Volumn 23, Issue 2, 2007, Pages 133-137
|
|
Stress corrosion cracking of NiTi in artificial saliva
a
|
|
Author keywords
Constant loading; Failure analysis; NiTi shape memory alloy; Orthodontic; Saliva; Stress corrosion cracking
|
|
Indexed keywords
ANODIC POLARIZATION;
DENTISTRY;
ENERGY DISPERSIVE SPECTROSCOPY;
FAILURE ANALYSIS;
NICKEL COMPOUNDS;
SCANNING ELECTRON MICROSCOPY;
SHAPE MEMORY EFFECT;
CONSTANT LOADING;
CRACK LENGTH;
SALIVA;
STRESS CORROSION CRACKING;
CHLORINE;
DENTAL ALLOY;
NICKEL;
OXYGEN;
PHOSPHORUS;
POTASSIUM;
SALIVA SUBSTITUTE;
SODIUM;
SULFUR;
TITANIUM;
TITANIUM NICKELIDE;
UNCLASSIFIED DRUG;
ARTICLE;
CHEMISTRY;
CORROSION;
ELECTRON PROBE MICROANALYSIS;
EQUIPMENT;
HUMAN;
MATERIALS TESTING;
MECHANICAL STRESS;
ORTHODONTIC DEVICE;
PH;
SCANNING ELECTRON MICROSCOPY;
SURFACE PROPERTY;
CHLORINE;
CORROSION;
DENTAL ALLOYS;
ELECTRON PROBE MICROANALYSIS;
EQUIPMENT FAILURE;
HUMANS;
HYDROGEN-ION CONCENTRATION;
MATERIALS TESTING;
MICROSCOPY, ELECTRON, SCANNING;
NICKEL;
ORTHODONTIC WIRES;
OXYGEN;
PHOSPHORUS;
POTASSIUM;
SALIVA, ARTIFICIAL;
SODIUM;
STRESS, MECHANICAL;
SULFUR;
SURFACE PROPERTIES;
TITANIUM;
|
|
EID: 33846048959
PISSN: 01095641
EISSN: None
Source Type: Journal
DOI: 10.1016/j.dental.2006.01.001 Document Type: Article |
|
Times cited : (49)
|
|
References (8)
|