Fatigue crack growth and thresholds at ultrasonic frequencies

International Journal of Fatigue

Volumn 28, Issue 11, 2006, Pages 1456-1464

  Stanzl Tschegg, Stefanie ^a  

^a UNIVERSITY OF NATURAL RESOURCES AND LIFE SCIENCES   (Austria)

Author keywords

7075; Air humidity; Corrosion fatigue; Fatigue crack growth; Fatigue threshold; Load ratio; Strain rate; Ti 6Al 4V; Ultrasonic fatigue; Very high cycle fatigue

Indexed keywords

ALUMINUM ALLOYS; CRACK PROPAGATION; DIFFUSION; MONOLAYERS; TITANIUM ALLOYS; ULTRASONIC EFFECTS;

AIR HUMIDITY; FATIGUE THRESHOLD; LOAD RATIO; TI-6AL-4V; ULTRASONIC FATIGUE; VERY HIGH CYCLE FATIGUE;

FATIGUE OF MATERIALS;

EID: 33746381497     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2005.06.058     Document Type: Article

References (33)

1. Sakai T., Sato Y., and Oguma N. Characteristic S-N properties of high-carbon-chromium-bearing steel under axial loading in long-life fatigue. Fat Fract Eng Mater Struct 25 (2002) 765-773
2. Mughrabi H. Mechanisms of fatigue failure in ultralong life regime. Fat Fract Eng Mater Struct 25 (2002) 755-764
3. Murakami Y., Yokoyama N.N., and Nagata J. Mechanism of fatigue failure in ultralong life regime. Fat Fract Eng Mater Struct 25 (2002) 735-746
4. Tanaka K., and Akiniwa Y. Fatigue crack propagation behaviour derived from S-N data in very high cycle regime. Fat Fract Eng Mater Struct 25 (2002) 775H-784H
5. Stanzl-Tschegg S, High-cycle crack growth in the Paris- and threshold regime at ultrasonic frequencies. In: Soboyejo WO, Srivatsan, editors. High cycle fatigue of structural materials, TMS-ASM symposium proceedings in honor of P. Paris. TMS, Warrendale; 1997. p. 211.
6. -12 m/cycle by a time saving method. Metal Sci 14 4 (1980) 143-197
7. Holper B., Mayer H., Vasudevan A.K., and Stanzl-Tschegg S.E. Near threshold fatigue crack growth in aluminium alloys at low and ultrasonic frequency: Influences of specimen thickness, strain rate, slip behaviour and air humidity. Int J Fatigue 25 (2003) 397-411
8. Laird C, Charsley P. Strain rate sensitivity effects in cyclic deformation and fatigue fracture ultrasonic fatigue, The Metallurgical Society of AIME, PA; 1982. p. 187.
9. Taylor D., and Knott J.F. The effect of frequency on fatigue crack propagation rate. Proceedings of the 6th international conference on fracture vol. 3 (1984), Pergamon Press, Oxford
10. Shih Y.S., and Chen J.J. The frequency effect on the fatigue crack growth rate of 304 stainless steel. Nucl Eng Design 191 (1999) 225-230
11. Baik Y.M., and Kim K.S. The combined affect of frequency and load level on fatigue crack growth in stainless steel 304. Int J Fatigue 23 (2001) 417-425
12. Mayer H., Holper B., Zettl B., and Stanzl-Tschegg S.E. Slow fatigue crack growth in 2024-T3 and Ti-6Al-4V at low and ultrasonic frequency. Z Metallkd 94 5 (2003) 539-546
13. Holper B., Mayer H., Vasudevan A.K., and Stanzl-Tschegg S.E. Near threshold fatigue crack growth at positive load ratio in aluminium alloys at low and ultrasonic frequency; influences of strain rate, slip behaviour and air humidity. Int J Fatigue 26 (2004) 27-38
14. ASTM. ASTM Designation E647-00: Standard Test Method for Measurement of Fatigue Crack Growth Rates; 2000.
