Modeling the Trans-Varestraint test with finite element method

Author keywords

Driving force; Local strain; Material resistance; Trans Varestraint test; Weld solidification crack

Indexed keywords

CRACKS; FINITE ELEMENT METHOD; SOLIDIFICATION; STRAIN; WELDING;

EID: 27544504717     PISSN: 09270256     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.commatsci.2005.03.007     Document Type: Article
Times cited : (8)

References (14)
  • 3
    • 0000756710 scopus 로고
    • The Varestraint test
    • W.F. Savage, and C.D. Lundin The Varestraint test Weld. J. 10 1965 432 433
    • (1965) Weld. J. , vol.10 , pp. 432-433
    • Savage, W.F.1    Lundin, C.D.2
  • 4
    • 0343026165 scopus 로고
    • Fundamental investigations on solidification crack susceptibility for weld metals with Trans-Varestraint test
    • T. Senda, and F. Matsuda Fundamental investigations on solidification crack susceptibility for weld metals with Trans-Varestraint test Trans. Jpn. Weld. Soc. 2 2 1971 1 22
    • (1971) Trans. Jpn. Weld. Soc. , vol.2 , Issue.2 , pp. 1-22
    • Senda, T.1    Matsuda, F.2
  • 5
    • 0002056779 scopus 로고
    • Solidification crack susceptibility of aluminum alloy weld metals (report I)-characteristics of ductility curves during solidification by means of the Trans-Varestraint test
    • Y. Arata, and F. Matsuda Solidification crack susceptibility of aluminum alloy weld metals (report I)-characteristics of ductility curves during solidification by means of the Trans-Varestraint test Trans. JWRI 5 21 1976 53 67
    • (1976) Trans. JWRI , vol.5 , Issue.21 , pp. 53-67
    • Arata, Y.1    Matsuda, F.2
  • 6
    • 0008634225 scopus 로고
    • Solidification crack susceptibility in weld metals of fully austenitic stainless steels (Report III)-effect of strain rate on cracking threshold in weld metal during solidification
    • F. Matsuda, Y. Arata, and S. Katayama Solidification crack susceptibility in weld metals of fully austenitic stainless steels (Report III)-effect of strain rate on cracking threshold in weld metal during solidification Trans. JWRI 6 21 1977 197 207
    • (1977) Trans. JWRI , vol.6 , Issue.21 , pp. 197-207
    • Matsuda, F.1    Arata, Y.2    Katayama, S.3
  • 7
    • 0020797541 scopus 로고
    • Quantitative evaluation of solidification brittleness of weld metal during solidification by means of in situ observation and measurement
    • F. Matsuda, and H. Nakagawa Quantitative evaluation of solidification brittleness of weld metal during solidification by means of in situ observation and measurement Trans. JWRI 12 1 1983 65 72
    • (1983) Trans. JWRI , vol.12 , Issue.1 , pp. 65-72
    • Matsuda, F.1    Nakagawa, H.2
  • 8
    • 0021444557 scopus 로고
    • A new finite element model for welding heat sources
    • J. Goldak A new finite element model for welding heat sources Metall. Trans. B 15 1984 587 600
    • (1984) Metall. Trans. B , vol.15 , pp. 587-600
    • Goldak, J.1
  • 9
    • 0033900457 scopus 로고    scopus 로고
    • A hot-cracking mitigating technique for welding high strength aluminum alloy
    • Y. Yang A hot-cracking mitigating technique for welding high strength aluminum alloy Weld. J. 79 1 2000 9 17
    • (2000) Weld. J. , vol.79 , Issue.1 , pp. 9-17
    • Yang, Y.1
  • 10
    • 0029371520 scopus 로고
    • Computational analysis and prediction of weld-solidification cracking
    • W.P. Liu Computational analysis and prediction of weld-solidification cracking Comput. Mater. Sci. 4 1995 211 219
    • (1995) Comput. Mater. Sci. , vol.4 , pp. 211-219
    • Liu, W.P.1
  • 11
    • 0031272050 scopus 로고    scopus 로고
    • Thermal stress development in a nickel based superalloy during weldability test
    • Z. Feng, T. Zagharia, and S.A. David Thermal stress development in a nickel based superalloy during weldability test Weld. J. 76 11 1997 470 483
    • (1997) Weld. J. , vol.76 , Issue.11 , pp. 470-483
    • Feng, Z.1    Zagharia, T.2    David, S.A.3
  • 12
    • 0033221181 scopus 로고    scopus 로고
    • Development of the model for simulating weld metal solidification cracking in stainless steel
    • Y.H. Wei, and R.P. Liu Development of the model for simulating weld metal solidification cracking in stainless steel China Weld. 8 2 1999 135 140
    • (1999) China Weld. , vol.8 , Issue.2 , pp. 135-140
    • Wei, Y.H.1    Liu, R.P.2
  • 13
    • 0034187236 scopus 로고    scopus 로고
    • Stress/strain distributions for weld metal solidification crack in stainless steels
    • Y.H. Wei, and R.P. Liu Stress/strain distributions for weld metal solidification crack in stainless steels China Weld. 9 1 2000 36 41
    • (2000) China Weld. , vol.9 , Issue.1 , pp. 36-41
    • Wei, Y.H.1    Liu, R.P.2


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.