Evaluation of microstructural parameters in 9-12% Cr-steels

International Journal of Pressure Vessels and Piping

Volumn 84, Issue 1-2, 2007, Pages 62-68

  Maile, K ^a  

^a UNIVERSITY OF STUTTGART   (Germany)

Author keywords

EFTEM; Martensitic steels; Microstructure; TEM

Indexed keywords

COMPOSITION EFFECTS; CRYSTAL MICROSTRUCTURE; HEAT TREATMENT; MARTENSITE; TRANSMISSION ELECTRON MICROSCOPY;

MARTENSITIC STEELS; PRECIPITATION REACTION;

STEEL;

COMPOSITION EFFECTS; CRYSTAL MICROSTRUCTURE; HEAT TREATMENT; MARTENSITE; STEEL; TRANSMISSION ELECTRON MICROSCOPY;

EID: 33846289624     PISSN: 03080161     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijpvp.2006.09.012     Document Type: Article

References (4)

1. Zies G. Determination of microstructure of the new 9-12% Cr Heat Resistant Steels. Final report, project D17, COST 522 steam turbines, MPA, Universität Stuttgart, 2003.
2. Liu XY., and Fujita T. Effect of chromium on creep strength rupture properties of a high chromium ferritic heat resisting steel. ISIJ Int 29 88 (1989) 680-686
3. Andrén, H-O, J. Agren. Creep behaviour and life assessment of modified 12% chromium steels. COST 522 final report, Chalmers University of Technology, Göteborg, Sweden.
4. Rauch M, Maile K, Reuter A, Seliger P. Charakterisierung der Schädigungsentwicklung zur Lebensdauerbewertung von Rohrleitungskomponenten aus den neuen 9%-Chromstählen. Forschungsvorhaben A152 gefördert durch die Stiftung Stahlanwendungsforschung im Stifterverband für die deutsche Wissenschaft e.V., Wirtschaftsverband Stahlbau und Energietechnik (SET), Abschlußbericht MPA Universität Stuttgart, 2004.