Control of the size for octahedral FePt nanoparticles and their magnetic properties

IEEE Transactions on Magnetics

Volumn 41, Issue 10, 2005, Pages 3373-3375

  Ito, Hirotaka ^a   Shima, Toshiyuki ^a   Takanashi, Koki ^a   Takahashi, Yukiko K ^b   Hono, Kazuhiro ^b  

^a TOHOKU UNIVERSITY   (Japan)

^b NATIONAL INSTITUTE FOR MATERIALS SCIENCE   (Japan)

Author keywords

FePt; L10 ordering; MgO; Octahedral nanoparticle; Sputtering

Indexed keywords

CRYSTAL STRUCTURE; DEPOSITION; MAGNESIA; MAGNETIC PROPERTIES; NANOSTRUCTURED MATERIALS; SINGLE CRYSTALS; SPUTTERING; X RAY DIFFRACTION ANALYSIS;

FEPT; L1O-ORDERING; MGO; OCTAHEDRAL NANOPARTICLES;

IRON COMPOUNDS;

EID: 27744448286     PISSN: 00189464     EISSN: None     Source Type: Journal    
DOI: 10.1109/TMAG.2005.855351     Document Type: Article

References (14)

1. M. H. Hong, K. Hono, and M. Watanabe, "Microstructure of FePt/Pt magnetic thin films with high perpendicular coercivity," J. Appl. Phys., vol. 84, pp. 4403-4409, 1998.
2. 0 ordering of off-stoichiometric FePt (001) thin films at reduced temparature," Appl. Phys. Lett., vol. 82, pp. 2461-2463, 2003.
3. S. Jeong, Y.-N. Hsu, D. E. Laughlin, and M. E. McHenry, "Atomic ordering and coercivity mechanism in FePt and CoPt polycrystalline thin films," IEEE Trans. Magn., vol. 37, no. 4, pp. 1299-1301, Jul 2001.
4. 0 ordering and microstructure of FePt thin films with Cu, Ag, and Au additive," J. Appl. Phys., vol. 92, pp. 6104-6109, 2002.
5. S. Sun, C. B. Murray, D. Weller, L. Folks, and A. Moser, "Monodisperse FePt nanoparticles and ferromagnetic FePt nanocrystal superlattices," Science, vol. 287, pp. 1989-1992, 2000.
6. 0 FePtAg nanoparticle arrays," J. Magn. Magn. Mater., vol. 266, pp. 49-56, 2003.
7. 2 granular thin film for high density magnetic recording," J. Appl. Phys., vol. 87, pp. 6941-6943, 2000.
8. Z. Zhang, K. Kang, and T. Suzuki, "Magnetic properties of granular-type FePt-MgO perpendicular recording media," IEEE Trans Magn., vol. 40, no. 4, pp. 2455-2457, Jul. 2004.
9. 0 structure produced by thermally created mass transport," IEEE Trans. Magn., vol. 39, no. 4, pp. 1925-1929, Jul. 2003.
10. 3 by ion beam synthesis: Annealing environment effects," J. Appl. Phys., vol. 95, pp. 8160-8166, 2004.
11. T. Shima, K. Takanashi, Y. K. Takahashi, and K. Hono, "Coercivity exceeding 100 kOe in epitaxially grown FePt sputtered films," Appl. Phys. Lett., vol. 85, pp. 2571-2573, 2004.
12. _, Fabrication of FePt nanoparticles with octahedral structure by thermal cycling process, submitted for publication.
13. 0 ordered FePt alloy by alternate monatomic layer deposition," Appl. Phys. Lett., vol. 80, pp. 288-290, 2002.
14. Y. K. Takahashi, T. Ohkubo, M. Ohnuma, and K. Hono, "Size effect on the ordering of FePt granular films," J. Appl. Phys., vol. 93, pp. 7166-7168, 2003.