A coupled kinetic-constitutive approach to the study of high temperature crack initiation in single crystal nickel-base superalloys

Author keywords

Creep; Diffusion; Finite elements; Fracture; Nickel superalloy; Surface

Indexed keywords

CASTING; CRACKS; CREEP; DEFORMATION; DIFFUSION; FINITE ELEMENT METHOD; FRACTURE; HIGH TEMPERATURE EFFECTS; OXIDATION; PROBABILITY; RATE CONSTANTS; SINGLE CRYSTALS; SUPERALLOYS;

EID: 28944438277     PISSN: 00225096     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.jmps.2005.09.001     Document Type: Article
Times cited : (67)

References (35)
  • 1
    • 28944438210 scopus 로고    scopus 로고
    • Hibbitt, Karlsson and Sorensen Inc. Providence, RI, USA
    • ABAQUS, V.6.2.8, 2003. Hibbitt, Karlsson and Sorensen Inc. Providence, RI, USA.
    • (2003) ABAQUS, V.6.2.8
  • 2
    • 0020895305 scopus 로고
    • Micromechancis of crystals and polycrystals
    • R.J. Asaro Micromechancis of crystals and polycrystals Adv. Appl. Mech. 23 1983 1 115
    • (1983) Adv. Appl. Mech. , vol.23 , pp. 1-115
    • Asaro, R.J.1
  • 3
    • 2942720302 scopus 로고    scopus 로고
    • High temperature oxidation of single-crystal Ni-base superalloys
    • K. Bouhanek, D. Oquab, and B. Pieraggi High temperature oxidation of single-crystal Ni-base superalloys Mater. Sci. Forum 251-254 1997 33 40
    • (1997) Mater. Sci. Forum , vol.251-254 , pp. 33-40
    • Bouhanek, K.1    Oquab, D.2    Pieraggi, B.3
  • 4
    • 0033502253 scopus 로고    scopus 로고
    • The effect of constraint on creep fracture assessments
    • P.J. Budden, and R.A. Ainsworth The effect of constraint on creep fracture assessments Int. J. Fracture 97 1999 237 247
    • (1999) Int. J. Fracture , vol.97 , pp. 237-247
    • Budden, P.J.1    Ainsworth, R.A.2
  • 6
    • 0029734615 scopus 로고    scopus 로고
    • A dislocation mechanics-based crystallographic model of a B2-type intermetallic alloy
    • E.P. Busso, and F.A. McClintock A dislocation mechanics-based crystallographic model of a B2-type intermetallic alloy Int. J. Plasticity 12 1996 1 28
    • (1996) Int. J. Plasticity , vol.12 , pp. 1-28
    • Busso, E.P.1    McClintock, F.A.2
  • 7
    • 0034325423 scopus 로고    scopus 로고
    • Gradient-dependent deformation of two-phase single crystals
    • E.P. Busso, F. Meissonnier, and N.P. O'Dowd Gradient-dependent deformation of two-phase single crystals J. Mech. Phys. Solids 48 2000 2333 2361
    • (2000) J. Mech. Phys. Solids , vol.48 , pp. 2333-2361
    • Busso, E.P.1    Meissonnier, F.2    O'Dowd, N.P.3
  • 8
    • 0035947490 scopus 로고    scopus 로고
    • A mechanistic study of oxidation-induced degradation in a plasma-sprayed thermal barrier coating system. Part I: Model formulation
    • E.P. Busso, J. Lin, S. Sakurai, and M. Nakayama A mechanistic study of oxidation-induced degradation in a plasma-sprayed thermal barrier coating system. Part I: model formulation Acta Materialia 49 2001 1515 1528
    • (2001) Acta Materialia , vol.49 , pp. 1515-1528
    • Busso, E.P.1    Lin, J.2    Sakurai, S.3    Nakayama, M.4
  • 10
    • 0022436688 scopus 로고
    • Behaviour of thermal barrier coatings for advanced gas turbine blades
    • G.C. Chang, and W. Phucharoen Behaviour of thermal barrier coatings for advanced gas turbine blades Surf. Coat. Technol. 30 1987 13 28
    • (1987) Surf. Coat. Technol. , vol.30 , pp. 13-28
    • Chang, G.C.1    Phucharoen, W.2
  • 13
