Stress corrosion cracking of bainite 0.3C-1Cr-1Mn-1Si-1Ni type steel in acid rain simulated solution

Materials and Corrosion

Volumn 55, Issue 5, 2004, Pages 373-380

  Lunarska, E ^a   Nikiforow, K ^a   Sitko, E ^b  

^a INSTITUTE OF PHYSICAL CHEMISTRY   (Poland)

^b AIR FORCE INSTITUTE OF TECHNOLOGY   (Poland)

Author keywords

[No Author keywords available]

Indexed keywords

ACID RAIN; CARBON; COMPUTER SIMULATION; CORROSION RESISTANCE; DIFFUSION IN GASES; HYDROGEN EMBRITTLEMENT; MICROCRACKING; MICROSTRUCTURE; PH EFFECTS; PITTING; QUENCHING; SHOT PEENING; SOLUTIONS; STRESS CORROSION CRACKING;

BAINITE LATHS; CATHODIC POLARIZATION; MATERIAL STRENGTH; PITTING CORROSION;

BAINITE;

EID: 2642514021     PISSN: 09475117     EISSN: None     Source Type: Journal    
DOI: 10.1002/maco.200303747     Document Type: Article

References (34)

1. E. Lunarska, K. Nikiforow, O. Czerniajewa, E. Sitko, presented at Intern. Conf. Environmental Degradation of Engineering Materials - EDEM-99, Jurata-Gdansk, Poland, September 19-23, 1999, 334.
2. Z. Szklarska-Smialowska, Pitting Corrosion of Metals, NACE publ., Houston, 1986.
3. G. E. Kern, M. T. Wang, R. W. Staehle, Stress Corrosion cracking and hydrogen embrittlement of iron base alloys, NACE-5, Houston, 1977, 700.
4. P. McIntyre, Hydrogen Degradation of Ferrous Alloys, Noyes Publ., Park Ridge, 1985, 763.
5. I. M. Bernstein, G. M. Presouyre, Hydrogen Degradation of Ferrous Alloys, Noyes Publ., Park Ridge, 1985, 641.
6. B. E. Wilde, C. D. Kim, E. H. Phelps, Corrosion, 1980, 36, 625.
7. M. I. Luppo, J. Ovejero-Garcia, Corrosion Sci, 1991, 32, 1125.
8. P. Manolatos, C. Duret-Thual, J. Le Coze, M. Jerome, E. Bollinger, Corrosion Sci, 1995, 57, 1785.
9. P. G. Bailey, J. M. Whalen, Surface Engineering, Elsevier Applied Science, London, 1990, 379.
10. D. W. Hammond, S. A. Meguid, Surface Engineering, Elsevier Applied Science, London, 1990, 386.
11. E. Lunarska, O. Czerniajewa, A. Nakonieczny, Inzynierla Powierzchni, 2000, 22, 12.
12. C. L. Ho, S. L. I. Chan, J. Y. Lin, presented at 12th ICC, Houston, USA, 1993, 2367.
13. Acid rain'95 - Abstract Book, Kluwier Academic Publ, 1996, 461.
14. M. A. V. Devanathan, Z. Stachurski, J. Electrochemical Soc. 1964, 121, 619.
15. R. M. Barrer, Diffusion trough and in Solids, Univ. Press, Cambridge, 1941.
16. D. T. DeHoff, F. N. Rhines, Quantitative Microscopy. McGraw-Hill, New York, 1973.
17. L. Habraken, J.-L. de Brouwe, Fundamentals of Metallography, Presses Academiques Europeennes, Bruxelles, 1975.
18. J. O'M. Bockris, P. K. Subramanyan, J. Electrochem. Soc. 1971, 118, 1114.
19. J. O'M. Bockris, Stress Corrosion cracking and hydrogen embrittlement of iron base alloys, NACE-5, Houston, 1977, 286.
20. G. M. Pressouyre, I. M. Bernstein, Metall. Trans. 1978, 9A, 1571.
21. W. C. Luu, J. K. Wu, Corrosion Sci. 1996, 38, 239.
22. M. Iino, Acta metall. 1982, 30, 367.
23. J. Yao, J. R. Cahoon, Acta metall. 1991, 39, 119.
24. I. Dikiy, Intern J. Physicochemical Mechanics of Materials, 1981, 17, 108.
25. Z. Szklarska-Smialowska, presented at Polish-Japanese Symposium on Environmental Effects on High Technology Materials, Zakopane, Poland, October 12-16, 1997, 131.
26. C. S. Kortovich, E. A. Staigerwald, Engn. Fract. Mech. 1972, 4, 637.
27. L. Nannis, T. K. G. Namboodhiri, Stress Corrosion cracking and hydrogen embrittlement of iron base alloys, NACE-5, Houston, 1977, 432.
28. A.Turnbull, Material Science Forum 1995, 192-194, 63.
29. A. Turnbull, M. W. Carroll, D. H. Ferriss, Acta metall. 1989, 37, 2039.
30. G. M. Pressouyre, I. M. Bernstein, Acta metall. 1979, 27, 89.
31. B. G. Pound, Corrosion 1989, 45, 18.
32. B. Marandent, Stress Corrosion cracking and hydrogen embrittlement of iron base alloys, NACE-5, Houston, 1977, p. 774.
33. R. Ash, R. M. Barrer, D. G. PalmerP, Brit. J. Appl. Phys. 1965, 16, 873.
34. E. Lunarska, J. Michalski, Materials and Corrosion 2000, 51, 1.