Mechanical property degradation of a Nicalon fiber reinforced SiNC ceramic matrix composite under thermal shock loading

Composite Structures

Volumn 78, Issue 4, 2007, Pages 477-485

  Salekeen, Sirajus ^a   Amoako, Justice Nana ^a   Mahfuz, Hassan ^a   Jeelani, Shaik ^a  

^a TUSKEGEE UNIVERSITY   (United States)

Author keywords

Acoustic emission; Ceramic matrix composites; Thermal shock

Indexed keywords

ACOUSTIC EMISSIONS; DEGRADATION; FAILURE ANALYSIS; FRACTURE TOUGHNESS; MECHANICAL PROPERTIES; QUENCHING; SCANNING ELECTRON MICROSCOPY; TENSILE TESTING; THERMAL LOAD;

FIBER PULLOUT; STRESS-STRAIN RELATIONSHIP; THERMAL SHOCK CYCLES; THERMAL SHOCK TEMPERATURE;

CERAMIC MATRIX COMPOSITES;

ACOUSTIC PROPERTY; CERAMIC MATRIX; DEGRADATION; FAILURE ANALYSIS; FIBER REINFORCED COMPOSITE; MECHANICAL PROPERTY; SCANNING ELECTRON MICROSCOPY; TEMPERATURE EFFECT; TENSILE PROPERTY; TESTING;

EID: 33751514560     PISSN: 02638223     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compstruct.2005.11.016     Document Type: Article

References (34)

1. Wang H., and Singh R.N. Thermal shock behavior of ceramics and ceramic composites. Int Mat Rev 39 (1994) 228-244
2. Hasselman D.P.H. Unified theory of thermal shock fracture initiation and crack propagation in brittle ceramics. J Am Ceram Soc 52 (1969) 600-604
3. Boccaccini A.R., Janczak-Rusch J., Pearce D.H., and Kern H. Assessment of damage by thermal shock in SiC-fiber reinforced borosilicate glass composite. Comp Sci Techn 59 (1999) 105-112
4. Wang H., Singh R.N., and Lowden R.A. Thermal shock behavior of two dimensional woven fiber-reinforced ceramic composites. J Am Ceram Soc 79 (1996) 1783-1792
5. Wiederhorn S.M., and Hockey B.J. Ceramics Intl 17 (1991) 243
6. Klug T., Reichert J., and Brckner R. Thermal shock behavior of SiC-fiber-reinforced glasses. Glastech Ber 65 (1992) 41-49
7. Shin D.-W., Auh K.H., and Knowles K.M. SiC fiber/borosilicate glass composite (part 3). J Ceram Soc Japan 103 (1995) 533-540
8. Kagawa Y., Kurosawa N., and Kishi T. Thermal shock resistance of SiC fiber-reinforced borosilicate glass and lithium aluminosilicate matrix composites. J Mat Sci 28 (1993) 735-741
9. Zawada L.P., and Wetherhold R.C. The effects of thermal fatigue on a SiC fiber/aluminosilicate glass composite. J Mat Sci 26 (1991) 648-654
10. Wang H., and Singh R.N. Thermal shock behavior of fiber reinforced ceramic composites. Mat Res Soc Symp Proc 365 (1995) 441-447
11. Harris B., Habib F.A., and Cooke R.G. Matrix cracking and the mechanical behavior of SiC/CAS composites. Proc Roy Soc London A 437 (1992) 109
12. Chen O., Karandikar P., Takeda N., Kishi T., Tredway R., and Prewo K. Acoustic emission characterization of the fracture mechanism of a glass-matrix composite. Ceram Eng Sci Proc (1991) 1586-1598
13. Kim R, Pegano N. Crack Initiation in unidirectional brittle composite. J Am Ceram Soc 199;74:1082.
14. Evans A.G., and Marshall D.B. Acta Met 37 (1989) 2567-2583
15. Huchinson J.W., and Jenson H.M. Mech Mater 9 (1990) 139
16. Chawla K.K. Ceramic matrix composites composites. second ed. (2003), Kluwer Academic Publishers, Boston p. 81
17. Blisset M.J., Smith P.A., and Yeomans J.A. Thermal shock behavior of unidirectional silicon carbide fiber reinforced calcium aluminosilicate. J Mater Sci 32 (1997) 317-325
18. Lundberg L., Pompe R., and Carlsson R. Comp Sci Tech 37 (1990) 165
19. Sirieix F., Goursat P., Lecomte A., and Dauger A. Comp Sci Tech 37 (1990) 7
20. Sato K, Morozumi H, Tezuka A, Funayama O, Isoda T. High Temperature Ceramic-Matrix Composite II. Am Ceram Soc Westerville, OH, 1995:199.
21. Gonon M.F., Fantozzi G., Murat M., and Disson J.P. J Eur Ceram Soc 15 (1995) 185
22. 0, and 2-D woven fiber reinforced CVI SiC matrix composites. J Mater Sci 32 (1997) 3305-3313
23. Takeda N., Chen O., Kishi T., Tredway W., and Prewo K. Acoustic emission characterization of the fracture mechanism of a high compliant glass-matrix composite. Eng Fract Mech 40 (1991) 791-799
24. Kageyama K, Enoki M, Kishi T. Effect of microfracture process on fracture toughness in fine particulate glass composites. In: Proceedings of the 3rd Japan SAMPE, Symposium, 1993. p. 2081-86.
25. Twitty A., Russell-Floyd R.S., Cooke R.G., and Harris B. Thermal shock resistance of nextel/silica-zirconia ceramic-matrix composites manufactured by freeze-gelation. J Eur Ceram Soc 15 (1995) 455
26. Plucknett K.P., Cain R.L., and Lewis M.H. Interface degradation in CAS/Nicalon during elevated temperature aging. Proc Mater Res Soc Symp 365 (1995) 421-426
27. Daniel A.M., Martin-Meizoso A., Plucknett K.P., Lewis M.H., and Braski D.N. Interface modification during oxidation of a glass-ceramic marix/SiC fiber composite. Ceram Eng Sci Proc 17 (1996) 280-287
28. Brennan J.J. Tailoring multiphase and composite ceramics. Mater Sci Res 20 (1986) 549-560
29. Cooper R.F., and Chung K. Structure and chemistry of fiber-matrix interfaces in silicon carbide fiber-reinforced glass-ceramic composites: an electron microscopy analysis. J Mater Sci 22 (1987) 3148-3160
30. Bonney L.A., and Cooper R.R. Reaction-layer interfaces in SiC-fiber-reinforced glass-ceramics: a high resolution scanning transmission electron microscopy analysis. J Am Ceram Soc 73 10 (1990) 2916-2921
31. Tortorelli P.F., Nijhawan S., Reister L., and Lowden R.A. Ceram Eng Sci Proc 14 7&8 (1993) 358
32. Jones R.H., Hanager C.H., and Tortorelli P.F. JOM 45 (1993) 26
33. Evans A.G., Zok F.W., McMeeking R.M., and Du Z.Z. Models of high-temperature, environmentally-assisted embrittlement in ceramic-matrix composites. J Am Cer Soc 79 9 (1996) 2345-2352
34. Ogbuji L.U.A. Pervasive mode of oxidative degradation in a SiC-SiC composite. J Am Cer Soc 81 11 (1998) 2777-2784