Fatigue of C/C composites in bending and in shear modes

Carbon

Volumn 42, Issue 8-9, 2004, Pages 1665-1670

  Tanabe, Yasuhiro ^a   Yoshimura, Takuya ^a   Watanabe, Tomoyuki ^a   Hiraoka, Toshiharu ^b   Ogita, Yasuhisa ^b   Yasuda, Eiichi ^a  

^a TOKYO INSTITUTE OF TECHNOLOGY   (Japan)

^b Toyo Tanso Co Ltd   (Japan)

Author keywords

A. Carbon composites; D. Fracture; Mechanical properties

Indexed keywords

BENDING (DEFORMATION); CRACK PROPAGATION; CRACKS; DEGRADATION; ELASTIC MODULI; FRACTURE; POLYCRYSTALLINE MATERIALS; WATER;

FATIGUE FRACTURE; SHEAR MODES;

CARBON CARBON COMPOSITES;

EID: 2542430519     PISSN: 00086223     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.carbon.2004.02.022     Document Type: Article

References (17)

1. Roy A.K. Tensile fatigue behavior of a coated two-dimensional carbon-carbon composite laminate. J. Compos. Technol. Res. 18:1996;202-208.
2. Mostafa I., Moet A. Effect of processing flaws on the fracture toughness of two-dimensional carbon-carbon composite. J. Mater. Sci. Lett. 15:1996;755-758.
3. Christel P.M., Meunier A., Leclercq S., Bouquet P., Buttazzoni B. Development of a carbon-carbon hip prosthesis. J. Biommed. Mater. Res. 21:1987;191-218.
4. Ozturk A., Moore R.E. Tensile fatigue behaviour of tightly woven carbon/carbon composites. Composites. 23:1992;39-46.
5. Mahfuz H., Maniruzzaman M., Krishnagopalan J., Hague A., Ismail M., Jeelani S. Effects of stress ratio on fatigue life of carbon-carbon composites. Theor. Appl. Fract. Mech. 24:1995;21-31.
6. Ozturk A. The influence of cyclic fatigue damage on the fracture toughness of carbon-carbon composites. J. Biomed. Mater. Res. 27A:1996;641-646.
7. Williams J.C., Yurgartis S.W., Moosbrugger J.C. Interlaminar shear fatigue damage evolution of 2-D carbon-carbon composites. J. Comp. Mater. 30(7):1996;785-799.
8. Fend T., Goering J. Strength and fatigue behavior of 2D-carbon/carbon composites under shear conditions. Ceram. Trans. 46:1994;165-176.
9. Goto K., Hatta H., Katsu D., Machida T. Tensile fatigue of a laminated carbon-carbon composite at room temperature. Carbon. 41:2003;1249-1255.
10. Sogabe T., Yoda S., Ioku I., Araki T., Oku T. Mechanism of delayed fracture of polycrystalline graphite. J. Soc. Mater. Sci. Jpn. 34:1985;1437-1440. [in Japanese].
11. Kobayashi H., Arai Y., Nakamura H., Araki T., Oku T. Evaluation of fracture mechanics characteristics of a high strength graphite IG-11. J. Soc. Mater. Sci. Jpn. 37:1988;934-938. [in Japanese].
12. Maruyama T, Nishimura Y. Effect of adsorbed gases on mechanical properties of nuclear graphite. TANSO 1992(152);1992:98-105 [in Japanese].
13. JUTEM (Japan ultra-high temperature material research center), A NEDO report on durability of super heat-resistant composites under ultra-high temperatures. NEDO, 1994:35-7 [in Japanese].
14. Ritchie R.O., Dauskardt R.H. Cyclic fatigue of ceramics. J. Ceram. Soc. Jpn. 99:1991;1047-1062.
15. Okazaki M., McEvily A.J., Tanaka T. On the mechanism of fatigue crack growth in silicon nitride. Metall. Trans. 22A:1991;1425-1426.
16. Kawakubo T., Goto A. Cyclic fatigue behavior of ceramics at room temperature. J. Soc. Mater. Sci. Jpn. 36:1987;1253-1258. [in Japanese].
17. Ueno A., Kishimoto H., Ookawara S., Kondo T., Yamamoto A. Crack propagation behavior of small crack of polycrystalline alumina and effects of cyclic load and grain size on bridging. J. Soc. Mater. Sci. Jpn. 43:1994;183-189. [in Japanese].