Epoxidation and deoxygenation of single-walled carbon nanotubes: Quantification of epoxide defects

Journal of the American Chemical Society

Volumn 128, Issue 35, 2006, Pages 11322-11323

  Ogrin, Douglas ^a   Chattopadhyay, Jayanta ^a   Sadana, Anil K ^a   Billups, W Edward ^a   Barron, Andrew R ^a  

^a RICE UNIVERSITY   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

CARBON NANOTUBE; EPOXIDE; NANOTUBE;

ARTICLE; DEOXYGENATION; EPOXIDATION; INFRARED SPECTROSCOPY; PHOSPHORUS NUCLEAR MAGNETIC RESONANCE; RAMAN SPECTROMETRY; X RAY PHOTOELECTRON SPECTROSCOPY;

EID: 33748373178     PISSN: 00027863     EISSN: None     Source Type: Journal    
DOI: 10.1021/ja061680u     Document Type: Article

References (18)

1. Mawhinney, D. B.; Naumenko, V.; Kuznetsova, A.; Yates, J. T., Jr.; Liu, J.; Smalley, R. E. J. Am. Chem. Soc. 2000, 122, 2383.
2. Lu, X.; Yuan, Q.; Zhang, Q. Org. Lett. 2003, 5, 3527.
3. Murray, R. W. Chem. Rev. 1989, 89, 1187.
4. 2 (20 mL) was added to the reaction mixture, and the mixture was filtered through a 0.2 μm PTFE membrane filter paper and dried in vacuo at 80 °C.
5. 2 (60 mL). After the solid has completely dissolved, purified SWNTs (40 mg, 3.3 mmol) were added, and the solution was stirred overnight. The reaction mixture was filtered through a 0.2 μm PTFE membrane filter paper and dried in vacuo at 80 °C.
6. Creegan, K. M.; Robbins, J. L.; Robbins, W. K.; Millar, J. M.; Sherwood, R. D.; Tindall, P. J.; Cox, D. M.; Smith, A. B., III; McCauley, J. P., Jr.; Jones, D. R.; Gallagher, R. T. J. Am. Chem. Soc. 1992, 114, 1103.
7. Zhang, L.; Zhang, J.; Schmandt, N.; Cratty, J.; Khabashesku, V. N.; Kelly, K. F.; Barron, A. R. Chem. Commun. 2005, 5429.
8. (a) Gurudutt, K. N.; Ravindranath, B. Tetrahedron Lett. 1980, 21, 1173.
9. (b) Kim, S.; Kim, K. H. J. Chem. Soc., Perkin Trans. 1 1997, 1095.
10. (c) Alper, H.; Des Roches, D. Tetrahedron Lett. 1977, 18, 4155.
11. (d) Zhu, Z.; Espenson, J. H. J. Mol. Catal. A 1995, 103, 87.
12. Ogrin, D.; Barron, A. R. J. Mol. Catal. A 2006, 244, 267.
13. 3 (25.46 ppm) was determined.
14. n was known by both MALDI-TOF MS and HPLC.
15. Dresselhaus, M. S.; Pimenta, M. A.; Ecklund, P. C.; Dresselhaus, G. Raman Scattering in Materials Science; Webber, W. H., Merlin, R., Eds.; Springer-Verlag: Berlin, 2000.
16. Rinzler, A. G.; Liu, J.; Dai, H.; Nikolaev, P.; Huffman, C. B.; Rodríguez-Macías, F. J.; Boul, P. J.; Lu, A. H.; Heymann, D.; Colbert, D. T.; Lee, R. S.; Fischer, J. E.; Rao, A. M.; Eklund, P. C.; Smalley, R. E. Appl. Phys. A: Mater. Sci. Process. 1998, 67, 29.
17. Lian, Y.; Maeda, Y.; Wakahara, T.; Akasaka, T.; Kazaoui, S.; Minami, N.; Shimizu, T.; Choi, N.; Tokumoto, H. J. Phys. Chem. B 2004, 108, 8848.
18. Gu, Z.; Smalley, R. E., personal communication.