Failure initiation in an epoxy joint between two steel plates

European Journal of Mechanics, A/Solids

Volumn 22, Issue 4, 2003, Pages 509-524

  Leguillon, D ^a   Laurencin, J ^b   Dupeux, M ^b  

^a INSTITUT JEAN LE ROND D ALEMBERT   (France)

^b UNIV GRENOBLE ALPES   (France)

Author keywords

[No Author keywords available]

Indexed keywords

ASPECT RATIO; CRACK INITIATION; ELASTICITY; EPOXY RESINS; FAILURE (MECHANICAL); JOINTS (STRUCTURAL COMPONENTS); LOADS (FORCES); STEEL; TOUGHNESS;

EPOXY JOINTS; FAILURE INITIATION; LOAD BEARING CAPACITY; STEEL PLATES;

PLATES (STRUCTURAL COMPONENTS);

EID: 2942513537     PISSN: 09977538     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0997-7538(03)00066-4     Document Type: Article

References (31)

1. Akisanya A.R., Fleck N.A. Interfacial cracking from the free-edge of a long bi-material strip. Int. J. Solids Structures. 34:1997;1645-1665.
2. Akisanya A.R., Meng C.S. Initiation of fracture at the interface corner of a bi-material joint. J. Mech. Phys. Solids. 51:2003;27-46.
3. Atkinson C., Chen C.Y. The influence of layer thickness on the stress intensity factor of a crack lying in an elastic (viscoelastic) layer embedded in a different elastic (viscoelastic) medium (mode III analysis). Int. J. Engrg. Sci. 34:(6):1996;639-658.
4. Cao H.C., Evans A.G. An experimental study of fracture resistance of bimaterial interfaces. Mech. Mater. 7:1989;295-304.
5. Delale F., Erdogan F., Aydinoglu M.N. Stresses in adhesively bonded joints: a closed form solution. J. Comp. Mater. 15:1981;249-271.
6. Dundurs J. Effect of elastic constants on stress in a composite under plane deformation. J. Comp. Mater. 1:1967;310-322.
7. Dunn M.L., Suwito W., Cunningham S. Fracture initiation at sharp notches: correlation using critical stress intensities. Int. J. Solids Structures. 34:(29):1997;3873-3883.
8. Gilibert Y., Rigolot A. Analyse asymptotique des assemblages collés à double recouvrement sollicités au cisaillement en traction. J. Méc. Appl. 3:1979;341-372.
9. Gilibert, Y., Rigolot, A., 1985. Analyse théorique et expérimentale, dans le domaine élastique, d'un assemblage collé du type tenon-mortaise, Rapport de Recherche n°198, L.M.E. ENSTA, Paris, 1985.
10. Goland M., Reissner E. The stresses in cemented lap joints. J. Appl. Mech. 11:1944;A17-A27.
11. Hutchinson J.W., Mear M.E., Rice J.R. Crack paralleling an interface between dissimilar materials. J. Appl. Mech. 54:1987;828-832.
12. Labossiere P.E.W., Dunn M.L. Stress intensities at interface corners in anisotropic bimaterials. Engrg. Fract. Mech. 62:1999;555-575.
13. Laurencin, J., 2002. Amorçage et propagation d'une fissure à l'interface d'un bi-matériau, Mémoire d'ingénieur CNAM, Conservatoire National des Arts et Métiers, Grenoble, France.
14. Leguillon D. Strength or toughness? A criterion for crack onset at a notch. Eur. J. Mech. A Solids. 21:2002;61-72.
15. Leguillon D., Abdelmoula R. Mode III near and far fields for a crack lying in or along a joint. Int. J. Solids Structures. 37:2000;2651-2672.
16. Leguillon D., Sanchez-Palencia E. Computation of Singular Solutions in Elliptic Problems and Elasticity. 1987;Wiley, New York. Masson Paris.
17. Leguillon D., Siruguet K. Finite fracture mechanics - application to the onset of a crack at a bimaterial corner. Karihaloo B.L. Proceedings of the IUTAM Symp. on Analytical and Computational Fracture Mechanics of Non-Homogeneous Materials, Cardiff, UK, 18-22 June 2001. 2002;11-18 Kluwer Academic, Dordrecht.
18. Leguillon, D., Yosibash, Z., 2002. Crack onset at a v-notch. Influence of the notch tip radius. Submitted for publication.
19. Mohammed I., Liechti K.M. Cohesive zone modeling of crack nucleation at bimaterial corners. J. Mech. Phys. Solids. 48:2000;735-764.
20. O'Dowd N.P., Shih C.F., Stout M.G. Test geometries for measuring interfacial fracture toughness. Int. J. Solids Structures. 29:(5):1992;571-589.
21. O'Dowd N.P., Stout M.G., Shih C.F. Fracture toughness of alumina-niobium interfaces: experiments and analyses. Phil. Mag. A. 66:(6):1992;1037-1064.
22. Qian Z., Akisanya A.R. An experimental investigation of failure initiation in bonded joints. Acta Mater. 46:(14):1998;4895-4904.
23. Qian Z., Akisanya A.R., Thompson D.S. Stress behavior at the interface junction of an elastic inclusion. J. Appl. Mech. 69:2002;844-852.
24. Reedy E.D., Guess T.R. Comparison of butt tensile strength data with interface corner stress intensity factor prediction. Int. J. Solids Structures. 30:(21):1993;2929-2936.
25. Reedy E.D., Guess T.R. Interface corner failure analysis of joint strength: effect of adherend sitffness. Int. J. Fracture. 88:1997;305-314.
26. Reedy E.D., Guess T.R. Additional interface corner toughness data for an adhesively-bonded butt joint. Int. J. Fract. 98:1999;L3-L8.
27. Rice J.R. Elastic fracture mechanics concepts for interfacial cracks. J. Appl. Mech. 55:1988;98-103.
28. Rose L.R.F. Crack reinforcement by distributed springs. J. Mech. Phys. Solids. 34:1987;383-405.
29. Suo Z., Hutchinson J.W. Sandwich test specimens for measuring interface crack toughness. Mater. Sci. Engrg. A. 107:1989;135-143.
30. Wang J.S., Suo Z. Experimental determination of interfacial toughness curves using brazil-nut-sandwiches. Acta Metal. Mater. 38:1990;1279-1290.
31. Yosibash, Z., Bussiba, A., Gilad, I., 2002. Failure criteria for brittle elastic materials. Submitted for publication.