Failure analysis of a set of stainless steel disc springs

Engineering Failure Analysis

Volumn 13, Issue 2 SPEC. ISS., 2006, Pages 226-234

  Atxaga, G ^a   Pelayo, A ^a   Irisarri, A M ^a  

^a TECNALIA RESEARCH AND INNOVATION   (Spain)

Author keywords

Baking treatment; Hydrogen embrittlement; Pickling; Stainless steels

Indexed keywords

AGE HARDENING; CRACKS; DUCTILITY; FAILURE ANALYSIS; FRACTURE MECHANICS; HIGH TEMPERATURE EFFECTS; HYDROGEN EMBRITTLEMENT; MORPHOLOGY; SEAWATER EFFECTS; SPRINGS (COMPONENTS); STAINLESS STEEL; STRESS CORROSION CRACKING;

ACID PICKLING; BAKING TREATMENT; STAINLESS STEEL DISC SPRINGS;

STEEL STRUCTURES;

FRACTURE MECHANICS;

EID: 27744473437     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfailanal.2005.01.011     Document Type: Article

References (6)

1. S.P. Lynch Failures of structures and components by environmentally assisted cracking Eng Fail Anal 1 1994 77-90
2. Failure analysis and prevention. ASM handbook, vol. 11, ASM International; 1986.
3. S.P. Lynch Failures of engineering components due to environmentally assisted cracking Pract Fail Anal 3 5 2003 33-42
4. L. Raymond Evaluation of hydrogen embrittlement ASM handbook corrosion vol. 13 1987 p. 283-284
5. Glossary of Terms. ASM handbook. Corrosion, vol. 13, 1987. p. 1-14.
6. Metallurgy and properties of wrought stainless steels. Stainless Steels. ASM International; 1994. p. 34-35.