Numerical investigation of progressive damage and the effect of layup in notched tensile tests

Author keywords

Finite element analysis; Interface element; Notched strength; Progressive damage

Indexed keywords

DELAMINATION; EPOXY RESINS; FAILURE ANALYSIS; FINITE ELEMENT METHOD; GLASS; NUMERICAL METHODS; SURFACE TENSION;

EID: 33745616366     PISSN: 00219983     EISSN: 1530793X     Source Type: Journal    
DOI: 10.1177/0021998305057432     Document Type: Article
Times cited : (104)

References (25)
  • 1
    • 0034245464 scopus 로고    scopus 로고
    • Characteristics of Three-dimensional Stress Fields in Plates with a Through-the-thickness Crack
    • Kwon, S.W. and Sun, C.T. (2000). Characteristics of Three-dimensional Stress Fields in Plates with a Through-the-thickness Crack, International Journal of Fracture, 104 (3). 291-315.
    • (2000) International Journal of Fracture , vol.104 , Issue.3 , pp. 291-315
    • Kwon, S.W.1    Sun, C.T.2
  • 2
    • 0031073015 scopus 로고    scopus 로고
    • Interlaminar Stresses in Composite Laminates with a Circular Hole
    • Hu, F.Z., Soutis, C. and Edge, E.C. (1997). Interlaminar Stresses in Composite Laminates with a Circular Hole, Composite Structures, 37 (2). 223-232.
    • (1997) Composite Structures , vol.37 , Issue.2 , pp. 223-232
    • Hu, F.Z.1    Soutis, C.2    Edge, E.C.3
  • 3
    • 0025684079 scopus 로고
    • Damage Mechanics of Composite Materials I: Measurements of Damage Strength
    • Kortschot, M.T. and Beaumont, P.W.R. (1990). Damage Mechanics of Composite Materials I: Measurements of Damage Strength, Composites Science and Technology, 39 (4). 289-301.
    • (1990) Composites Science and Technology , vol.39 , Issue.4 , pp. 289-301
    • Kortschot, M.T.1    Beaumont, P.W.R.2
  • 4
    • 31344451583 scopus 로고    scopus 로고
    • Experimental Investigation of Progressive Damage and the Effect of Layup in Notched Tensile Tests
    • Hallett, S.R. and Wisnom, M.R. (2006). Experimental Investigation of Progressive Damage and the Effect of Layup in Notched Tensile Tests, Journal of Composite Materials, 40 (2). 119-141.
    • (2006) Journal of Composite Materials , vol.40 , Issue.2 , pp. 119-141
    • Hallett, S.R.1    Wisnom, M.R.2
  • 5
    • 0026627529 scopus 로고
    • Fatigue Damage Mechanics of Composite Materials II: A Damage Growth Model
    • Spearing, S.M., Beaumont, P.W.R. and Ashby, M.F. (1992). Fatigue Damage Mechanics of Composite Materials II: A Damage Growth Model, Composites Science and Technology, 44 (2). 169-177.
    • (1992) Composites Science and Technology , vol.44 , Issue.2 , pp. 169-177
    • Spearing, S.M.1    Beaumont, P.W.R.2    Ashby, M.F.3
  • 6
    • 0033324075 scopus 로고    scopus 로고
    • A Progressive Damage Methodology for Residual Strength Predictions of Notched Composite Panels
    • Coats, T.W. and Harris, C.E. (1999). A Progressive Damage Methodology for Residual Strength Predictions of Notched Composite Panels, Journal of Composite Materials, 33 (23). 2193-2224.
    • (1999) Journal of Composite Materials , vol.33 , Issue.23 , pp. 2193-2224
    • Coats, T.W.1    Harris, C.E.2
  • 7
    • 0022217124 scopus 로고
    • Role of Delamination and Damage Development on the Strength of Thick Notched Laminates
    • Harris, C.E. and Morris, D.H. (1985). Role of Delamination and Damage Development on the Strength of Thick Notched Laminates, Delamination and Debonding of Materials, ASTM STP 876, 424-447.
