Failure analysis of gas turbine blades in a thermal power plant

Engineering Failure Analysis

Volumn 14, Issue 4, 2007, Pages 743-749

  Vardar, N ^a   Ekerim, A ^a  

^a YILDIZ TECHNICAL UNIVERSITY   (Turkey)

Author keywords

Carbide film; Crack; Failure; Gas turbine blade failure; Gas turbine blades

Indexed keywords

CRACK INITIATION; CRACK PROPAGATION; CRACKS; FAILURE ANALYSIS; GAS TURBINES; GRAIN BOUNDARIES; TURBOMACHINE BLADES;

FAILURE MECHANISM; GAS TURBINE BLADES; INTERGRANULAR CRACKS; THERMAL POWER PLANT;

GAS TURBINE POWER PLANTS;

CRACK INITIATION; CRACK PROPAGATION; CRACKS; FAILURE ANALYSIS; GAS TURBINE POWER PLANTS; GAS TURBINES; GRAIN BOUNDARIES; TURBOMACHINE BLADES;

EID: 33846321591     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfailanal.2006.06.001     Document Type: Article

References (11)

1. Eliaz N., Shemesh G., and Latanision R.M. Hot corrosion in gas turbine components. Eng Failure Anal 9 (2002) 31-43
2. Gallardo J.M., Rodriguez J.A., and Herrera E.J. Failure of gas turbine blades. Wear 252 (2002) 258-264
3. Mazur Z., Luna-Ramirez A., Juarez-Islas J.A., and Campos-Amezcua A. Failure analysis of a gas turbine blade made of Inconel 738LC alloy. Eng Failure Anal 12 (2005) 474-486
4. Khajavi M.R., and Shariat M.H. Failure of first stage gas turbine blades. Eng Failure Anal 11 (2004) 589-597
5. Chang J.C., Yun Y.H., Choi C., and Kim J.C. Failure analysis of gas turbine buckets. Eng Failure Anal 10 (2003) 559-567
6. Hou J., Wicks B.J., and Antoniau R.A. An investigation of fatigue failures of turbine blades in a gas turbine engine by mechanical analysis. Eng Failure Anal 9 (2002) 201-211
7. Park M., Hwang Y.H., Choi Y.S., and Kim T.G. Analysis of a J69-T-25 engine turbine blade fracture. Eng Failure Anal 9 (2002) 593-601
8. ASM Metals Handbook - Atlas of microstructures of industrial alloys, 1973.
9. Libera M. "Fracture, fatigue and creep". Available from: , 2005, Chapter 6.
10. Bacos M.P., Morel A., Naveos A., Bachelier-locq A., Josso P., and Thomas M. The effect of long term exposure in oxidizing and corroding environments on the tensile properties of two gamma-TiAl alloys. Intermetallics 14 (2006) 102-113
11. Lukas P., Kunz L., and Svoboda M. High-temperature ultra-high cycle fatigue damage of notched single crystal superalloys at high mean stresses. Int J Fatigue 27 (2005) 1535-1540