A comparison study of stress corrosion crack growth rates for AA7XXX alloys as a function of bulk aqueous chloride concentrations

Corrosion

Volumn 61, Issue 10, 2005, Pages 976-986

  Connolly, B J ^a   Koul, M G ^a   Moran, A L ^a  

^a UNITED STATES NAVAL ACADEMY   (United States)

Author keywords

Aluminum; Crack growth rate; Cracking; Environmentally assisted corrosion; Sodium chloride; Stress corrosion cracking

Indexed keywords

ALUMINUM ALLOYS; ALUMINUM CORROSION; COMPOSITION EFFECTS; CRACK PROPAGATION; ENVIRONMENTAL TESTING; MECHANICAL PROPERTIES; MECHANICAL TESTING; SODIUM CHLORIDE;

CRACK GROWTH RATES; ENVIRONMENTALLY ASSISTED CORROSION; OLD GENERATION MATERIALS;

STRESS CORROSION CRACKING;

ALUMINUM; ENVIRONMENTAL CORROSION; SALT; STRESS CORROSION CRACKING;

EID: 27844539387     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3280898     Document Type: Article

References (37)

1. W.H. Hunt, J.T. Staley, "High Strength Aluminum Alloys for Aerospace Applications," in Proc. Light Weight Alloys for Aerospace Applications Symp., held Feb. 28 - March 2 (Las Vegas, NV: 1989), p. 111-120.
2. R.J. Bucci, C.J. Warren, E.A. Starke, J. Aircraft 37, 1 (2000): p. 122.
3. Program Executive Office, Air ASW, Assault and Special Mission Programs, "Statement of Work: P-3C Service Life Assessment Program, Phases II and III, Rev. G," PMA-290, Department of the Navy, Naval Air Systems Command, 1998.
4. I. McCallum, S.S. Brown, J.R. Whitehead, T.H. Williams, "7150-T77511 Materials Qualification for the P-3 Service Life Extension Program," 12th AeroMat Conf. (Long Beach, CA: 2001).
5. D. Tenney, S.S. Brown, J.R. Whitehead, T.H. Williams, "7249-T76511 Materials Qualification for the P-3 Service Life Extension Program," 12th AeroMat Conf. (Long Beach, CA: 2001).
6. E. Colvin, S.S. Brown, J.R. Whitehead, T.H. Williams, "7055-T74511 and T76511 Materials Qualification for the P-3 Service Life Extension Program," 12th AeroMat Conf. (Long Beach, CA: 2001).
7. S.S. Brown, J.R. Whitehead, T.H. Williams, D.R. Tenney, "7055-T74511 Extruded Material Development for the P-3 Service Life Extension Program," 6th Joint FAA/DoD/NASA Aging Aircraft Conference (2002).
8. J.J. Thompson, E.S. Tankins, V.S. Agarwala, Mater. Perform. 26 (1987): p. 45.
9. E.A. Starke, J.T. Staley, Prog. Aerosp. Alloys 32 (1996): p. 131.
10. P. Sainfort, C. Sigli, G.M. Raynaud, P.H. Gomiero, Mater. Sci. Forum 242 (1997): p. 25.
11. Pechiney Aerospace Technical Data Sheet, Pechiney Rolled Products, ATI Division, Aerospace Department (April 2001).
12. ASTM G34-01, "Standard Test Method for Exfoliation Corrosion Susceptibility in 2XXX and 7XXX Series Aluminum Alloys (EXCO Test)," in Annual Book of ASTM Standards (West Conshohocken, PA: ASTM International, 1996).
13. ASTM G44-00, "Standard Practice for Exposure of Metals and Alloys by Alternate Immersion in Neutral 3.5% Sodium Chloride Solution," in Annual Book of ASTM Standards (West Conshohocken, PA: ASTM International, 1996).
14. C. Warren, "Alcoa 7150 Alloy, -T7751 Temper Plate, -T77511 Temper Extrusion," Alcoa Aerospace Engineering Division Technical Report, rev. no. 5, July 1996.
