Tensile behavior of corroded reinforcing steel bars BSt 500s

Construction and Building Materials

Volumn 20, Issue 9, 2006, Pages 782-789

  Apostolopoulos, Ch Alk ^a   Papadopoulos, M P ^a   Pantelakis, Sp G ^a  

^a UNIVERSITY OF PATRAS   (Greece)

Author keywords

Corrosion damage; Mass loss; Salt spray; Steel bars BSt 500s; Tensile property degradation

Indexed keywords

CORROSION; DUCTILITY; MECHANICAL PROPERTIES; REINFORCED CONCRETE; TENSILE STRENGTH;

CORROSION DAMAGE; MASS LOSS; SALT SPRAY; STEEL BARS BST 500S; TENSILE PROPERTY DEGRADATION;

STEEL;

EID: 33646898840     PISSN: 09500618     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.conbuildmat.2005.01.065     Document Type: Article

References (27)

1. Hellenic Regulation for the Technology of Steel in Reinforced Concrete; no. Δ14/36010-29.2/24.3.2000 (Government Gazette Issue) 381B.
2. Strategic High Research Program. Concrete and Structures; Progress and Product Update. Washington, DC: National Research Council; 1989.
3. Wallbank E.J. The performance of concrete in bridges (1989), HMSO, London
4. Manning D.G. Design life of concrete highway structures - The North American scene. Design Life Struct (1992) 144-153
5. Broomfield J.P. Corrosion of steel in concrete (1997), E & FN Spon, London p. 22
6. Papadakis VG. Supplementary cementing materials in concrete - activity, durability and planning. Danish Technological Institute Concrete Center, January; 1999.
7. Capozucca R. Damage to reinforcement concrete due to reinforcement corrosion. Construct Build Mater 9 5 (1995) 295-303
8. Diamond S.E. Chloride concentrations in concrete pore solutions resulting from calcium and sodium chloride admixtures. Cement Concrete Aggr 8 2 (1986) 97-102
9. Alvarez M.G., and Galvele J.R. The mechanisms of pitting of high purity iron in Nacl solutions. Corros Sci 24 (1984) 27-48
10. Maslehuddin M., Ibrahim I.M., Saricimen H., and Al-Mana A.l. Influence of atmospheric corrosion on the mechanical properties of reinforcing steel. Construct Build Mater 8 1 (1993) 35-41
11. Fang C., Lundgren K., Chen L., and Zhu C. Corrosion influence on bond in reinforced concrete. Cement Concrete Res (2004)
12. Borgard B, Warren C, Somayaji S, Heidersbach R. Mechanisms of corrosion of steel in concrete. ASTM STP 1065, Philadelphia; 1990. p. 174.
13. Thomas M.D.A., and Mathews J.D. Performance of pfa concrete in a marine environment - 10-year results. Cement Concrete Compos 26 (2004) 5-20
14. Yonezawa T., Ashworth V., and Procter R.P.M. Pore solution composition and chloride effects on the corrosion of steel in concrete. Corrosion 44 (1988) 489-499
15. Montemor M.F., Simoes A.M.P., and Salta M.M. Effect of fly ash on concrete reinforcement corrosion studied by EIS. Cement Concrete Compos 22 (2000) 175-185
16. Elsener B. Macrocell corrosion of steel in concrete - implications for corrosion monitoring. Cement Concrete Compos 24 (2002) 65-72
17. Arya C., and Vassie P.R.W. Influence of cathode-to-anode area ratio separation distance on galvanic corrosion currents of steel in concrete containing chlorides. Cement Concrete Res 25 (1995) 989-998
18. Almusallam A.A. Effect of degree of corrosion on the properties of reinforcing steel bars. Construct Build Mater 15 8 (2001) 361-368
19. Mpatis G, Rakanta E, Tsampras L, Mouyiakos S, Agnantiari G. Corrosion of steel used in concrete reinforcement, in various corrosive environments, Technical Chamber of Greece, 13th Hellenic Convention for Concrete. vol. II, Rethymnon, Crete; 1999. p. 497-505.
20. DIN 488-1, Reinforcing steel grades, properties, marking; 1986.
21. ELOT 971, Hellenic standard, weldable steels for the reinforcement of concrete, 1994-04-01.
22. DIN 488-3, Reinforcing steel bars testing; 1986.
23. ASTM B 117-94, Standard practice for operating salt (fog) testing apparatus. In: Annual book of ASTM standards, section 3, Metal test methods and analytical procedures, West Conshohocken, ASTM, Philadelphia, USA; 1995. p. 1-8.
24. Hellenic Anti-Seismic Code 2000 (EAK 2000).
25. ASTM G1 - 90, Standard practice for preparing, cleaning, and evaluating corrosion test specimens.
26. Sih G.C., and Chao C.K. Failure initiation in unnotched specimens subjected to monotonic and loading. Theor Appl Fract Mech 2 (1984) 67-73
27. Jeong D.Y., Orringen O., and Sih G.C. Strain energy density approach to stable crack extension under net section yielding of aircraft fuselage. Theor Appl Fract Mech 22 (1995) 127-137