Damage modelling of adhesively bonded joints

International Journal of Fracture

Volumn 141, Issue 1-2, 2006, Pages 147-161

  Liljedahl, C D M ^a   Crocombe, A D ^a   Wahab, M A ^a   Ashcroft, I A ^b  

^a UNIVERSITY OF SURREY   (United Kingdom)

^b LOUGHBOROUGH UNIVERSITY   (United Kingdom)

Author keywords

Adhesive joint; Cohesive zone modelling; Failure prediction; Plasticity

Indexed keywords

ADHESIVE JOINTS; ADHESIVES; CRACK PROPAGATION; ELASTICITY; ELASTOPLASTICITY; FAILURE (MECHANICAL); MATHEMATICAL MODELS; SHEAR STRESS;

COHESIVE ZONE MODEL; FAILURE PREDICTION;

FRACTURE MECHANICS;

EID: 33845330277     PISSN: 03769429     EISSN: 15732673     Source Type: Journal    
DOI: 10.1007/s10704-006-0072-9     Document Type: Article

References (28)

1. ABAQUS6.3/Standard User's Manual 24.2.9. Hibitt, Karlsson & Sorensen Inc.
2. ABAQUS 6.3/Explicit User's Manual 16.2.1. Hibitt, & Sorensen Inc.
3. ABAQUS 6.3 Standard User's Manual 11.3.1. Hibitt, Karlsson & Sorensen Inc.
4. ABAQUS 6.3/Explicit User's Manual 10.3.1. Hibitt, & Sorensen Inc.
5. RD Adams RW Atkins JA Harris AJ Kinloch 1988 Stress-analysis and failure properties of carbon-fibre-reinforced-plastic steel double lap joints J Adhes 20 29-33
6. RD Adams JA Harris 1987 The influence of local geometry on the strength of adhesively bonded joints Int J Adhes Adhes 7 2 69-80 10.1016/ 0143-7496(87)90092-3
7. RD Adams NA Peppiat 1974 Stress analysis of adhesively-bonded lap joints J Strain Anal 9 3 185-196
8. AR Akisanya CS Meng 2003 Initiation of fracture at the interface corner of biomaterial joints J Mech Phys Solids 51 27-46 01929462 10.1016/ S0022-5096(02)00076-5
9. T Andersen U Stigh 2004 The stress-elongation relation for an adhesive layer loaded in peel using equilibrium of energetic forces Int J Solids Struct 41 413-434 10.1016/j.ijsolstr.2003.09.039
10. SR Chowdury R Narasimhan 2000 A finite element analysis of quasistatic crack growth in a pressure sensitive constrained ductile layer Eng Frac Mech 66 551-571 10.1016/S0013-7944(00)00033-3
11. AD Crocombe RD Adams 1982 An elastoplastic investigation of the peel test J Adhes 13 3-4 241-267
12. Krueger R, Paris IL, O'Brien TK, Minguet PJ (2001) Fatigue life methodology for bonded composite skin/stringer configurations, NASA/ TM-2001-210842 ARL-TR-2432, National Aeronautics and Space Administration, Langely Research Center, Hampton, Virginia
13. H Li N Chandra 2003 Analysis of crack growth and crack-tip plasticity in ductile materials using cohesive zone models Int J Plast 19 849-882 01901759 10.1016/S0749-6419(02)00008-6
14. S Li MD Thouless AM Waas JA Schroeder PD Zavattieri 2005a Mode-I cohesive-zone models for fracture of an adhesively bonded polymer-matrix composite Comp Sci Technol 65 2 281-293 10.1016/j.compscitech.2004.07.009
15. S Li MD Thouless AM Waas JA Schroeder PD Zavattieri 2005 Use of cohesive-zone models to analyze fracture of a fiber-reinforced polymer-matrix composite Comp Sci Technol 65 3-4 537-549 10.1016/ j.compscitech.2004.08.004
16. WK Loh AD Crocombe MA Wahab IA Ashcroft 2003 Modelling interfacial degradation using interfacial rupture elements J Adhes 79 12 1135-1160
17. WK Loh AD Crocombe MM Abdel Wahab IA Ashcroft 2005 Modelling anomalous moisture uptake, swelling and thermal characteristics of a rubber toughened epoxy adhesive Int J Adhes Adhes 25 1-12 10.1016/ j.ijadhadh.2004.02.002
18. KS Madhusudhana R Narasimhan 2002 Experimental and numerical investigations of mixed mode crack resistance of ductile adhesive joint Eng Frac Mech 69 865-885 10.1016/S0013-7944(01)00110-2
19. T Schön T Nyman A Blom H Ansell 2000 A numerical and experimental investigation of delamination behaviour in a DCB specimen Comp Sci Techno 60 2 173-184 10.1016/S0266-3538(99)00113-X
20. A Shirani KM Liechti 1998 A calibrated fracture process zone model for thin film blistering Int J Frac 93 281-314 10.1023/A:1007548519223
21. BF Sorensen TK Jacobsen 2003 Determination of cohesive laws by the J-Integral approach Eng Frac Mech 70 1842-1858 10.1016/ S0013-7944(03)00127-9
22. V Tvergaard JW Hutchinson 1992 The relation between crack growth resistance and fracture process parameters in elastic-plastic solids J Mech Phys Solids 40 6 1377-1397 0775.73218 10.1016/0022-5096(92)90020-3
23. V Tvergaard JW Hutchinson 1993 The influence of plasticity on mixed mode interface toughness J Mech Phys Solids 41 6 1119-1135 0775.73219 10.1016/ 0022-5096(93)90057-M
24. V Tvergaard JW Hutchinson 1996 On toughness of ductile adhesive joints J Mech Phys Solids 44 5 789-800 10.1016/0022-5096(96)00011-7
25. V Tvergaard 2001 Resistance growth of mixed mode interface crack growth between dissimilar elastic-plastic solids J Mech Phys Solids 49 11 2689-2703 0991.74062 10.1016/S0022-5096(01)00074-6
26. D Xie AM Waas KW Shahwan JA Schroeder R G Boeman 2005 Fracture criterion for kinking cracks in a tri-material adhesively bonded joint under mixed mode loading Eng Frac Mech 72 2487-2504 10.1016/j.engfracmech.2005.03.008
27. QD Yang MD Thouless SM Ward 2001 Elastic-plastic mode-II fracture of adhesive joints Int J Solids Struct 38 3251-3262 1012.74545 10.1016/ S0020-7683(00)00221-3
28. CH Wang P Chalkley 2000 Plastic yielding of a film adhesive under multiaxial stresses Int J Adhes Adhes 20 2 155-164 0970.93034 10.1016/ S0143-7496(99)00033-0