Observations and insights into Pb-assisted stress corrosion cracking of alloy 600 steam generator tubes

Proceedings of the Twelfth International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors

Volumn , Issue , 2005, Pages 1143-1154

  Thomas, Larry E ^a   Bruemmer, Stephen M ^a  

^a PACIFIC NORTHWEST NATIONAL LABORATORY   (United States)

Author keywords

Alloy 600; Intergranular stress corrosion cracking; PbSCC; Transmission electron microscopy

Indexed keywords

ALLOYING ELEMENTS; ANNEALING; GRAIN BOUNDARIES; LEAD; STEAM GENERATORS; STRESS CORROSION CRACKING; TRANSMISSION ELECTRON MICROSCOPY;

CORROSION FILMS; HIGH-TEMPERATURE-WATER SERVICE; INTERGRANULAR STRESS CORROSION CRACKING; PBSCC;

TUBES (COMPONENTS);

EID: 33745188221     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (15)

1. H.R. Copson and S.W. Dean, Corrosion 21 (1965), 1-8.
2. th Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (ANS, 1997) 216-223.
3. T. Sakai et al, Corrosion, 54, No. 7 (1998), 515-523.
4. Castaño-Marin, M.L., Gomez-Briceño, D., Hernandez-Arroyo, F., Proc. 6th Int. Conf. Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, ed. Gold, R.E. and Simonen, E.P., (IMS 1993) 189-196.
5. B. P. Miglin and J. M. Sarver, "Investigation of Lead as a Cause of Stress Corrosion Cracking at Support Plate Intersections," (Report EPRI NP-7367-S, Palo Alto, 1991).
6. M. Helie, I. Lambert and G. Santarini, 247-258. Proc. 7th Int. Conf. Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, ed. G. Airey et al., (NACE, Houston 1995) 247-258.
7. M.J. Psala-Dombrowski and F.H. Hua, Proc. 9th Int. Conf. Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, ed. F.P. Ford et al., (TMS, 1999) 703-710.
8. th Int. Conf. Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, ed. G. D. Cubicciotti, (NACE, Houston, 1990) 7/1-17.
9. R.W. Staehle and J.A. Gorman, Corrosion, 60, No.2 (2004) 115-180.
10. Thomas, L.E. and Bruemmer, S.M. (2004) Proc. 10th Int. Conf. Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, (NACE 2002) Paper 112.
11. L.E. Thomas and S. M. Bruemmer, "Summary of Analytical Electron Microscopy Observations of Intergranular Attack and Stress Corrosion Cracks in alloy 600 Steam Generator Tubing," EPRI Report 1011683, May 2005
12. L. E. Thomas and S. M. Bruemmer, Corrosion J., 2000, 56, 572.
13. Laire, C., Platbrood, G., and Stubbe, J., Proc. 7th Int. Conf. Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, ed. S.M. Bruemmer and A.R. McIlree, (TMS, 1995). 387-397.
14. International Centre for Diffraction Data, Newtown Square, PA.
15. L. E. Thomas, S. M. Bruemmer and P.M. Scott, pp. 1037-48 in Proc. Fontevraud V International Symposium: Contribution of Materials Investigation to the Resolution of Problems Encountered in Pressurized Water Reactors," SFEN, Paris, 2002.