2003) 341-351
24. Cerutti A., Flocchini P., Madini L., Mangani F., Putignano A., and Docchio F. Effects of bonded composite vs. amalgam on resistance to cuspal deflection for endodontically-treated premolar teeth. Am J Dentistry 17 (2004) 295-300
25. Asmussen E., and Peutzfeldt A. Influence of UEDMA BisGMA and TEGDMA on selected mechanical properties of experimental resin composites. Dent Mater 14 (1998) 51-56
26. Silikas N., Eliades G., and Watts D.C. Light intensity effects on resin-composite degree of conversion and shrinkage strain. Dent Mater 16 (2000) 292-296
27. Watts D.C., and Al Hindi A. Intrinsic 'soft-start' polymerisation shrinkage-kinetics in an acrylate-based resin-composite. Dent Mater 15 (1999) 39-45