The effect of in-situ noble metal chemical addition on crack growth rate behavior of structural materials in 288°C water

NACE - International Corrosion Conference Series

Volumn 1996-March, Issue , 1996, Pages

  Andresen, Peter L ^a   Angeliu, Tom ^a  

^a GE GLOBAL RESEARCH   (United States)

Author keywords

Boiling water reactors; Corrosion potential; Crack growth rate; Crack initiation; Electroless plating; High temperature water; In situ coating; Nickel alloys; Noble metal catalysis; Stainless steel; Stress corrosion cracking

Indexed keywords

BOILING WATER REACTORS; CATALYSIS; CRACK INITIATION; CRACK PROPAGATION; CRACKING (CHEMICAL); ELECTROCATALYSIS; ELECTROLESS PLATING; HIGH TEMPERATURE CORROSION; NICKEL ALLOYS; NICKEL COATINGS; OXIDANTS; PRECIOUS METALS; RESIDUAL STRESSES; STAINLESS STEEL; STEEL CORROSION; THERMAL SPRAYING;

BOILING WATER REACTOR (BWR); CATALYTIC RESPONSE; CORROSION POTENTIALS; HIGH-TEMPERATURE WATER; IN-SITU COATING; METAL CATALYSIS; OXIDANT CONCENTRATIONS; SYSTEM WIDE APPROACHES;

STRESS CORROSION CRACKING;

EID: 33745218826     PISSN: 03614409     EISSN: None     Source Type: Book Series    
DOI: None     Document Type: Conference Paper

References (17)

1. P.L. Andresen, "Modeling of Waterand Material Chemistry Effects on Crack Tip Chemistry and the Resulting Crack Growth Kinetics", Proc 3rd Int. Symp. on Environmental Degradation of Materais in Nuclear Power Systems-Water Reactors, AIME, p.301-312, 1988.
2. P.L. Andresen & F.P. Ford, "Life Prediction by Mechanistic Modeling & System Monitoring of Environmental Cracking of Fe & Ni Alloys in Aqueous Systems", Mat'Is Sci. and Eng. A103, p.167-184, 1988.
3. F.P. Ford & P.L. Andresen, "Development and Use of a Predictive Model of Crack Propagation in 304/316L, A533B/A508 and Inconel 600/182 alloys in 288°C Water", Proc. Third Int. Symp. on Degradation of Materials in Nuclear Power Systems-Water Reactors, AIME, p.789-800, 1988.
4. P.L. Andresen, "Irradiation Assisted Stress Corrosion Cracking", in Stress Corrosion Cracking: Materials Performance and Evaluation, Ed. R.H. Jones, ASM, p.l 81-210, 1992.
5. P.L. Andresen, F.P. Ford, S.M. Murphy & J.M. Perks, "State of Knowledge of Radiation Effects on Environmental Cracking in Light Water Reactor Core Materials", Proc. Fourth Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, NACE, p. 1-83 to 1-121, 1990
6. P.L. Andresen, "Fracture Mechanics Data & Modeling of Environmental Cracking of Nickel-Base Alloys in High Temperature Water", Corrosion Al, p. 917-938, December 1991.
7. B.M. Gordon, M.E. Indig, R.B. Davis, A.E. Pickett & C.W. Jewett, "Environmentally Assisted Cracking Resistance of BWR Structural Materials in Hydrogen Water Chemistry", Proc. 2nd Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, ANS, p.583-592, 1986.
8. P.L. Andresen, "Mitigation of Stress Corrosion Cracking By Underwater Thermal Spray Coating of Noble Metals". Paper #95412, Corrosion/95, NACE, 1995.
9. P.L. Andresen & Y.J. Kim, "Noble Metal Technology for BWRs", Int. Symp. on Plant Aging & Life Prediction of Corrodible Structures, Sapporo, Japan, May 1995.
10. P.L. Andresen, "Effect of Noble Metal Coating & Alloying on the Stress Corrosion Crack Growth Rate of Stainless Steel in 288°C Water", Proc. Sixth Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, AIME, 1994, p.245-253.
11. Y.J. Kim, L.W. Niedrach, M.E. Indig & P.L. Andresen, "Applications of Noble Metals in Coatings and Alloys for Light Water Reactors", Journal of Metals, Vol. 44, No. 2, p. 14-18, April 1992.
12. S. Hettiarachchi, G.P. Wozadlo & T.P. Diaz, "A Novel Approach for Noble Metal Exposition on Surfaces for IGSCC Mitigation in BWR Internals", Paper 95413, Corrosion/95, NACE, 1995.
13. P.L. Andresen, "The Effects of Aqueous Impurities on Intergranular Stress Corroision Cracking of Sensitized Type 304 Stainless Steel", NP-3384 Tl 15-3, EPRI, Palo Alto, 1983.
14. P.L. Andresen & CL. Briant, "Environmentally Assisted Crack Growth Response of Nonsensitized AISI 316L Grade Stainless Steels in High Temperature Water", Corrosion 44, p.450-460, 1988.
15. S. Hettiarachchi & T.P. Diaz, P.L. Andresen, Y.J. Kim & T.M. Angeliu, "Palhdium Additives for Control of Corrosion Potential & SCC in BWRs", Int. Symp. on Plant Aging & Life Prediction of Corrodible Structures Sapporo, Japan, May 15-18, 1995.
16. S. Hettiarachchi, G.P. Wozadlo, T.P. Diaz, P.L. Andresen and R.L Cowan, "The Concept of Noble Metal Addition Technology for IGSCC Mitigation of Nuclear Materials", Proc. Seventh Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, NACE, 1995.
17. P.L. Andresen and L.M. Young, "Characterization of the Roles of Electrochemistry, Convection and Crack Chemistry in Stress Corrosion Cracking", Proc. Seventh International Symposium on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, NACE, 1995.