Evaluation of the fracture research institute theoretical stress corrosion cracking model

Proceedings of the Twelfth International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors

Volumn , Issue , 2005, Pages 145-154

  Eason, Ernest D ^a   Pathania, Raj ^b   Shoji, Tetsuo ^c  

^a Modeling and Computing Services   (United States)

^b ELECTRIC POWER RESEARCH INSTITUTE   (United States)

^c TOHOKU UNIVERSITY   (Japan)

Author keywords

BWR; SCC; Stainless Steel; Stress Corrosion Cracking Model

Indexed keywords

CRACK GROWTH RATES (CGR); FRACTURE RESEARCH INSTITUTE (FRI); MATERIAL PROPERTIES; WELL-CONTROLLED LABORATORY DATA;

BOILING WATER REACTORS; COMPUTATIONAL COMPLEXITY; COMPUTER SIMULATION; CRACK PROPAGATION; ELECTROCHEMISTRY; LABORATORIES; STAINLESS STEEL; STRAIN RATE;

STRESS CORROSION CRACKING;

EID: 33745192601     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (18)

1. th Intl. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, Houston, TX: NACE International, Vol. 2., 1995, pp. 881-891.
2. J. Kwon, Q. Peng, and T. Shoji, "Development of Methodologies for the Quantitative Prediction of Environmentally Assisted Crack Growth Rate of Stainless Steels in High-Temperature Oxygenated Water," working paper, Fracture Research Institute, Tohoku University, 2001.
3. J. Kwon and Q. Peng, "Crack-Tip Strain Rate Approach to the Estimation of Stress-Corrosion Crack Growth - Theoretical Approach," presented at 2001 PEACE Program Annual Review Meeting, June 28-29, 2001, in "Reliability Centered Life Time Prediction of Environmentally Assisted Cracking," Fracture Research Institute Report URIPR-0101, Mar. 2001, pp. 103-109.
4. th Intl. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, LaGrange Park, 111: American Nuclear Society, Vol. 2., 1997, pp. 695-703.
5. F. P. Ford, "The Crack-Tip System and Its Relevance to the Prediction of Cracking in Aqueous Environments," Environment-Induced Cracking of Metals, Proceedings of the First International Conference, R. Gangloff and M. Ives, eds., NACE, Houston, TX, Vol. NACE-10, pp. 139-165, 1990.
6. W. W. Gerberich, D. L. Davidson, and M. Kaczorowski, "Experimental and Theoretical Strain Distributions for Stationary and Growing Cracks," J. Mech. Phys. Solids, Vol. 38, No. 1, pp. 87-113, 1990.
7. th International Conference on Fracture, Cannes France, Vol. 2, pp. 669-682, 1981.
8. E. D. Eason, "Evaluation of the Fracture Research Institute Theoretical Stress Corrosion Cracking Model," (EPRI Report 1008274, 2004).
9. E. Kikuchi, et al., "Intergranular Stress Corrosion Crack Growth of Sensitized Type 304 Stainless Steel in a Simulated Boiling Water Reactor Environment," Corrosion, Vol. 53, No. 4, 1997, pp. 306-311.
10. J. Kwon, Personal Communication, Fracture Research Institute, Tohoku University, Feb. 20, 2002.
11. P. L. Andresen and P. W. Emigh, "IGSCC Crack Propagation Rate Measurement in BWR Environments," Swedish Nuclear Power Inspectorate (SKi) Report 98:27, Appendix 3, ISSN 1104-1374, ISRN SKI-R-98/27-SE, Stockholm: SKi, 1999.
12. P. Lidar, "IGSCC Crack Propagation Rate Measurement in BWR Environments," Swedish Nuclear Power Inspectorate (SKi) Report 98:27, Appendix 4, ISSN 1104-1374, ISRN SKI-R-98/27-SE, Stockholm: SKi, 1999.
13. P. L. Andresen, K. Gott, and J. L. Nelson, "Stress Corrosion Cracking of Sensitized Type 304 Stainless Steel in 288C Water: A Five Laboratory Round Robin," Proc. 9th Int'l Symposium on Environmental Degradation of Materials in Nuclear Power Systems Water Reactors, Warrendale, PA: TMS, Aug. 2000, pp. 423-433.
14. P. L. Andresen, "IGSCC Crack Propagation Rate Measurements in BWR Environments: Executive Summary of a Round Robin Study," Swedish Nuclear Power Inspectorate (SKi), Report 98:27, ISSN 1104-1374, ISRN SKI-R-98/27-SE, Stockholm: SKi, 1999.
15. P. L. Andresen and P. Emigh, "Stress Corrosion Crack Growth Rate Measurements on Unsensitized Type 304 Stainless Steel in 288°C," EPRI Report TR-113489, Feb. 2000.
16. K. Pettersson, Personal Communication, July 9, 2002.
17. F. P. Ford, D. F. Taylor, P. L. Andresen, R. G. Ballinger, "Corrosion Assisted Cracking of Stainless Steel and Low Alloy Steels in LWR Environments," (EPRI Report NP5064S, Feb. 1987).
18. P. L. Andresen, L. M. Young, W. R. Catlin, and R. M. Horn, "Stress Corrosion Crack Growth Rate Behavior of Various Grades of Cold Worked Stainless Steel in High Temperature Water," Corrosion 2002 Paper 02511, 2002.