Hydrogen embrittlement of a low carbon steel during slow strain testing in chloride solutions containing sulphate reducing bacteria

Materials Science and Technology

Volumn 21, Issue 9, 2005, Pages 1094-1098

  Singh Raman, R K ^a   Javaherdashti, R ^a   Panter, C ^a   Pereloma, E V ^a  

^a MONASH UNIVERSITY   (Australia)

Author keywords

Hydrogen embrittlement; Microbiologically induced corrosion; Slow strain rate testing; Sulphate reducing bacteria

Indexed keywords

BACTERIA; ELECTROCHEMISTRY; HYDROGEN EMBRITTLEMENT; MICROBIOLOGY; STRAIN CONTROL; STRAIN RATE; STRESS CORROSION CRACKING;

BIOTIC CONDITIONS; MICROBIOLOGICALLY INDUCED CORROSION; SLOW STRAIN RATE TESTING; SULFATE REDUCING BACTERIA;

CARBON STEEL;

EID: 25644446831     PISSN: 02670836     EISSN: None     Source Type: Journal    
DOI: 10.1179/174328405X51811     Document Type: Article

References (22)

1. H. A. Videla: Proc. Argentine-USA Workshop on Biodeterioration 7 (CONICET-NSF)', (ed. H. A. Videla), 43; 1986, Sao Paulo, Brazil, Aquatec Quimica.
2. S. W. Borenstein, Mater. Perform., 1988, 27, 62.
3. H. A. Videla: 'Manual of biocorrosion', 8 and 5; 1996, Boca Raton, FL, CRC Press.
4. E. Heitz: 'A working party report on microbiological degradation of materials and methods of protection', (ed. E. Heitz, A. D. Mercer, W. Sand and A. K. Tiller), 31; 1992, London, The Institute of Materials.
5. M. G. Fontana and N. D. Greene: 'Corrosion engineering'; 1984, Maidenhead, UK, McGraw-Hill.
6. R. K. Singh Raman, B. C. Muddle and B. W. Cherry: in 'Proc. 10th International Congress on Marine Corrosion and Biofouling', Melbourne, February 1999, (ed. J. Lewis), 229-236; 1999, DSTO, Aeronautical and Maritime Research Laboratory, DSTO-GD-0287.
7. F. Egan and G Clapp: Proc. Corrosion and Prevention 1998, Hobart, Paper 38-066, 1-6.
8. V. M. Linton, N. J. Laycock, S. J. Thomsen, S. Y. Ling and M. Sinathuraja: Proc. Int. Conf. of 'Failure analysis', Melbourne, November 2002, Institute of Materials Engineering of Australia, CD-ROM.
9. R. K. Singh Raman and B. C. Muddle: Mater. Sci. Technol., 2003, 19, 642-645.
10. R. K. Singh Raman and B. C. Muddle: Mater. Sci. Technol., 2003, 19, 1751-1754.
11. J. G. Stoecker: Mater. Perform., 1995, 34, 49.
12. S. W. Borenstein: Mater. Perform., 1991, 30, 52.
13. H. A. Videla: Biofouling, 2000, 15, 37.
14. J. F. D. Stott, B. S. Skerry and R. A. King: 'Laboratory evaluation of materials for resistance to anaerobic corrosion caused by sulphate reducing bacteria: philosophy and practical design, the use of synthetic environments for corrosion testing', ASTM STP 970, (ed. P. E. Francis and T. S. Lee), 98-111; 1988, Pittsburg, PA, ASTM.
15. R. Javaherdashti: Anti-Corros. Meth. Mater., 1999, 46(3), 173-180.
16. H. A. Videla: 'Manual of biocorrosion', 74-120; 1996, Boca Raton, CRC Press.
17. W. A. Hamilton: Ann. Rev. Microbiol, 1985, 39, 195-217.
18. R. Jeffrey and R. E. Melchers: Corros. Mgmt, May 2002, 3-11.
19. M. O. Spiedel and P. M. Fort, NACE-5, NACE Houston, 1977, 57-60.
20. R. N. Parkins, P. W. Slattery and B. S. Poulson: Corrosion - NACE, 1981, 37, 651.
21. D. Singbeil and D. Tromans: J. Electrochem. Soc.: Electrochem. Sci. Technol., 1981, 128, 2065.
22. H. H. Le and E. Ghali: J. Appl. Electrochem., 1992, 22, 396.