Performance and thermal stability of Pt-modified Al-diffusion coatings for superalloys under cyclic and isothermal conditions

Materials at High Temperatures

Volumn 22, Issue 3-4, 2005, Pages 411-420

  Littner, A ^a   Pedraza, F ^b   Kennedy, A D ^b   Moretto, P ^c   Peichl, L ^c   Weber, T ^a   Schuetze, M ^a  

^a KARL WINNACKER INSTITUT   (Germany)

^b Carrigtwohill Co   (Ireland)

^c MTU AERO ENGINES GMBH   (Germany)

Author keywords

Oxidation protection; PtAl diffusion coatings; Superalloys

Indexed keywords

ALUMINUM; COMPOSITION; MICROSTRUCTURE; OPTICAL MICROSCOPY; OXIDATION; PLATINUM; SCANNING ELECTRON MICROSCOPY; SUPERALLOYS; THERMODYNAMIC STABILITY; X RAY DIFFRACTION ANALYSIS;

OXIDATION PROTECTION; PTAL-DIFFUSION COATINGS;

DIFFUSION COATINGS;

EID: 33745158957     PISSN: 09603409     EISSN: None     Source Type: Journal    
DOI: 10.1179/mht.2005.048     Document Type: Article

References (16)

1. Purvis, A.L. and Warnes, B.M. The effects of platinum concentration on the oxidation resistance of superalloys coated with single-phase platinum aluminide. Surf. Coat. Technol., 146-147, 1-6 (2001).
2. Angenete, J. and Stiller, K. A comparative study of two inward grown Pt modified Al diffusion coatings on a single crystal Ni base superalloy. Mater. Sci. Enging., A, 316, 182-194 (2001).
3. 3 on platinum-aluminum alloys. Oxidat. Met., 10, 189-223 (1976).
4. Zhang, Y., Lee, W.Y., Haynes, J.A., Wright, I.G., Pint, B.A., Cooley, K.M. and Liaw, P.K. Synthesis and cyclic oxidation behavior of a (Ni,Pt)Al coating on a desulfurized Ni-base superalloy. Metal. Trans., A30, 2679-2687 (1999).
5. Felten, E.J. Use of platinum and rhodium to improve oxide adherence on Ni-8Cr-6Al alloys. Oxidat. Met., 10, 23-28 (1976).
6. 3 as a Protective Scale. Oxidat.Met., 5, 341-345 (1976).
7. Gleeson, B., Wang, W., Hayashi, S. and Sordelet, D. Effects of platinum on the interdiffusion and oxidation behavior of Ni-Al based alloys. In: Steinmetz, P. et al. High Temperature Corrosion and Protection of Materials 6. TransTech Publ., Uetikon-Zuerich, 2004.
8. Yanar, N.M., Meier, G.H. and Pettit, F.S. The influence of platinum on the failure of EBPVD YSZTBCs on NiCoCrAlY bond coats. Scripta Mater., 46, 325-330 (2002).
9. Chen, J.H. and Little, J.A. Degradation of the platinum aluminide coating on CMSX4 at 1100°C. Surf. Coat. Technol., 92, 69-77 (1997).
10. Krishna, G.R., Das, D.K., Singh, V. and Joshi, S.V. Role of Pt content in the microstructural development and oxidation performance of Pt-aluminide coatings produced using a high activity aluminizing process. Mater. Sci. Enging., A251, 4047 (1998).
11. Pedraza, F. and Moretto, P. Investigation of the microstructure of platinum-modified aluminide coatings. Suf. Coat. Technol., (in press).
12. Tolpygo, V.K. and Clarke, D.R. Microstructural evidence for counter-diffusion of aluminium and oxygen during the growth of alumina scales. Mater. High Temp., 20, 261-271 (2003).
13. 3 on ss-NiAl. J. Electrochem. Soc., 127, 16301635 (1980).
14. 3 scales grown on beta-NiAl. Oxidat. Met., 47, 1-20 (1997).
15. Tolpygo, V.K. and Clarke, D.R. and surface rumpling of a (Ni,Pt)Al bond coat induced by cyclic oxidation. Acta Mater., 48, 3283-3293 (2000).
16. Littner, A. and Schuetze, M. The Cyclic Oxidation Behaviour of Several Aluminide and Platinum Aluminide Diffusion Coatings at 1150°C. Proc. Int. Conf. of Corrosion Science in the 21st Century, UMIST, Manchester, July 2003a.