Quantitative fractography of 2205 duplex stainless steel after a sulfide stress cracking test

Materials Characterization

Volumn 56, Issue 4-5 SPEC. ISS., 2006, Pages 384-388

  Klyk Spyra, Katarzyna ^a   Sozańska, Maria ^a  

^a SILESIAN UNIVERSITY OF TECHNOLOGY   (Poland)

Author keywords

Duplex stainless steel; Hydrogen embrittlement; Profile analysis; Quantitative fractography; Sulfide stress cracking

Indexed keywords

FRACTOGRAPHY; FRACTURE MECHANICS; HYDROGEN EMBRITTLEMENT; STRESS CORROSION CRACKING; SULFIDE CORROSION CRACKING; SURFACE ROUGHNESS;

DUPLEX STAINLESS STEEL; PROFILE ANALYSIS; QUANTITATIVE FRACTOGRAPHY; SULFIDE STRESS CRACKING;

STAINLESS STEEL;

EID: 33746846519     PISSN: 10445803     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.matchar.2005.11.017     Document Type: Article

References (8)

1. Girones A., Llanes L., Anglada M., and Mateo A. Influence of artificial seawater on the cyclic response of superduplex stainless steels. Int J Fatigue 27 (2005) 197-202
2. El-Yazgi A.A., and Hardie D. Stress corrosion cracking of duplex and super duplex stainless steels in sour environments. Corros Sci 40 (1998) 909-930
3. Liou H.Y., Hsieh R.I., and Tsai W.T. Microstructure and stress corrosion cracking in simulated heat-affected zones of duplex stainless steels. Corros Sci 44 (2002) 2841-2856
4. 2S refinery service, interaction of steels with hydrogen in petroleum industry pressure vessel service (1993), The Materials Properties Council Inc, New York
5. 2s-containing environments in oil and gas production. London, The Institute of Materials, 1995; 16:13-15.
6. 2S environments (1996)
7. Ryś J. Stereologia materiałów (1995), Fotobit-design, Kraków 323-358
8. Szala J. Computer program "Analiza profilu v 2,2" (2001), Silesian University of Technology, Department of Materials Science, Katowice