Corrosion fatigue phenomena learned from failure analysis

Engineering Failure Analysis

Volumn 13, Issue 3 SPEC. ISS., 2006, Pages 516-525

  Ebara, R ^a  

^a KAGAWA UNIVERSITY   (Japan)

Author keywords

Corrosion fatigue; Failure analysis; Ship hull structure; Steam turbine blade

Indexed keywords

CORROSION FATIGUE; CRACK INITIATION; CRACK PROPAGATION; FRACTURE; HULLS (SHIP); HYDROGEN; OIL TANKERS; STEAM TURBINES; TURBOMACHINE BLADES;

CORROSION PIT; SHIP HULL STRUCTURE; STEAM TURBINE BLADE;

FAILURE ANALYSIS;

CORROSION; FAILURE ANALYSIS; HULL;

EID: 28344446499     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfailanal.2004.12.024     Document Type: Article

References (24)

1. D.J. McAdam Jr. Proc ASTM 26 1926 224-254
2. H.J. Gough D.G. Sopwith J Inst Metals 49 1932 93-112
3. O.F. Devereux A.J. McEvily R. Staehle editors. Corrosion fatigue, chemistry, mechanics and engineering 1972 NACE
4. H.L. Craig Jr. T.W Crooker D.W. Hoeppner editors. Corrosion fatigue technology ASTM STP 642 1978 ASTM
5. Crooker TW, Leis BN. Corrosion fatigue, mechanics, metallurgy, electrochemistry and engineering, ASTP801; 1983.
6. K. Endo K. Komai Met Corr Fatig Strength Des 1982 [in Japanese]
7. Ebara R, Kai T, Mihara M, Kino H, Katayama K, Shiota K. Corrosion fatigue behavior of 13Cr stainless steel for turbine moving blades. In: Jaffee RI editor. Corrosion fatigue of steam turbine blade materials. New York: Pergamon Press; 1983. p. 4-150-4-167.
8. O. Jonas L.G. Bias Analyzing steam-turbine deposits Power 120 1976 26-29
9. EPRI. Corrosion fatigue of steam turbine-blading alloys in operational environments. CS-2932; 1984.
10. R. Ebara T. Yamada H. Kawano ISIJ Int 30 1990 535-539
11. R. Ebara T. Kai K. Inoue Corrosion-fatigue behavior of 13Cr stainless steel in sodium-chloride aqueous solution and steam environment. In: H.L. Craig Jr. T.W. Crooker D.W. Hoepnner editors. ASTM STP 642 1978 ASTM 155-166
12. R. Ebara T. Kai K. Inoue I. Masumoto Fractographic analysis of corrosion fatigue cracking of 13Cr stainless steel in NaCl aqueous solution 27 1978 64-68
13. R. Ebara Y. Yamada Availability of ultrasonic fatigue testing for evaluation of corrosion fatigue behavior of structural materials In: X.R. Wu Z.G. Editors. Wang Fatigue'99 4/4 1999 2323-2328
14. K. Iwamoto On the S-N curves of carbon steel under rotary bending condition in city water Trans JSME 30 1964 500-503
15. K. Endo K. Komai S. Kinoshita Long life corrosion fatigue strength under continuous and alternate immersion in 1% NaCl J Mater Sci Jpn 25 1976 894-898
16. K. Hirakawa I. Kitaura Corrosion fatigue of steel in sea water Sumitomo Search 26 1981 136-151
17. Yamanouchi H, Kino H, Ebara R. 82-JPGC-Pwr-18, ASME, p. 1-6.
18. Watanabe E. PhD Dissertation. Hiroshima University; 1998.
19. R. Ebara Y. Yamada A. Fushimi D. Sakai E. Watanabe H. Yajima J Soc Naval Achitect Jpn 173 1993 337-347
20. Y. Nakano S. Matsumoto E. Sugie H. Yajima R. Ebara E. Watanabe J Soc Naval Architect Jpn 174 1993 571-578
21. O. Vosikovsky Corrosion 32 1976 472-475
22. O. Vosikovsky A. Rivard Corrosion 38 1982 19-22
23. Ebara R, Yamada Y, Sakai D, Fushimi A, Yajima H. J Soc Mater Sci Jpn, No. 488, 1994;43:580-586.
24. Wei RP. In: Fong JT, editor. Fatigue mechanisms. ASTM STP 675; 1979. p. 816-31.