    • 0346896478 scopus 로고    scopus 로고
    • A multiscale approach for coupled phenomena in fcc materials at high temperatures
    • S. Dumoulin, E.P. Busso, and N.P. O'Dowd A multiscale approach for coupled phenomena in fcc materials at high temperatures Philos. Mag. 83 2003 3895 3916
    • (2003) Philos. Mag. , vol.83 , pp. 3895-3916
    • Dumoulin, S.1    Busso, E.P.2    O'Dowd, N.P.3
  • 14
    • 0027582922 scopus 로고
    • The isothermal-oxidation behaviour of several nickel-base single-crystal superalloys with and without coatings
    • M. Gobel, A. Rahmel, and M. Schutze The isothermal-oxidation behaviour of several nickel-base single-crystal superalloys with and without coatings Oxid. Met. 39 1993 231 261
    • (1993) Oxid. Met. , vol.39 , pp. 231-261
    • Gobel, M.1    Rahmel, A.2    Schutze, M.3
  • 15
    • 0346673602 scopus 로고    scopus 로고
    • Oxidation of the turbine blade material CMSX4 studied by X-ray diffraction
    • M. Gross, J. Goitia Bigordà, V. Koralic, and W. Engel Oxidation of the turbine blade material CMSX4 studied by X-ray diffraction J. Physique IV 8 1998 505 510
    • (1998) J. Physique IV , vol.8 , pp. 505-510
    • Gross, M.1    Goitia Bigordà, J.2    Koralic, V.3    Engel, W.4
  • 16
  • 18
    • 0025465413 scopus 로고
    • Fatigue crack propagation behaviour of a single crystal superalloy
    • B.A. Lerch, and S.D. Antolovich Fatigue crack propagation behaviour of a single crystal superalloy Metall. Trans. A 21A 1990 2169 2177
    • (1990) Metall. Trans. A , vol.21 , pp. 2169-2177
    • Lerch, B.A.1    Antolovich, S.D.2
  • 19
    • 0038607070 scopus 로고    scopus 로고
    • Oxidation behaviour of a single-crystal Ni-base superalloy in air. I: At 800 and 900°C
    • M.H. Li, X.F. Sun, J.G. Li, Z.Y. Zhang, T. Jin, and H.R. Guan Oxidation behaviour of a single-crystal Ni-base superalloy in air. I: at 800 and 900 ° C Oxid. Met. 59 2003 591 605
    • (2003) Oxid. Met. , vol.59 , pp. 591-605
    • Li, M.H.1    Sun, X.F.2    Li, J.G.3    Zhang, Z.Y.4    Jin, T.5    Guan, H.R.6
  • 20
    • 0035972129 scopus 로고    scopus 로고
    • Modelling and prediction of the stress rupture behaviour of single crystal superalloys
    • D.W. MacLachlan, and D.M. Knowles Modelling and prediction of the stress rupture behaviour of single crystal superalloys Mater. Sci. Eng. A 302 2001 275 285
    • (2001) Mater. Sci. Eng. , vol.302 , pp. 275-285
    • MacLachlan, D.W.1    Knowles, D.M.2
  • 21
  • 22
    • 0034744751 scopus 로고    scopus 로고
    • Finite element implementation of a generalised non-local rate dependent crystallographic formulation for finite strains
    • F. Meissonnier, E.P. Busso, and N.P. O'Dowd Finite element implementation of a generalised non-local rate dependent crystallographic formulation for finite strains Int. J. Plasticity 17 2001 601
    • (2001) Int. J. Plasticity , vol.17 , pp. 601
    • Meissonnier, F.1    Busso, E.P.2    O'Dowd, N.P.3
  • 23
    • 28944449132 scopus 로고
    • Solute transport during the cyclic oxidation of Ni-Cr-Al alloys
    • Nesbitt, J.A., 1982. Solute transport during the cyclic oxidation of Ni-Cr-Al alloys. NASA Contractor Report 165544.
    • (1982) NASA Contractor Report 165544
    • Nesbitt, J.A.1
  • 24
    • 0141818188 scopus 로고    scopus 로고
    • Probabilistic analysis of creep crack initiation and growth in pipe components
