Viscoelastic properties of wood treated by different reagents

Beijing Linye Daxue Xuebao/Journal of Beijing Forestry University

Volumn 28, Issue 1, 2006, Pages 88-92

  Jiang, Jia Li ^a   Lu, Jian Xiong ^a   Zhao, Guang Jie ^b  

^a RESEARCH INSTITUTE OF FORESTRY   (China)

^b BEIJING FORESTRY UNIVERSITY   (China)

Author keywords

Activation energy; Chinese fir; Dynamic viscoelastic properties; Loss modulus; Methylol groups; Storage modulus

Indexed keywords

ACTIVATION ENERGY; METHANOL; STRESS RELAXATION; VISCOELASTICITY;

CHINESE FIR; DYNAMIC VISCOELASTIC PROPERTIES; LOSS MODULUS; METHYLOL GROUPS; STORAGE MODULUS;

WOOD;

ACTIVATION ENERGY; METHANOL; STRESS RELAXATION; VISCOELASTICITY; WOOD;

EID: 33645646087     PISSN: 10001522     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (11)

1. WANG J Y, ZHAO G J. Gamma irradiation of compressed wood of Chinese fir[J]. Forest Studies in China, 2001, 3(1): 58-65.
2. TANG X S, ZHAO G J. Chemical stress relaxation of wood[J]. Journal of Beijing Forestry University, 2002, 24(1): 92-96.
3. OBATAYA E, YOKOYAMA M, NORIMOTO M. Mechanical and dielectric relaxations of wood in a low temperature range (I) - Relaxations due to methylol groups and adsorbed water[J]. Mokuzai Gakkaishi, 1996, 42(3): 243-249.
4. SUGIYAMA M, OBATAYA E, NORIMOTO M. Viscoelastic properties of the matrix substance of chemically treated wood[J]. Journal of Material Science, 1998, 33: 3505-3510.
5. EURUTA Y, OBATA Y, KANAYAM K. Thermal-softening properties of water-swollen wood: The ralaxation process due to water soluble polysaccharides[J]. Journal of Material Science, 2001, 36: 887-890.
6. HE M J, CHEN W X. Macromolecular physics[M]. Shanghai: Fudan University Publishing House, 2003.
7. ZHAO G J. Dielectric relaxation of water adsorbed on wood cell wall[M]. Beijing: China Forestry Publishing House, 2002.
8. YOKOYAMA M, OBATAYA E, NORIMOTO M. Mechanical and dielectric relaxations of wood in a low temperature range (II) - Relaxation due to adsorbed water[J]. Mokuzai Gakkaishi, 1999, 45(2): 95-102.
9. SUGIYAMA M, NORIMATO M. Temperature dependence of dynamic viscoelasticities of chemically treated woods[J]. Mohuzai Gakkaishi, 1996, 42(11): 1049-1056.
10. SATO S, SHIRAISHI N, SADOH T, et al. Setting of wood using cellulose and lignin-solvents[J]. Material, 1975, 24(264): 885-889.
11. AOKI T, YAMADA T. Creep of wood during decrystallization and of decrystallized wood[J]. Mokuzai Gakkaishi, 1977, 23(1): 10-16.