Tensile and corrosion behavior of Zr705 for nuclear hydrogen generation

Materials Science and Engineering: A

Volumn 427, Issue 1-2, 2006, Pages 320-326

  Roy, Ajit K ^a   Kaiparambil, Ancila V ^a  

^a Las Vegas   (United States)

Author keywords

Applied potential; Fractography; Stress corrosion cracking; Zr705

Indexed keywords

CRACKS; DECOMPOSITION; DUCTILITY; FAILURE (MECHANICAL); FRACTOGRAPHY; HYDROGEN; STRAIN; STRESS CORROSION CRACKING; TENSILE STRENGTH; THERMAL EFFECTS;

CRACKING SUSCEPTIBILITY; FAILURE STRAIN; NUCLEAR HYDROGEN GENERATION; SLOW-STRAIN-RATE (SSR);

ZIRCONIUM METALLURGY;

CRACKS; DECOMPOSITION; DUCTILITY; FAILURE (MECHANICAL); FRACTOGRAPHY; HYDROGEN; STRAIN; STRESS CORROSION CRACKING; TENSILE STRENGTH; THERMAL EFFECTS; ZIRCONIUM METALLURGY;

EID: 33746940423     PISSN: 09215093     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.msea.2006.04.109     Document Type: Article

References (20)

1. O'Keefe D., Allen C., Besenbruch G., Brown L., Norman J., and Sharp R. Int. J. Hydrogen Energy 7 5 (1982) 381-392
2. Murhammer D. Outlook vol. 5, no. 3 (Summer 1984)
3. Abraham M. Outlook vol. 24, no. 1 (First Quarter 2003)
4. Te-Lin Y. Corros.-NACE 39 5 (1983) 167-174
5. Zaritskii V. Chem. Pet. Eng. 26 7-8 (1991) 374-375
6. Purdy I.M., and Todd J.A. IEEE/NPSS Symposium on Fusion Engineering, vol. 2 (1995) 1178-1181
7. ASTM Designation E 8, Standard Test Methods for Tension Testing of Metallic Materials, American Society for Testing and Materials (ASTM) International, 2004.
8. Corrosion Testing Equipment, Cortest, Incorporated, http://www.cortest.com.
9. ASTM Designation G 129, Standard Practice for Slow Strain Rate Testing to Evaluate the Susceptibility of Metallic Materials to Environmentally Assisted Cracking, American Society for Testing and Materials (ASTM) International, 2000.
10. Roy A.K., Valliyil U., and Govindaraj E. J. ASTM Int. 3 April (4) (2006) 1-11
11. ASTM Designation G 5-94, Standard Reference Test Method for Making Potentiostatic and Potentiodynamic Anodic Polarization Measurements, American Society for Testing and Materials (ASTM) International, 1999.
12. ASTM Designation G 38, Standard Practice for Making and Using C-Ring Stress-Corrosion Test Specimens, American Society for Testing and Materials (ASTM) International, 2001.
13. P.E. Danielson, ASM Handbook, Metallography and Microstructures, vol. 9, ninth ed., American Society for Metals, 2000, pp. 497-502.
14. x decomposition, M.S. Thesis, Department of Mechanical Engineering, University of Nevada, Las Vegas, December 2005.
15. Lustman B., and Kerze Jr. F. The Metallurgy of Zirconium. first ed. (1955), McGraw-Hill Book Company
16. Hammad A.M., El-Mashri S.M., and Nasr M.A. J. Nucl. Mater. 186 (1992) 166-176
17. Thorpe W.R., and Smith I.O. J. Nucl. Mater. 78 (1978) 49-57
18. Thorpe W.R., and Smith I.O. J. Nucl. Mater. 80 (1979) 35-42
19. U. Valliyil, The role of applied potential on cracking of zircaloy-2, M.S. Thesis, Department of Mechanical Engineering, University of Nevada, Las Vegas, August 2005.
20. E. Govindaraj, Corrosion study of zirconium alloys under controlled cathodic potential, M.S. Thesis, Department of Mechanical Engineering, University of Nevada, Las Vegas, August 2005.