Effect of reactive element yttrium on oxidation behavior of K38G superalloy at 800 °C in air

Corrosion Science and Protection Technology

Volumn 18, Issue 3, 2006, Pages 183-186

  Yu, Ping ^a,b   Wang, Ya Quan ^a   Wang, Wen ^c  

^a TIANJIN UNIVERSITY   (China)

^b SHENYANG UNIVERSITY OF CHEMICAL TECHNOLOGY   (China)

^c INSTITUTE OF METAL RESEARCH   (China)

Author keywords

High temperature oxidation; K38G; Rare earth element; Superalloy; Yttrium

Indexed keywords

ADDITION REACTIONS; OXIDATION; REACTION KINETICS; SUPERALLOYS;

EID: 33845716748     PISSN: 10026495     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (9)

1. R Cueff, H Buscail, E Caudron, et al. Oxidation of alumina formers at 1173K:effect of yttrium ion implantation and yttrium alloying addition[J].Corrosion Science, 2003, 45(8):1815.
2. F A Golightl, F H Stott, G C Wood. The influence of yttrium additions on the oxide-scale adhesion to an iron-chromium-aluminum alloy[J]. Oxid. Met., 1976, 10:163.
3. 2 alloy[J]. Corrosion Science, 1999, 41(5):901.
4. B A Pint. Experimental observations in support of the dynamic-segregation theory to explain the reactive-element effect[J]. Oxid. Met., 1996, 45(1/2):1.
5. A Rahmel, M Schutze. Mechanical aspects of the rare-earth effect[J]. Oxid Met., 1992, 38:255.
6. G Fisher, P K Datta, J S Burnell-Gray, et al. The effects of active element additions on the oxidation performance of a platinum aluminide coating at 1100 °C [J]. Surf. Coat. Tech., 1998, 110:24.
7. J Stringer, B A Wilcox, R I Jaffee. The high-temperature oxidation of nickel-20wt. % chromium alloys containing dispersed oxide phases[J]. Oxid Met., 1972, 5:11.
8. W J Quadakkers, M J Bennett. Oxidation induced lifetime limits of thin walled, iron based, alumina forming, oxide dispersion strengthened alloy components [J]. Mater. Sci. and Technol., 1994, 10(1):126.
9. Z Liu, W Gao, Y He. Modeling of oxidation kinetics of Y-Doped Fe-Cr-Al alloys [J]. Oxid Met., 1999, 53:341.