Damage analysis for structural integrity and durability of composite materials

Fatigue and Fracture of Engineering Materials and Structures

Volumn 29, Issue 7, 2006, Pages 481-506

  Talreja, R ^a  

^a Texas AandM University   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

COMPOSITE MATERIALS; COMPRESSIVE STRENGTH; DURABILITY; FATIGUE OF MATERIALS; SERVICE LIFE; SHEAR STRENGTH; TENSILE STRENGTH; VISCOELASTICITY;

CYCLIC LOADING; DAMAGE ANALYSIS; FATIGUE LIFE PREDICTION; MECHANICAL BEHAVIOUR; MONOTONIC LOADING; STRUCTURAL INTEGRITY;

FRACTURE MECHANICS;

EID: 33745030306     PISSN: 8756758X     EISSN: 14602695     Source Type: Journal    
DOI: 10.1111/j.1460-2695.2006.00974.x     Document Type: Review

References (72)

1. Aveston, J., Cooper, G. A. and Kelly, A. (1971) Single and multiple fracture. The Properties of Fibre Composites, Conference Proceedings, IPC Science and Technology Press, Guilford, UK, pp. 15 -26.
2. Weibull, W. (1939) The phenomenon of rupture in solids. Proceedings of the Royal Swedish Institute for Engineering Research, No. 153, Stockholm, Sweden.
3. Daniels, H. E. (1945) The statistical theory of the strength of bundles and threads. Proc R. Soc. Lond. A183.
4. Rosen, B. W. (1964) Tensile failure of fibrous composites, Vol. 2, AIAA J. 1985 -1991.
5. Jones, R. M. (1999) Mechanics of Composite Materials. Taylor & Francis, Philadelphia, PA.
6. Argon, A. (1972) Fracture of composites. In: Treatise on Materials Science and Technology (Edited by H. Herman). Vol. 1, Academic Press, New York, London, pp. 79-114.
7. Phoenix, S. L. and Beyerlein, I. J. (2000) Statistical strength theory for fibrous composite materials. Comprehensive Composite Materials (Edited by T.-W. Chou). Chapter 1.19, Vol. 1, Elsevier Science, Pergamon, pp. 559-639.
8. Budiansky, B. (1983) Micromechanics. Comput. Struct. 16, 3-12.
9. Niu, K. and Talreja, R. (1999) Modeling of wrinkling in sandwich panels under compression. J. Engng Mech. 125, 875-883.
10. Slaughter, W. S. and Fleck, N. A. (1994) Microbuckling of fibre composites with random fibre waviness. J. Mech. Phys. Solids 42, 1743-1766.
11. Fleck, N. A., Deng, L. and Budiansky, B. (1995) Prediction of kink width in compressed fibre composites. J. Appl. Mech. 62, 329-337.
12. Fleck, N. A. (1997) Compressive failure of fibre composites. Adv. Appl. Mech. 33, 43-119.
13. O unidirectional CFRP laminates by fibre microbuckling. Compos. Sci. Technol. 59, 1451-1455.
14. Guz, I. A. and Soutis, C. (2001) Predicting fracture of layered composites caused by internal stability. Composites 32 A, 1243-1253.
15. Talreja, R. (1985) Transverse cracking and stiffness reduction in composite laminates. J. Comp. Maths 19, 355-375.
16. Gamstedt, E. K., Redon, O. and Br-øndsted, P. (2002) Fatigue dissipation and failure in unidirectional and angle-ply glass fibre/ carbon fibre hybrid Laminates. Key Engng Mater. 221-222 35-48.
17. Sun, C. T. (2000) Strength analysis of unidirectional composites and laminates, In: Comprehensive Composite Materials (Edited by T. -W. Chou). Chapter 1.20, Vol. 1, Elsevier Science, Pergamon.
18. Hart-Smith, L. J. (2000) Strength of unnotched laminates under multiaxial stress. Chapter 1.21, Vol. 1, (Edited by T. -W. Chou), Comprehensive Composite Materials Elsevier Science, Pergamon, pp. 667.
19. Hinton, M. J., Soden, P. D. and Kaddour, A. S. (1996) Strength of composite laminates under biaxial loads. Appl. Compos Mater. 3, 151-162.
20. Reddy, J. N. and Miravete, A. (1995) Practical Analysis of Composite Laminates. CRC Press, Boca Raton, FL.
21. Hashin, Z. (1980) Failure criteria for unidirectional composites. J. Appl. Mech. 47, 329-334.
22. Sørensen, B. F. and Talreja, R. (1993) Analysis of damage in a ceramic matrix composite. Int. J. Damage Mech. 2, 246-271.
23. Talreja, R. (1991) Continuum modelling of damage in ceramic matrix composites. Mech. Mater. 12, pp. 165-180.
