Influence of surface condition on the fatigue behaviour of specimens made of a SAE 5115 case-hardened steel

Fatigue and Fracture of Engineering Materials and Structures

Volumn 29, Issue 3, 2006, Pages 229-241

  Laue, S ^a   Bomas, Hubert ^b   Hoffmann, F ^b  

^a ROBERT BOSCH GMBH   (Germany)

^b STIFTUNG INSTITUT FÜR WERKSTOFFTECHNIK   (Germany)

Author keywords

Case hardened steel; Fracture mechanics approach; Internal oxidation; Shot peening; Surface oxidation; Weakest link concept

Indexed keywords

CASE HARDENING; CRACK INITIATION; CRACK PROPAGATION; CYCLIC LOADS; FAILURE (MECHANICAL); FRACTURE MECHANICS; INTERNAL OXIDATION; MICROSTRUCTURE; RESIDUAL STRESSES; STEEL; SURFACE ROUGHNESS; SURFACE STRUCTURE;

CASE-HARDENED STEEL; FATIGUE BEHAVIOUR; SURFACE CONDITION; WEAKEST-LINK CONCEPT;

FATIGUE OF MATERIALS;

EID: 33644792659     PISSN: 8756758X     EISSN: 14602695     Source Type: Journal    
DOI: 10.1111/j.1460-2695.2005.00984.x     Document Type: Article

References (33)