15. M. Speidel, M. Hyatt, Advances in Corrosion Science and Technology, vol. 2, eds. M. Fontana, R. Staehle (New York, NY: Plenum Press, 1979), p. 115.
16. ASTM E8-96a, "Standard Test Method for Tension Testing of Metallic Materials," in Annual Book of ASTM Standards (West Conshohocken, PA: ASTM International, 1996).
17. ASTM E1820-96, "Standard Test Method for Measurement of Fracture Toughness," in Annual Book of ASTM Standards (West Conshohocken, PA: ASTM International, 1996).
18. Military Handbook - MIL-HDBK-5H: Metallic Materials and Elements for Aerospace Vehicle Structures (Washington, DC: U.S. Department of Defense, 1998).
19. C.P. Ferrer, "Optimizing the Strength and SCC Resistance of Aluminum Alloys used for Refurbishing Aircraft," United States Naval Academy Trident Scholar Report no. 281, April 2001.
20. C.P. Ferrer, M.G. Koul, B.J. Connolly, A.L. Moran, Corrosion 59 (2003): p. 520.
21. ASTM G168-00, "Standard Practice for Making and Using Precracked Double Beam Stress Corrosion Specimens," in Annual Book of ASTM Standards (West Conshohocken, PA: ASTM International, 2000).
22. M.V. Hyatt, Corrosion 26 (1970): p. 487.
23. D.O. Sprowls, M.B. Shumaker, J.D. Walsh, J.W. Coursen, "Evaluation of Stress Corrosion Cracking Susceptibility Using Fracture Mechanics Techniques," NASA CR- 124469, NASA, May 13, 1973.
24. ISCC and da/dt Measurements for Aluminum Alloys Using Pre-Cracked Specimens," in Stress Corrosion Cracking: Science and Engineering, ASTM STP 1049, eds. W.B. Lisagor, T.W. Crooker, B.N. Leis (West Conshohocken, PA: ASTM International, 1990), p. 391-409.
25. ASTM 647-95a, "Standard Test Method for Measurement of Fatigue Crack Growth Rates," in Annual Book of ASTM Standards (West Conshohocken, PA: ASTM International, 1995).
26. J. Hatch, Aluminum: Properties and Physical Metallurgy (Materials Park, OH: ASM, 1983).
27. T. Ramgopal, P. Gouma, G. Frankel, Corrosion 58 (2002): p. 687.
28. T. Ramgopal, G.S. Frankel, Corrosion 57 (2001): p. 702.
29. T. Burleigh, Corrosion 47 (1991): p. 89.
30. K. Cooper, "Chemistry and Electrochemistry of Environment-Assisted Cracking of an Al-Zn-Mg-Cu Alloy" (Ph.D. diss. University of Virginia, 2001).
31. G. Koch, ASM Handbook (Materials Park, OH: ASM International, 1996).
32. L. Young, "Microstructural Dependence of Aqueous-Environment Assisted Crack Growth and Hydrogen Uptake in AA7050" (Ph.D. thesis, University of Virginia, 1999).
33. D. Sprowls, M. Shumaker, J. Walsh, J. Coursen, "Evaluation of Stress Corrosion Crack Susceptibility Using Fracture Mechanics Techniques," Alcoa Laboratories Final Report - Part I prepared for George C. Marshal Space Flight Center, Contract no. NAS 8-21487, May 31, 1973.
34. R. Dorward, K. Hasse, Corros. Sci. 19 (1979): p. 131.
35. Q. Meng, G. Frankel, J. Electrochem. Soc. 151 (2004): p. 271.
36. K. Deffenbaugh, "Environmentally Assisted Cracking Properties of AA7249 Extrusions for Aerospace Applications," United States Naval Academy Trident Scholar Report no. 304, April 2003.
37. A. Le, B. Brown, R. Foley, Corrosion 36 (1980): p. 673.