Microstructure and mechanical properties of spray-deposited Al-10.8Zn-2.8Mg-1.9Cu alloy after two-step aging treatment at 110 and 150 °C

Materials Characterization

Volumn 58, Issue 1, 2007, Pages 82-86

  Wang, Feng ^a   Xiong, Baiqing ^a   Zhang, Yongan ^a   Zhu, Baohong ^a   Liu, Hongwei ^a   Wang, Zixing ^a   He, Xiaoqing ^a  

^a GENERAL RESEARCH INSTITUTE FOR NONFERROUS METALS   (China)

Author keywords

Aging; Al Zn Mg Cu alloy; Microstructure; Precipitate

Indexed keywords

GRAIN BOUNDARIES; HEAT TREATMENT; MECHANICAL PROPERTIES; MICROSTRUCTURE; PRECIPITATION (CHEMICAL); SPRAYED COATINGS;

AGING TREATMENT; AL-ZN-MG-CU ALLOYS; SCC RESISTANCE;

ALUMINUM COPPER ALLOYS;

EID: 33846028529     PISSN: 10445803     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.matchar.2006.04.004     Document Type: Article

References (7)

1. Engdahl T., Hansen V., Warren P.J., and Stiller K. Investigation of fine scale precipitates in Al-Zn-Mg alloys after various heat treatments. Mater Sci Eng A327 (2002) 59-64
2. Ramgopal T., Gouma P.I., and Frankel G.S. Role of grain-boundary precipitates and solute-depleted zone on the intergranular corrosion of aluminum alloy 7150. Corrosion 58 8 (2002) 687-697
3. Puiggali M., Zielinski A., Olive J.M., Renauld E., Desjardins D., and Cid M. Effect of microstructure on stress corrosion cracking of an Al-Zn-Mg-Cu alloy. Corros Sci 40 (1998) 805-819
4. Singh P.M., and Lewandowski J.J. Effects of heat treatment on stress corrosion cracking of a discontinuously reinforced aluminium 7XXX alloy during slow strain rate testing. Scr Mater 33 9 (1995) 1393-1399
5. Sharma M.M., Amateau M.F., and Eden T.J. Mesoscopic structure control of spray formed high strength Al-Zn-Mg-Cu alloys. Acta Mater 53 (2005) 2919-2924
6. Salamci E. Ageing behaviour of spray cast Al-Zn-Mg-Cu alloys. Turk J Eng Environ Sci 25 (2001) 81-86
7. Deshais G., and Newcomb S.B. The influence of microstructure on the formation of stress corrosion cracks in 7XXX series aluminium alloys. Mater Sci Forum 313-317 (2000) 1635-1640