Degradation of materials and fatigue durability of aircraft constructions after long-term operation

Materials Science

Volumn 42, Issue 4, 2006, Pages 427-439

  Ostash, O P ^a   Andreiko, I M ^a   Holovatyuk, Yu V ^a  

^a KARPENKO PHYSICOMECHANICAL INSTITUTE   (Ukraine)

Author keywords

[No Author keywords available]

Indexed keywords

CORRECTION FACTORS; FATIGUE DURABILITY; LONG TERM OPERATION; RESIDUAL LIFETIME;

ALUMINUM ALLOYS; DEGRADATION; FATIGUE TESTING; STRENGTH OF MATERIALS;

AIRCRAFT MANUFACTURE;

EID: 33846867454     PISSN: 1068820X     EISSN: None     Source Type: Journal    
DOI: 10.1007/s11003-006-0098-1     Document Type: Article

References (19)

1. G. I. Nesterenko, "Fatigue and damage tolerance of ageing aircraft structures," J. Soc. Nondestruct. Testing Monitor. Diagn., V.XXI, No. 3, 20-28 (2000).
2. O. P. Ostash, V. M. Uchanin, I. M. Andreiko, and I. R. Makoviichuk, "Engineering diagnostics and lifetime of constructions after long-term operation," in: Physical Methods and Means of Control of Media, Materials, and Products [in Ukrainian], Kyiv (1999), pp. 3-8.
3. O. N. Romaniv, A. N. Tkach, I. R. Dzioba, et al., "Effect of long-term thermomechanical action on the crack resistance of 12KH1MF steel," Fiz.-Khim. Mekh. Mater., 25, No. 2, 87-92 (1989).
4. O. Z. Student, "Accelerated method of hydrogen degradation of structural steel," Fiz.-Khim. Mekh. Mater., 34, No. 4, 45-52 (1998).
5. G. I. Nesterenko, "Calculation of the characteristics of operational survivability of aircraft constructions based on fracture mechanics," Fiz.-Khim. Mekh. Mater., 19, No. 1, 12-20 (1983).
6. S. Ya. Yarema, O. P. Ostash, A. G. Vovnyanko, et al., "Effect of anisotropy, thickness, and operating time on crack growth in pressed and rolled semifinished items of D 16chT and V95pchT1 alloys," Fiz.-Khim. Mekh. Mater., 19, No. 1, 20-24 (1983).
7. K. Wakamatsu, M. Tsubota, Y. Kunii, and T. Iida, "Life prediction of aluminium-magnesium alloys for power transmission equipment," in: Proc. Int. Sympos. Plant Aging Life Predict. Corrod. Struct. (Sapporo, Japan, May 15-18, 1995), Sapporo, Japan (1995), pp. 201-207.
8. O. D. Zinyuk, Determination of the Cyclic Crack Resistance of Constructional Magnesium and Aluminum Alloys and Their Welded Joints [in Russian], Author's Abstract of Candidate-Degree Thesis (Eng.), Lvov (1987).
9. S. Ya. Yarema and I. B. Polutranko, "Cyclic crack resistance of pressed panels of D16chT and V95pchT1 alloys in liquid media," Fiz.-Khim. Mekh. Mater., 19, No. 6, 56-59 (1983).
10. A. M. Dotsenko and G. B. Denisova, "Propagation of a fatigue crack in D16-T and V95-T1 aluminum alloys in tests in sprayed and unsprayed NaCl solutions," Fiz.-Khim. Mekh. Mater., 18, No. 1, 51-53 (1982).
11. B. I. Ermolenko, "A study of the corrosive action of the environment on the growth rate of fatigue cracks," Fiz.-Khim. Mekh. Mater., 15, No. 1, 12-15 (1979).
12. G. S. Neshpor, A. A. Armyagov, and D. A. Andreev, "Growth of fatigue cracks and fracture toughness of constructional aluminum alloys in air and 3.5% NaCl solution," Fiz.-Khim. Mekh. Mater., 18, No. 4, 91-92 (1982).
13. A Study of the Cyclic Crack Resistance of High-Strength Aluminum Alloys [in Russian], Report on Contract No. 1135/081, Karpenko Physicomechanical Institute, Ukrainian Academy of Sciences, Lviv (1985).
14. Determination of the Resistance of High-Strength Aluminum Alloys to Fatigue Crack Initiation [in Russian], Report on Contract No. 1374/317, Karpenko Physicomechanical Institute, Ukrainian Academy of Sciences, Lviv (1987).
15. H. M. Nykyforchyn and O. Z. Student, "Effect of hydrogen on the formation of fatigue thresholds of constructional steels," Fiz.-Khim. Mekh. Mater., 37, No. 2, 97-106 (2001).
16. O. P. Ostash, "New approaches in the mechanics of fatigue fracture," Fiz.-Khim. Mekh. Mater., 42, No. 1, 13-25 (2006).
17. O. P. Ostash, "Application of the unified model of fatigue fracture of materials for the evaluation of their degradation in objects of long-term operation," in: V. V. Panasyuk (editor), Fracture Mechanics of Materials and Strength of Structures [in Ukrainian], Karpenko Physicomechanical Institute, Ukrainian Academy of Sciences, Lviv (2004), pp. 457-464.
18. O. P. Ostash, V. M. Uchanin, I. M. Andreiko, and Yu. V. Holovatyuk, A Method for Determination of the Size of the Prefracture Zone [in Ukrainian], Patent of Ukraine, No. 64240A, Publ. 16.02.2004, Bull. No. 2 (2004).
19. O. P. Ostash, R. V. Chepil', V. V. Vira, and V. T. Zhmur-Klymenko, "Prediction of the durability of cyclically loaded constructional elements," Fiz.-Khim. Mekh. Mater., 41, No. 4, 39-44 (2005).