Microtensile bond strength of dual-polymerizing cementing systems to dentin using different polymerizing modes

Journal of Prosthetic Dentistry

Volumn 97, Issue 2, 2007, Pages 99-106

  Arrais, Cesar A G ^a   Giannini, Marcelo ^a   Rueggeberg, Frederick A ^b   Pashley, David H ^b  

^a UNIVERSITY OF CAMPINAS   (Brazil)

^b MEDICAL COLLEGE OF GEORGIA   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

DENTIN BONDING AGENT;

ANALYSIS OF VARIANCE; ARTICLE; CHEMISTRY; DENTAL BONDING; DENTAL CARE; DENTAL SURGERY; HUMAN; LIGHT; METHODOLOGY; MOLAR TOOTH; TENSILE STRENGTH;

ANALYSIS OF VARIANCE; DENTAL BONDING; DENTAL RESTORATION FAILURE; DENTAL STRESS ANALYSIS; DENTIN-BONDING AGENTS; HUMANS; LIGHT; MOLAR, THIRD; TENSILE STRENGTH;

EID: 33847305853     PISSN: 00223913     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.prosdent.2006.12.007     Document Type: Article

References (25)

1. Inokoshi S., Willems G., Van Meerbeek B., Lambrechts P., Braem M., and Vanherle G. Dual-cure luting composites: Part I: filler particle distribution. J Oral Rehabil 20 (1993) 133-146
2. Sjogren G., Molin M., van Dijken J., and Bergman M. Ceramic inlays (Cerec) cemented with either a dual-cured or a chemically cured composite resin luting agent. A 2-year clinical study. Acta Odontol Scand 53 (1995) 325-330
3. Milleding P., Ortengren U., and Karlsson S. Ceramic inlay systems: some clinical aspects. J Oral Rehabil 22 (1995) 571-580
4. Nathanson D. Etched porcelain restorations for improved esthetics, part II: onlays. Compendium 8 (1987) 105-110
5. Strang R., McCrosson J., Muirhead G.M., and Richardson S.A. The setting of visible-light-cured resins beneath etched porcelain veneers. Br Dent J 163 (1987) 149-151
6. Rasetto F.H., Driscoll C.F., Prestipino V., Masri R., and von Fraunhofer J.A. Light transmission through all-ceramic dental materials: a pilot study. J Prosthet Dent 91 (2004) 441-446
7. Sanares A.M., Itthagarun A., King N.M., Tay F.R., and Pashley D.H. Adverse surface interactions between one-bottle light-cured adhesives and chemical-cured composites. Dent Mater 17 (2001) 542-556
8. Ruyter I.E. Unpolymerized surface layers on sealants. Acta Odontol Scand 39 (1981) 27-32
9. Bowen R.L., Cobb E.N., and Rapson J.E. Adhesive bonding of various materials to hard tooth tissues: improvement in bond strength to dentin. J Dent Res 61 (1982) 1070-1076
10. Yamauchi J. Study of dental adhesive containing phosphoric acid methacrylate monomer. Japanese J Dent Mater 5 (1986) 144-154
11. De Munck J., Van Meerbeek B., Yoshida Y., Inoue S., Vargas M., Suzuki K., et al. Four-year water degradation of total-etch adhesives bonded to dentin. J Dent Res 82 (2003) 136-140
12. Yiu C.K., Garcia-Godoy F., Tay F.R., Pashley D.H., Imazato S., King N.M., et al. A nanoleakage perspective on bonding to oxidized dentin. J Dent Res 81 (2002) 628-632
13. Jacobsen T., and Soderholm K.J. Some effects of water on dentin bonding. Dent Mater 11 (1995) 132-136
14. Blackman R., Barghi N., and Duke E. Influence of ceramic thickness on the polymerization of light-cured resin cement. J Prosthet Dent 63 (1990) 295-300
15. Hasegawa E.A., Boyer D.B., and Chan D.C. Hardening of dual-cured cements under composite resin inlays. J Prosthet Dent 66 (1991) 187-192
16. Peutzfeldt A. Dual-cure resin cements: in vitro wear and effect of quantity of remaining double bonds, filler volume, and light curing. Acta Odontol Scand 53 (1995) 29-34
17. Braga R.R., Cesar P.F., and Gonzaga C.C. Mechanical properties of resin cements with different activation modes. J Oral Rehabil 29 (2002) 257-262
18. Rueggeberg F.A., and Caughman W.F. The influence of light exposure on polymerization of dual-cure resin cements. Oper Dent 18 (1993) 48-55
19. Hofmann N., Papsthart G., Hugo B., and Klaiber B. Comparison of photo-activation versus chemical or dual-curing of resin-based luting cements regarding flexural strength, modulus and surface hardness. J Oral Rehabil 28 (2001) 1022-1028
20. Asmussen E. Setting time of composite restorative resins vs. content of amine, peroxide, and inhibitor. Acta Odontol Scand 39 (1981) 291-294
21. Lee I.B., and Um C.M. Thermal analysis on the cure speed of dual cured resin cements under porcelain inlays. J Oral Rehabil 28 (2001) 186-197
22. Tanoue N., Koishi Y., Atsuta M., and Matsumura H. Properties of dual-curable luting composites polymerized with single and dual curing modes. J Oral Rehabil 30 (2003) 1015-1021
23. Tay F.R., and Pashley D.H. Aggressiveness of contemporary self-etching systems. I: depth of penetration beyond dentin smear layers. Dent Mater 17 (2001) 296-308
24. Montes M.A., de Goes M.F., and Sinhoreti M.A. The in vitro morphological effects of some current pretreatments on dentin surface: an SEM evaluation. Oper Dent 30 (2005) 201-212
25. Mak Y.F., Lai S.C., Cheung G.S., Chan A.W., Tay F.R., and Pashley D.H. Micro-tensile bond testing of resin cements to dentin and an indirect resin composite. Dent Mater 18 (2002) 609-621