Durability of CFRP laminates under thermomechanical loading: A micro - Meso damage model

Composites Science and Technology

Volumn 66, Issue 7-8, 2006, Pages 983-992

  Lubineau, G ^a   Ladeveze P ^a   Violeau, D ^a  

^a SORBONNE UNIVERSITÉ   (France)

Author keywords

Fatigue; Microcracking; Micromechanics; Oxidation

Indexed keywords

COMPOSITE MICROMECHANICS; DEGRADATION; DURABILITY; FATIGUE OF MATERIALS; LAMINATED COMPOSITES; MATHEMATICAL MODELS; MICROCRACKING; OXIDATION; STRESSES;

STATIC LOADING; THERMOMECHANICAL LOADING;

CARBON FIBER REINFORCED PLASTICS;

CRACKING; DURABILITY; FATIGUE; FIBER REINFORCED COMPOSITE; LAMINATE; LOADING (TESTING); OXIDATION;

EID: 33644904054     PISSN: 02663538     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compscitech.2005.07.031     Document Type: Article

References (31)

1. A. Parvisi J. Bailey On multiple transverse cracking in glass-fiber epoxy cross-ply laminates J Mater Sci 13 1978 2131-2136
2. Highsmith A, Reifsnider K. Stiffness reduction mechanism in composite laminates. In: Reifsnider K, editor. Damage in composite materials. ASTM-STP 775; 1982. p. 103-117.
3. S. Tan R. Nuismer A theory for progressive matrix cracking in composites laminates J Comput Mater 23 1989 1029-1047
4. Ladevèze P. About a damage mechanics approach. In Baptiste D, editor. Mechanics and mechanisms of damage in composite and multimaterials. MEP; 1989. p. 119-142.
5. C. Herakovich Mechanics of fibrous composites 1998 Wiley New York
6. H. McManus D. Bowles S. Tompkins Prediction of thermal cycling induced matrix cracking J Reinforced Plastics Compos 15 1996 124-140
7. S. Kobayashi K. Terada S. Ogihara N. Takeda Damage-mechanics analysis of matrix cracking in cross-ply cfrp laminates under thermal fatigue Compos Sci Technol 61 2001 1735-1742
8. M. Lafarie-Frenot S. Rouquie Influence of oxidative environments on damage in c/epoxy laminates subjected to thermal fatigue Compos Sci Technol 64 2004 1725-1735
9. Ladevèze P. Multiscale computational damage modelling of laminate composites. Course CISM 2005.
10. G. Lubineau P. Ladevèze Towards a micromechanics-based damage mesomodel for CFRP laminates under thermomechanical cyclic loading Sci Eng Compos Mater 12 1-2 2004 71-82
11. P. Ladevèze G. Lubineau A computational mesodamage model for life prediction for laminates B. Harris Fatigue in composite materials: A review of the science and technology of the fatigue response of fibre-reinforced plastics 2003 Woodhead-Publishing 434-441
12. A. Wang P. Chou S. Lei A stochastic model for the growth of matrix cracks in composite laminates J Compos Mater 18 1984 239-254
13. Lafarie-Frenot M, Ho NQ. Influence of free edge intra-laminar stresses on damage process of CFRP laminates under thermal cycling conditions. J Compos Mater 2005 [accepted].
14. J. Nairn Matrix microcracking in composites R. Talreja J.-A. Manson Polymer matrix composites Comprehensive composite materials vol. 2 2000 Elsevier Amsterdam 403-432
15. J. Berthelot Transverse cracking and delamination in cross-ply glass-fiber and carbon-fiber reinforced plastic laminates: Static and fatigue loading Appl. Mech. Rev. 56 1 2003 1-37
16. P. Ladevèze E. LeDantec Damage modeling of the elementary ply for laminated composites Compos Sci Technol 43 3 1992 257-267
17. Ladevèze P, Lubineau G, Marsal D. Towards a bridge between the micro- and the mesomechanics of delamination for laminated composites. Compos Sci Technol 2005, in press.
18. Ladevèze P. A bridge between the micro- and mesomechanics of laminates: Fantasy or reality? ICTAM 2004 [to appear].
19. G. Dvorak N. Laws Analysis of progressive matrix cracking in composite laminates. Part 2: First ply failure J Compos Mater 21 1987 309-329
20. L. Boniface P. Smith M. Bader A. Rezaifard Transverse ply cracking in cross-ply cfrp laminates. initiation or propagation controlled J Compos Mater 31 11 1997 1080-1112
21. P. Ladevèze G. Lubineau On a damage mesomodel for laminates: micro-meso relationships possibilities and limits Compos Sci Technol 61 15 2001 2149-2158
22. P. Ladevèze G. Lubineau Relationships between "micro" and "meso" mechanics of laminated composites C. R. Mecanique 331 2003 537-544
23. J. Payan C. Hochard Damage modelling of laminated carbon/epoxy composites under static and fatigue loading Int J Fatigue 24 2002 299-306
24. L. Boniface S. Ogin Application of the paris equation to the fatigue growth of transverse ply cracks J Compos Mater 23 1989 735-754
25. J. Berthelot A.E. Mahi J.-F.L. Corre Development of transverse cracking in cross-ply laminates during fatigue tests Compos Sci Technol 61 2001 1711-1721
26. T. Yokozeki T. Aoki T. Ishikawa Fatigue growth of matrix cracks in the transverse direction of cfrp laminates Compos Sci Technol 62 2002 1223-1229
27. Z. Sun I. Daniel J. Luo Modeling of fatigue damage in a polymer matrix composite Mater Sci Eng A 361 2003 302-311
28. X. Colin C. Marais J. Verdu Kinetic modelling and simulation of gravimetric curves application to the oxidation of bismaleide and epoxy resins Polym Degradation Stability 78 2002 545-553
29. X. Colin C. Marais J. Verdu Kinetic modelling of the stabilizing effect of carbon fibres on thermal ageing of thermoset matrix composites Compos Sci Technol 65 2005 117-127
30. P. Ladevèze O. Loiseau D. Dureisseix A micro-macro and parrallel computational strategy for highly heterogeneous structures Int J Numer Meth Eng 52 2001 121-138
31. P. Ladevèze A. Nouy On a multiscale computational strategy with time and space homogenization for structural mechanics Comput Meth Appl Mech 192 2003 3061-3087