    • K.M. Nikbin, M. Yatomi, K. Wasmer, and G.A. Webster Probabilistic analysis of creep crack initiation and growth in pipe components Int. J. Pressure Vessels Piping 80 7-8 2003 585 595
    • (2003) Int. J. Pressure Vessels Piping , vol.80 , Issue.7-8 , pp. 585-595
    • Nikbin, K.M.1    Yatomi, M.2    Wasmer, K.3    Webster, G.A.4
  • 25
    • 0024736350 scopus 로고
    • Thermomechanical fatigue, oxidation, and creep: Part I: Damage mechanisms
    • R.W. Nue, and H. Sehitoglu Thermomechanical fatigue, oxidation, and creep: part I: damage mechanisms Metall. Trans. A 20A 1989 1755 1767
    • (1989) Metall. Trans. A , vol.20 , pp. 1755-1767
    • Nue, R.W.1    Sehitoglu, H.2
  • 26
  • 27
    • 0025465404 scopus 로고
    • Intrinsic stage i crack growth of directionally solidified Ni-base superalloys during low-cycle fatigue at elevated temperature
    • M.R. Okazaki, T. Tabata, and S. Nohmi Intrinsic stage I crack growth of directionally solidified Ni-base superalloys during low-cycle fatigue at elevated temperature Metall. Trans. A 21A 1990 2201 2208
    • (1990) Metall. Trans. A , vol.21 , pp. 2201-2208
    • Okazaki, M.R.1    Tabata, T.2    Nohmi, S.3
  • 28
    • 0020719659 scopus 로고
    • High temperature low cycle fatigue of MAR-M 509 superalloy II: The influence of oxidation at high temperatures
    • J. Reuchet, and L. Remy High temperature low cycle fatigue of MAR-M 509 superalloy II: the influence of oxidation at high temperatures Mater. Sci. Eng. 58 1983 33 42
    • (1983) Mater. Sci. Eng. , vol.58 , pp. 33-42
    • Reuchet, J.1    Remy, L.2
  • 30
    • 0019105728 scopus 로고
    • Tensile cracks in creeping solids
    • Am. Soc. Test. Mater
    • Riedel, H., Rice, J.R., 1980. Tensile cracks in creeping solids. ASTM STP 700. Am. Soc. Test. Mater. pp. 112-130.
    • (1980) ASTM STP , vol.700 , pp. 112-130
    • Riedel, H.1    Rice, J.R.2
  • 31
    • 0022020361 scopus 로고
    • On macroscopic and microscopic analyses for crack initiation and crack growth toughness in ductile alloys
    • R.O. Ritchie, and A.W. Thompson On macroscopic and microscopic analyses for crack initiation and crack growth toughness in ductile alloys Metall. Trans. A 16A 1985 236 248
    • (1985) Metall. Trans. A , vol.16 , pp. 236-248
    • Ritchie, R.O.1    Thompson, A.W.2
  • 32
    • 0036680292 scopus 로고    scopus 로고
    • Numerical investigation of residual stress fields and crack behaviour in TBC systems
    • K. Sfar, J. Aktaa, and D. Munz Numerical investigation of residual stress fields and crack behaviour in TBC systems Mater. Sci. Eng. A 333 2002 351 360
    • (2002) Mater. Sci. Eng. A , vol.333 , pp. 351-360
    • Sfar, K.1    Aktaa, J.2    Munz, D.3
  • 33
    • 85086516183 scopus 로고
    • Small-scale yielding analysis of mixed mode plane-strain crack problems
    • Am. Soc. Test. Mater
    • Shih, C.F., 1974. Small-scale yielding analysis of mixed mode plane-strain crack problems. ASTM STP 560. Am. Soc. Test. Mater. pp. 187-210.
    • (1974) ASTM STP , vol.560 , pp. 187-210
    • Shih, C.F.1
  • 34
    • 0037425395 scopus 로고    scopus 로고
    • Effect of thermal exposure on stress distribution in the TGO layer of EB-PVD TBC
    • T. Tomimatsu, S. Zhu, and Y. Kagawa Effect of thermal exposure on stress distribution in the TGO layer of EB-PVD TBC Acta Materialia 51 2003 2397 2405
    • (2003) Acta Materialia , vol.51 , pp. 2397-2405
    • Tomimatsu, T.1    Zhu, S.2    Kagawa, Y.3


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.