24. Talreja, R. (1985) A continuum mechanics characterization of damage in composite materials. Proc. R. Soc. Lond. A399, 195-216.
25. Talreja, R. (1990) Internal variable damage mechanics of composite materials. In: Yielding, Damage and Failure of Anisotropic Solids (Edited by J. P. Boehler). Mechanical Engineering Publications, London, pp. 509-533.
26. Talreja, R. (1994) Damage characterization by internal variables. In: Damage Mechanics of Composite Materials (Edited by R. Talreja). Chapter 2, Elsevier Science, Amsterdam, pp. 53-78.
27. Talreja, R., (Ed.) (1994) Damage mechanics of composite materials. In: Composite Materials Series, Vol. 9, Elsevier Science, Amsterdam.
28. s laminates. Compos. Sci. Technol. 61, 657-665.
29. Varna, J., Krasnikovs, A., Kumar, R. S. and Talreja, R. (2004) A synergistic damage mechanics approach to viscoelastic response of cracked cross ply laminates. Int. J. Damage Mech. 13. 301-334.
30. s composite laminates. Part I: In-plane stiffness properties. Composites 23, 291-298.
31. s composite laminates. Part II: Development of transverse ply cracks. Composites 23, 299-304.
32. Kashtalyan, M. and Soutis, C. (2000) Stiffness degradation in cross-ply laminates damaged by transverse cracking and splitting. Composites 31A, 335-351.
33. Kashtalyan, M. and Soutis, C. (2000) The effect of delaminations induced by transverse cracking and splitting on stiffness properties of composite laminates. Composites 31A, 107-119.
34. Ladeveze, P. (1994) Inelastic strains and damage. In: Damage Mechanics of Composite Materials (Edited by R. Talreja). Chapter 4. Elsevier Science, Amsterdam, pp. 117-138.
35. Aveston, J. and Kelly, A. (1973) Theory of multiple fracture of fibrous composites. J. Mater. Sci. 8, 3520362.
36. Garrett, K. W. and Bailey, J. E. (1977) Multiple transverse fracture in 90° cross-ply laminates of glass fibre-reinforced polyester. J. Mater. Sci. 12, 157-168.
37. Hashin, Z. (1985) Analysis of cracked laminates: A variational approach. Mech. Mater. 4, 121-136.
38. Nairn, J. A. (2000) Matrix microcracking in composites. In: Comprehensive Composite Materials (Edited by R. Talreja and J. A. E. Månson) Chapter 2.12, Vol. 2, Elsevier Science, Pergamon, p. 403.
39. Nairn, J. A. and Hu, S. (1994) Matrix microcracking. In: Damage Mechanics of Composite Materials. (Edited by R. Talreja). Chapter 6. Elsevier Science, Amsterdam, pp. 187-243.
40. McCartney, L. N. (1996) Stress transfer mechanics for ply cracking in general symmetric laminates. NPL Report CMMT(A)50, National Physical Laboratory, Middlesex, UK.
41. McCartney, L. N. (1996) Generalised Framework for the Prediction of Ply Cracking in Any General Symmetric Laminate Subject to General In-Plane Loading. NPL Report CMMT(A)51, National Physical Laboratory, Middlesex, UK.
42. Wang, A. S. D. and Crossman, F. W. (1980) Initiation and growth of transverse cracks and edge delamination in composite laminates, Parts 1 and 2. J. Compos. Mater. Supplemental Volume 14, 71-106.
43. Budiansky, B., Hutchinson, J. W. and Evans, A. G. (1986) Matrix fracture in fibre-reinforced ceramics. J. Mech. Phys. Solids 34, 167-189.
44. Talreja, R. and Akshantala, N. V. (1998) An inadequacy in a common micromechanics approach to analysis of damage evolution in composites. Int. J. Damage Mech. 7, 238-249.
45. Talreja, R. (1981) Fatigue of composite materials: Damage mechanisms and fatigue life diagrams. Proc. R. Soc. Lond. 378A, 461-475.
46. Talreja, R. (1989) Fatigue of composites. In: Encyclopedia of Composite Materials (Edited by S. Lee). VCH Publishers, New York, pp. 483-488.
47. Talreja, R. (1989) Fatigue of composites. In: Concise Encyclopedia of Composite Materials (Edited by A. Kelly). Pergamon Press, Oxford, pp. 77-81.
48. Talreja, R. (1993) Fatigue of fibre composites. In Materials Science and Technology (Edited by T. W. Chou). Chapter 13, VCH Publishers, Weinheim, pp. 584-607.
