Cracks in a powder vibrating sieve disc

Engineering Failure Analysis

Volumn 13, Issue 1, 2006, Pages 32-43

  Asi, Osman ^a  

^a AFYON KOCATEPE UNIVERSITY   (Turkey)

Author keywords

Bolted joint; Failure analysis; Fretting fatigue; Surface coatings; Vibration

Indexed keywords

BOLTED JOINTS; COATINGS; CRACK INITIATION; CRACK PROPAGATION; FAILURE ANALYSIS; FATIGUE OF MATERIALS; FRACTURE; POWDERS; SIEVES; SILICON; VIBRATIONS (MECHANICAL); ZINC;

FRETTING FATIGUE; POWDER VIBRATING SIEVE DISC; STRUCTURAL STEEL; SURFACE COATINGS;

STEEL;

CRACK; FAILURE ANALYSIS; FRETTING WEAR;

EID: 27244436096     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfailanal.2004.12.034     Document Type: Article

References (13)

1. Failure analysis and prevention. ASM Handbook, vol. 11. Metals Park (OH): American Society for Metals; 1998.
2. Fatigue and fracture. ASM Handbook, vol. 19. Metals Park (OH): American Society for Metals; 1998.
3. K. Sato Damage formation during fretting fatigue Wear 125 1998 163-174
4. T.C. Lindley Fretting fatigue in engineering alloys Int J Fatigue 19 1 1997 S39-S49
5. P.C. Chan J.C. Thornley Common features of fretting-fatigue cracking in steels Practical Failure Anal, Am Soc Metals 2 6 2002 85-90
6. K. Endo H. Goto Initiation and propagation of fretting fatigue cracks Wear 38 1976 311-324
7. A.R. Marder The metallurgy of zinc-coated steel Progr Mater Sci 45 2000 1191-1271
8. A.R.B. Verma W.J. Ooij High-temperature batch hot-dip galvanizing. Part 1. General description of coatings formed at 560 °C Surface Coatings Technol 89 1997 132-142
9. E. Tzimas G. Papadimitriou Cracking mechanisms in high temperature hot-dip galvanized coatings Surface Coatings Technol 145 2001 176-185
10. R.I. Zadoks X. Yu An investigation of the self-loosening behavior of bolts under transverse vibration J Sound Vib 208 2 1997 189-209
11. W. Bickley The distribution of stress round a circular hole in plate Phil Trans Royal Soc Lond A227 1928 383-415
12. W. Barrois Repeated plastic deformation as a cause of mechanical surface damage in fatigue, wear, fretting-fatigue, and rolling fatigue Int J Fatigue 23 1979 167-189
13. H. Yan P.D. Zhong N.S. Xi C.H. Tao A case study of cracks in aeroengine compressor discs Eng Failure Anal 7 2000 181-188