15. Stanzl S.E., Czegley M., Mayer H.R., and Tschegg E.K. Fatigue crack growth under combined mode I and mode II loading. Fracture mechanics, perspectives and directions, ASTM STP 1020 (1989) 479-496
16. Boyce B.L., and Ritchie R.O. Effect of load ratio and maximum stress intensity on fatigue threshold in Ti-6Al-4V. Eng Fract Mech 68 (2001) 129
17. Stanzl S.E., and Tschegg E.K. Fatigue crack growth and threshold behaviour at ultrasonic frequencies. Fracture mechanics, ASTM STP 791 II (1983) 3-18
18. Ricker R.E., and Duquette D.J. The role of hydrogen in corrosion fatigue of high purity Al-Zn-Mg exposed to water vapor. Metall Trans A 19A (1988) 1775-1783
19. Lynch S.P. Environmentally assisted cracking: overview of evidence for an adsorption-induced localised-slip process. Acta Metall Mater 36 10 (1988) 2639-2661
20. Wei R.P. Rate controlling processes and crack growth response. In: Bernstein I.M., Thompson A.W., and Bernstein I.M. (Eds). Hydrogen effects in metals (1980), TMS, Thompson (AW) 677
21. Holroyd N.J.H., and Hardie D. Factors controlling crack velocity in 7000 series aluminium alloys during fatigue in an aggressive environment. Corros Sci 23 6 (1983) 527-546
22. Tien J.K., Nair S., Bates R.C., and Buck O. Dislocation sweeping model for hydrogen assisted subcritical crack growth. Scripta Metall Mater 14 (1980) 591-594
23. Suresh S., Vasudevan A.K., and Bretz P.E. Mechanism of slow fatigue crack growth in high strength aluminium alloys: role of microstructure and environment. Metall Trans A 15 (1984) 369-379
24. Petit J., Fouquet J., and Henaff G. Influence of ambient atmosphere on fatigue crack growth behaviour of metals. In: Carpinteri A. (Ed). Handbook of fatigue crack propagation in metallic structures (1994), Elsevier, Amsterdam
25. Stanzl-Tschegg S.E., Mayer H.R., and Tschegg E.K. The influence of air humidity ion near-threshold fatigue crack growth of 2024-T3 aluminium alloy. Mater Sci Eng A 147 (1991) 45-54
26. Mayer H., Papakyriacou M., Pippan R., and Stanzl-Tschegg S. Influence of loading frequency on the high cycle fatigue properties of AlZnMgCu1.5 aluminium alloy. Mater Sci Eng A 314 (2001) 51-57
27. Papakyriacou M., Mayer H., Fuchs U., Stanzl-Tschegg S.E., and Wei R.P. Influence of atmospheric moisture on slow fatigue crack growth at ultrasonic frequency in aluminium and magnesium alloys. Fatigue Fract Eng Mater Struct 25 8/9 (2002) 795-804
28. Stanzl S., and Tschegg E. Influence of environment on fatigue crack growth in the threshold region. Acta Metall 29 (1981) 21-32
29. Stanzl S.E., and Tschegg E.K. Effect of environment on near-threshold fatigue crack growth at ultrasonic frequencies. Ultrasonic fatigue (1982), The Metallurgical Society of AIME, Pennsylvania, USA 553
30. Davidson D.L., and Lankford J. The effect of water vapor on fatigue crack tip mechanics in 7075-T651 aluminium alloy. Fatigue Fract Eng Mater Struct 6 (1983) 241
31. McEvily A.J., and Gonzalez-Velazquez J.L. Fatigue crack tip deformation process as influenced by the environment. Metall Trans A 23 (1992) 2211
32. Henaff G., Marchal K., and Petit J. On fatigue crack propagation enhancement by a gaseous atmosphere: experimental and theoretical aspects. Acta Metall 43 (1995) 2931
33. Vasudevan A.K., Sadananda K., and Louat N. A review of crack closure, fatigue crack threshold and related phenomena. Mater Sci Eng 188 (1994) 1