49. Talreja, R. (2000) Fatigue of polymer matrix composites. In: Comprehensive Composite Materials. Vol. 2, Elsevier, Oxford, p. 529.
50. Talreja, R. (2003) Fatigue of composite materials. In: Modern Trends in Composite Laminates Mechanics (Edited by H. Altenbach and W. Becker). Springer, Vienna, pp. 281-294.
51. Talreja, R. (1987) Fatigue of Composite Materials. Technomic Publishing Co., Lancaster and Basel.
52. Degrieck, J. and Paepegem, W. V. (2001) Fatigue damage modelling of fibre-reinforced composite materials: Review. Appl. Mech. Rev. 54, 279-300.
53. Berthelot, J. -M. (2003) Transverse cracking and delamination in cross-ply glass-fibre and carbon-fibre reinforced plastic laminates: static and fatigue loading. Appl. Mech. Rev. 56, 111-147.
54. Charewicz, A. and Daniel, I. M. (1986) Damage mechanisms and accumulation in graphite/epoxy laminates. In: Composite materials: fatigue and Fracture (Edited by H. T. Hahn). ASTM STP 907, American Society for Testing and Materials, Philadelphia, pp. 274-297.
55. Ogihara, S. and Takeda, N. (1995) Interaction between transverse cracks and delamination during damage process in CFRP cross-ply laminates. Compos. Sci. Technol. 54, 395-404.
56. Dharani, L. R. and Tang, H. (1990) Micromechanics characterization of sublaminate damage. Int. J. Fract. Mech. 46, 123-140.
57. Kim, T. W., Kim, H. J. and Im, S. (1991) Delamination crack originating from transverse cracking in cross-ply laminates under extension. Int. J. Solids Struct. 27, 1925-1941.
58. Akshantala, N. V. and Talreja, R. (1998) A mechanistic model for fatigue damage evolution in composite laminates. Mech. Mater. 29, 123-140.
59. Akshantala, N. V. and Talreja, R. (2000) A micromechanics based model for predicting fatigue life of composite laminates. Mater. Sci. Engng A285, 303-313.
60. Christensen, R. M. (1982) Theory of Viscoelasticity, Dover Publications, New York.
61. Zocher, M. A., Allen, D. H. and Groves, S. E. (1997) Stress analysis of a matrix-cracked viscoelastic laminate. Int. J. Solids Struct. 34, 3235-3257.
62. Kumar, R. S. and Talreja, R. (2001) Linear viscoelastic behaviour of matrix cracked cross-ply laminates. Mech. Mater. 33, 139-154.
63. Schapery, R. A. (1996) Characterization of Nonlinear, Time-dependent Polymers and Polymeric Composites for Durability Analysis. In: Progress in Durability Analysis of Composite System (Edited by A. H. Cardon, H. Fukuda and K. Reifsnider). A. A. Balkema, Rotterdam, pp. 21-38.
64. Schapery, R. A. (1997) Nonlinear viscoelastic and viscoplastic constitutive equations based on thermodynamics. Mech. Time-Dependent Mater. 1, 209-240.
65. Abdel-Tawab, K. and Weitsman, Y. J. (1998) A coupled viscoelasticity/ damage model with application to swirl-mat composites. Int. J. Damage Mech. 7, 351-380.
66. Schapery, R. A. (1999) Nonlinear viscoelastic and viscoplastic constitutive equations with growing damage Int. J. Fract. 97, 33-66.
67. Kumar, R. S. and Talreja, R. (2003) A continuum damage model for linear viscoelastic composite materials. Mech. Mater. 35, 463-480.
68. Nemat-Nasser, S. and Hori, M. (1993) Micromechanics: Overall Properties of Heterogeneous Materials. North Holland, Amsterdam.
69. Needleman, A. (1987) A continuum model for void nucleation by inclusion debonding. J. Appl. Mech. 54, 525-531.
70. Needleman, A. (1992) Micromechanical modelling of interfacial decohesion. Ultramicroscopy 40, 203-214.
71. Jamison, R. D., Schulte, K., Reifsnider, K. L. and Stinchcomb, W. W. (1984) Characterization and analysis of damage mechanisms in tension-tension fatigue of graphite/epoxy laminates. In Effects of defects in Composite Materials, ASTM STP 836, American Society for Testing and Materials, Philadelphia, pp. 21-55.
72. Diao, X., Ye, L. and Mai, Y. -W. (1995) Simulation of Fatigue Performance of Cross-Ply Laminates. Appl. Compos. Mater. 3, 391-406.