1. Kozlovskii I. S., Kalinin A. T., Novikova A. Y., Lebedeva E. A. and Feofanova A. I. (1967) Internal oxidation during case-hardening of steels in endothermic atmospheres. Met. Sci. Heat Treat. 3/4, 157-161.
2. Chatterjee-Fischer R. (1978) Internal oxidation during carburizing and heat treating. Metall. Trans. 9A, 1553-1560.
3. Verhoeven J. D., Chen N. and Bevolo A. J. (1992) A scanning auger microscopy characterization of the internal oxidation produced on carburizing. J. Heat Treat. 9, 73-80.
4. Lerche W., Lohrmann M., Edenhofer B., Gräfen W. and Bouwman J.W. (1998) Mikrostrukturelle Erscheinungen in der Randschicht einsatzgehärteter Bauteile. Mat.-wiss. u. Werkstofftech. 29, 679-685.
5. Laumen, C., Åström A. and Jonsson S. (1999) Untersuchung der Randoxidation nach dem Gasaufkohlen in mit Restsauerstoff verunreinigten Stickstoff-/Methanolatmosphären. Härterei-Techn. Mitt. 54, 15-20.
6. Lohrmann M. and Lerche W. (2000) Einfluss der Prozess- und Werkstoffauswahl auf das Randoxidationsausmaß bei der Gasaufkohlung. Härterei-Techn. Mitt. 55, 372-378.
7. Hoffmann R. and Vogel W. (2002) Randoxidation - Ursache, Ausmaß, Auswirkung. Härterei-Techn. Mitt. 57, 49-56.
8. Beumelburg W. (1970) Der Einfluss von Randoxidation auf die Umlaufbiegefestigkeit und statische Festigkeit einsatzgehärteter Proben. Härterei-Techn. Mitt. 25, 191-194.
9. Parrish H. G. (1976) The influence of microstructure on the properties of case-carburized components. Heat Treat. Met., pp. 6-12.
10. Cameron T. B., Diesburg D. E. and Kim C. (1983) Fatigue and overload fracture of carburized steels. J. Met. 7, 37-41.
11. Naito T., Ueda H. and Kikuchi M. (1984) Fatigue behavior of carburized steel with internal oxides and nonmartensitic microstructure near the surface. Metall. Trans. A 15A, 1431-1436.
12. Lyu, S.-K., Inoue K., Kato M., Onisi M. and Shimoda K. (1996) Effects of surface treatment on the bending fatigue strength of carburized spur gears. JSME Int. J. Ser. C 39, 108-114.
13. Löwisch G. (1994) Werkstoffkennwerte. Zuordnung von Werkstoffkennwerten zu Bauteileigenschaften von einsatzgehärteten und carbonitrierten Zahnrädern. Forschungsvereinigung Antriebstechnik, Heft 414, Frankfurt.
14. Melander A. and Preston S. (1992) Influence of surface microstructure on bending fatigue strength of carburized steels. Mater. Sci. Forum 102-104, 199-210.
15. Bomas H. and Schleicher M. (2005) Application of the weakest-link concept to the endurance limit of notched and multiaxially loaded specimens of the carburised steel 16MnCrS5. Fatigue Fract. Eng. Mater. Struct. 28, 983-995.
16. Bomas H., Mayr P. and Schleicher M. (1997) Calculation method for the fatigue limit of parts of case hardened steels. Mater. Sci. Eng. A234-236, 393-396.
17. EN 10084: Einsatzstähle - Technische Lieferbedingungen. Beuth, Berlin (1998).
18. Hirsch T., Wohlfahrt H. and Macherauch E. (1987) Fatigue strength of case hardened and shot peened gears. In: Shot Peening, Science, Technology, Application (Edited by H.Wohlfahrt, R. Kopp and O. Vöhringer), DGM Informationsgesellschaft, Oberursel, Germany, pp. 547-560.
19. DIN 3990, Teil 3 (1987) Tragfähigkeitsberechnung von Stirnrädern - Berechnung der Zahnfußtragfahigkeit, Beuth, Berlin.
20. Anzinger M. (1991) Werkstoff- und Fertigungseinflüsse auf die Zahnfußtragfähigkeit, insbesondere im hohen Zeitfestigkeitsgebiet. Forschungsvereinigung Antriebstechnik, Heft 335, Frankfurt.
21. DIN EN ISO 6507 Teil 1 (1998) Häarteprüfung nach Vickers; Prüfverfahren. Beuth, Berlin.
22. Krug T. and Laue S. (2002) Randschichtschädigung - Zahnfußfestigkeit, Forschungsvereinigung Antriebstechnik, Heft 669, Frankfurt.
23. 2 Ψ-Verfahren der röntgenographischen Spannungsmessung. Z. für angewandte Physik 13, 305-312.
24. Scholtes B. (1991) Eigenspannungen in mechanisch randschichtverformten Werkstoffzuständen. DGM Informationsgesellschaft, Oberursel.
25. Hänel B. and Wirthgen G. (1994) Festigkeitsnachweis. Forschungskuratorium Maschinenbau, Heft 183-2, Frankfurt.
26. Kim C., Diesburg D. E. and Eldis G. T. (1981) Effect of residual stress on fatigue fracture of case-hardened steels. Residual Stress Effects in Fatigue, ASTM Special Technical Publication 776, 224-234.
27. Newman J. C. and Raju I. S. (1986) Stress-intensity factors equations for cracks in three-dimensional finite bodies subjected to tension and bending loads. In: Computational Methods in the Mechanics of Fracture (Edited by S. N. Atluri). Elsevier North Holland, New York, NY.
28. WeibullW. (1949) A statistical representation of fatigue failures in solids. Transactions of the Royal Institute of Technology, Stockholm, Sweden, Number 27.
29. Heckel K. and Köhler J. (1975) Experimentelle Untersuchung des statistischen Größeneinflusses im Dauerschwingversuch an ungekerbten Stahlproben. Z. Werkstofftech. 6, 52-54.
30. Böhm J. and Heckel K. (1982) Die Vorhersage der Dauerschwingfestigkeit unter Berücksichtigung des statistischen Größeneinflusses. Z. Werkstofftech. 13, 120-128.
31. Bomas H., Linkewitz T. and Mayr P. (1999) Application of a weakest-link concept to the fatigue limit of the bearing steel SAE 52100 in a bainitic condition. Fatigue Fract. Eng. Mater. Struct. 22, 733-741.
32. Dang Van K., Griveau B. and Message O. (1989) On a new multiaxial fatigue criterion: Theory and application. In: Biaxial and Multiaxial Fatigue EGF 3 (Edited by M.W. Brown and K. J. Miller). Mechanical Engineering Publications, London, pp. 479-498.
33. Murakami Y. and Takahashi K. (1998) Torsional fatigue of a medium carbon steel containing an initial small surface crack introduced by tension-compression fatigue: Crack branching, non-propagation and fatigue limit. Fatigue Fract. Eng. Mater. Struct. 21, 1473-1484.