    • (1985) Delamination and Debonding of Materials, ASTM STP , vol.876 , pp. 424-447
    • Harris, C.E.1    Morris, D.H.2
  • 8
    • 0016080845 scopus 로고
    • Stress Fracture Criteria for Laminated Composites Containing Stress Concentrations
    • Whitney, J.M. and Nuismer, R.J. (1974). Stress Fracture Criteria for Laminated Composites Containing Stress Concentrations, Journal of Composite Materials, 8: 253-265.
    • (1974) Journal of Composite Materials , vol.8 , pp. 253-265
    • Whitney, J.M.1    Nuismer, R.J.2
  • 9
    • 0025597554 scopus 로고
    • Damage Mechanics of Composite Materials II: A Damage-based Notch Strength Model
    • Kortschot, M.T. and Beaumont, P.W.R. (1990). Damage Mechanics of Composite Materials II: A Damage-based Notch Strength Model, Composites Science and Technology, 39 (4). 303-326.
    • (1990) Composites Science and Technology , vol.39 , Issue.4 , pp. 303-326
    • Kortschot, M.T.1    Beaumont, P.W.R.2
  • 10
    • 0023420567 scopus 로고
    • A Progressive Damage Model for Laminated Composites Containing Stress Concentrations
    • Chang, F.K. and Chang, K.Y. (1987). A Progressive Damage Model for Laminated Composites Containing Stress Concentrations, Journal of Composite Materials, 21 (9). 834-855.
    • (1987) Journal of Composite Materials , vol.21 , Issue.9 , pp. 834-855
    • Chang, F.K.1    Chang, K.Y.2
  • 11
    • 0035089723 scopus 로고    scopus 로고
    • Progressive Failure Modelling on Notched Cross-ply Fibrous Composites
    • Kwon, Y.W. and Craugh, L.E. (2001). Progressive Failure Modelling on Notched Cross-ply Fibrous Composites, Applied Composite Materials, 8 (1). 63-74.
    • (2001) Applied Composite Materials , vol.8 , Issue.1 , pp. 63-74
    • Kwon, Y.W.1    Craugh, L.E.2
  • 12
    • 33745584881 scopus 로고    scopus 로고
    • Three-dimensional Modeling and Experimental Investigation of Damage Accumulation in Open Hole Composite Laminates
    • Iarve, E.V., Mollenhauer, D. and Kim, R. (2003). Three-dimensional Modeling and Experimental Investigation of Damage Accumulation in Open Hole Composite Laminates, ICCM14, San Diego.
    • (2003) ICCM14
    • Iarve, E.V.1    Mollenhauer, D.2    Kim, R.3
  • 13
    • 0027071524 scopus 로고
    • Interlaminar Interface Modelling for the Prediction of Delamination
    • Allix, O. and Ladeveze, P. (1992). Interlaminar Interface Modelling for the Prediction of Delamination, Composite Structures, 22 (4). 235-242.
    • (1992) Composite Structures , vol.22 , Issue.4 , pp. 235-242
    • Allix, O.1    Ladeveze, P.2
  • 14
    • 0035306458 scopus 로고    scopus 로고
    • Simulation of Delamination in Fiber Composites with Discrete Cohesive Failure Model
    • Borg, R., Nilsson, L. and Simonsson, K. (2001). Simulation of Delamination in Fiber Composites with Discrete Cohesive Failure Model, Composites Science and Technology, 61 (5). 667-677.
    • (2001) Composites Science and Technology , vol.61 , Issue.5 , pp. 667-677
    • Borg, R.1    Nilsson, L.2    Simonsson, K.3
  • 15
    • 0042527223 scopus 로고    scopus 로고
    • Numerical Simulation of Mixed-mode Progressive Delamination in Composite Materials
    • Camanho, P.P., Davila, C.G. and De Moura, M.F. (2003). Numerical Simulation of Mixed-mode Progressive Delamination in Composite Materials, Journal of Composite Materials, 37 (16). 1415-1437.
    • (2003) Journal of Composite Materials , vol.37 , Issue.16 , pp. 1415-1437
