Embrittlement evaluation and lifetime assessment of hydrocracking pressure vessel made of 3Cr-1Mo low-alloy steel

Engineering Failure Analysis

Volumn 14, Issue 1, 2007, Pages 164-169

  Jahromi, S A Jenabali ^a   Najmi, M ^a  

^a SHIRAZ UNIVERSITY   (Iran)

Author keywords

3Cr 1Mo Low alloy steel; Crack growth; Hydrocracking pressure vessel; Temper embrittlement

Indexed keywords

BRITTLE FRACTURE; CHROMIUM ALLOYS; COMPUTATIONAL METHODS; CRACK PROPAGATION; DEFECTS; EMBRITTLEMENT; HIGH PRESSURE EFFECTS; HIGH TEMPERATURE EFFECTS; SERVICE LIFE; STEEL;

EMBRITTLEMENT EVALUATION; HYDROCRACKING PRESSURE VESSEL; LIFETIME ASSESSMENT; TEMPER EMBRITTLEMENT;

PRESSURE VESSELS;

BRITTLE FRACTURE; CHROMIUM ALLOYS; COMPUTATIONAL METHODS; CRACK PROPAGATION; DEFECTS; EMBRITTLEMENT; HIGH PRESSURE EFFECTS; HIGH TEMPERATURE EFFECTS; PRESSURE VESSELS; SERVICE LIFE; STEEL;

EID: 33746640139     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfailanal.2005.11.009     Document Type: Article

References (16)

1. Viswanathan R. Damage Mechanisms and life Assessment of high temperature components. 1995.
2. Kermad A., et al. PVP Vol. 336 (1996), ASME pp. 231-66
3. Schlögl S.M., et al. Metall Trans A 31A (2000) 125-137
4. Coudreuse L., et al. PVP Vol. 336 (1996), ASME pp. 49-59
5. Iwadate T., et al. Corrosion 44 2 (1988) 103-112
6. Iwadate T., et al. J Pressure Vessel Tech 107 (1985) 230-238
7. Charkravartty JK et al. Advances in fracture research. In: 6th international conference on fracture, vol. 4; 1984. p. 2419-26.
8. Hippsley C.A., and Lewandowski J.J. Metall Trans A 19A (1998) 3005-3011
9. Bowker J, et al. Advances in fracture research. In: 6th international conference on fracture. vol. 4; 1984 p. 2371-8.
10. Shigley JE. Mechanical engineering design. 6th ed., 2001.
11. Benham PP, Crawford RJ. Mechanics of engineering materials. 1990, p. 392-9.
12. Fitness-for- service, API RP 579, American Petroleum Institute, 2000.
13. Schlögl S.M., and Vander Giessen E. Mater Sci Forum 347-349 (2000) 628-633
14. Dieter GE. Mechanical metallurgy. 2nd ed. 1982, p. 513-6.
15. Anderson TL. Fracture mechanics: fundamental and application. 2nd ed., 1955, p.55-63.
16. Mc Henry H.I., et al. Corros Sci 27 10/11 (1987) 1041-1057