    • Camanho, P.P.1    Davila, C.G.2    De Moura, M.F.3
  • 16
    • 0348044416 scopus 로고    scopus 로고
    • Simulating DCB, ENF and MMB Experiments using Shell Elements and a Cohesive Zone Model
    • Borg, R., Nilsson, L. and Simonsson, K. (2004). Simulating DCB, ENF and MMB Experiments using Shell Elements and a Cohesive Zone Model, Composites Science and Technology, 64 (2). 269-278.
    • (2004) Composites Science and Technology , vol.64 , Issue.2 , pp. 269-278
    • Borg, R.1    Nilsson, L.2    Simonsson, K.3
  • 17
    • 0034322950 scopus 로고    scopus 로고
    • Modeling of Splitting and Delamination in Notched Cross-ply Laminates
    • Wisnom, M.R. and Chang, F.K. (2000). Modeling of Splitting and Delamination in Notched Cross-ply Laminates, Composites Science and Technology, 60 (15). 2849-2856.
    • (2000) Composites Science and Technology , vol.60 , Issue.15 , pp. 2849-2856
    • Wisnom, M.R.1    Chang, F.K.2
  • 19
    • 0031652610 scopus 로고    scopus 로고
    • Prediction of Delamination Initiation and Growth from Discontinuous Plies using Interface Elements
    • Petrossian, Z. and Wisnom, M.R. (1998). Prediction of Delamination Initiation and Growth from Discontinuous Plies using Interface Elements, Composites: Part A, 29 (5 - 6). 503-515.
    • (1998) Composites: Part A , vol.29 , Issue.5-6 , pp. 503-515
    • Petrossian, Z.1    Wisnom, M.R.2
  • 20
    • 0027150308 scopus 로고
    • Mode II Fracture of +/- Angled Laminate Interfaces
    • Shi, Y.B., Hull, D. and Price, J.N. (1993). Mode II Fracture of +/- Angled Laminate Interfaces, Composites Science and Technology, 47 (2). 173-184.
    • (1993) Composites Science and Technology , vol.47 , Issue.2 , pp. 173-184
    • Shi, Y.B.1    Hull, D.2    Price, J.N.3
  • 21
    • 0029232438 scopus 로고
    • The Effect of Fibre Rotation in ±45 degree Tension Tests on Measured Shear Properties
    • Wisnom, M.R. (1994). The Effect of Fibre Rotation in ±45 degree Tension Tests on Measured Shear Properties, Composites, 26 (1). 25-32.
    • (1994) Composites , vol.26 , Issue.1 , pp. 25-32
    • Wisnom, M.R.1
  • 22
    • 0028699132 scopus 로고
    • Initiation and Growth of Delamination from the Tips of Transverse Cracks in CFRP Cross-ply Laminates
    • Takeda, N. and Ogihara, S. (1994). Initiation and Growth of Delamination from the Tips of Transverse Cracks in CFRP Cross-ply Laminates, Composites Science and Technology, 52 (3). 309-318.
    • (1994) Composites Science and Technology , vol.52 , Issue.3 , pp. 309-318
    • Takeda, N.1    Ogihara, S.2
  • 23
    • 31344471467 scopus 로고    scopus 로고
    • Suppression of Delamination at Ply Drops in Tapered Composites by Ply Chamfering
    • Khan, B., Potter, K. and Wisnom, M.R. (2006). Suppression of Delamination at Ply Drops in Tapered Composites by Ply Chamfering, Journal of Composite Materials, 40 (2). 157-174.
    • (2006) Journal of Composite Materials , vol.40 , Issue.2 , pp. 157-174
    • Khan, B.1    Potter, K.2    Wisnom, M.R.3
  • 24
    • 0033885057 scopus 로고    scopus 로고
    • Stiffness Degradation in Cross-ply Laminates Damaged by Transverse Cracking and Splitting
    • Kashtalyan, M. and Soutis, C. (2000). Stiffness Degradation in Cross-ply Laminates Damaged by Transverse Cracking and Splitting, Composites: Part A, 31 (4). 335-351.
    • (2000) Composites: Part A , vol.31 , Issue.4 , pp. 335-351
    • Kashtalyan, M.1    Soutis, C.2


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.