Anisotropic fracture behavior in ferroelectric relaxor PZN-4.5%PT single crystals

Journal of the American Ceramic Society

Volumn 88, Issue 7, 2005, Pages 1838-1844

  Oates, William S ^a   Lynch, Christopher S ^a,c   Kounga Njiwa, Alain B ^b   Lupascu, Doru C ^b,c  

^a GEORGIA INSTITUTE OF TECHNOLOGY   (United States)

^b DARMSTADT UNIVERSITY OF TECHNOLOGY   (Germany)

^c AMERICAN CERAMIC SOCIETY   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

ANISOTROPIC FRACTURE; CRACK TIP TOUGHNESS; ENERGY RELEASE; FERROELECTRIC RELAXORS;

ANISOTROPY; CRACKS; FRACTURE; FRACTURE TOUGHNESS; LEAD COMPOUNDS; SINGLE CRYSTALS;

FERROELECTRIC CERAMICS;

EID: 25144509000     PISSN: 00027820     EISSN: None     Source Type: Journal    
DOI: 10.1111/j.1551-2916.2005.00332.x     Document Type: Article

References (32)

1. R. M. McMeeking and A. G. Evans, "Mechanics of Transformation- Toughening in Brittle Materials," J. Am. Ceram. Soc., 65 [5] 242-6 (1981).
2. B. Budiansky, J. W. Hutchinson, and J. C. Lambropoulos, "Continuum Theory of Dilatant Transformation Toughening in Ceramics," Int. J. Solids Struct., 19 [4] 337-55 (1983).
3. S.-E. Park and T. R. Shrout, "Ultrahigh Strain and Piezoelectric Behavior in Relaxor Based Ferroelectric Single Crystals," J. Appl. Phys., 82 [4] 1804-11 (1997).
4. T. Liu and C. S. Lynch, "Ferroelectric Properties of [110], [001], and [111] Poled Relaxor Single Crystals: Measurements and Modeling," Acta Mater., 51, 407-16 (2003).
5. 3," Phys. Rev. B, 65, 224101-1-7 (2002).
6. F. Fang and W. Yang, "Indentation-Induced Cracking and 90° Domain Switching Pattern in Barium Titanate Ferroelectric Single Crystals Under Different Poling," Mater. Lett., 57, 198-202 (2002).
7. 3 Single Crystal Produced by Solution Bridgman Method," Jpn. J. Appl. Phys., 38 [9B] 5512-5 (1999).
8. 3 Crystal," Acta Mater., 49, 2993-9 (2001).
9. 3" Appl. Phys. Lett., 76 [25] 3732-4 (2000).
10. T. Liu, W. S. Dates, S. Wan, and C. S. Lynch, "Effect of Partial Electrodes on the Fracture of Ferroelectric Relaxor Single Crystal PZN-4.5%PT," J. Int. Mater. Systems Str., (2004) to appear.
11. 3 Single Crystals," J. Appl. Phys., 92 [1] 444-8 (2002).
12. J. Erhart and W. Cao, "Effective Material Properties in Twinned Ferroelectric Crystals," J. Appl. Phys., 86 [2] 1073-81 (1999).
13. G. C. Sih, P. C. Paris, and G. R. Irwin, "On Cracks in Rectilinearly Anisotropic Bodies," Int. J. Fract. Mech., 1, 189-203 (1965).
14. Z. Suo, C.-M. Kuo, D. M. Barnett, and J. R. Willis, "Fracture Mechanics for Piezoelectric Ceramics," J. Mech. Phys. Solids, 40 [4] 739-65 (1992).
15. J. Qu and Q. Li, "Interfacial Dislocation and its Application to Interface Crack in Anisotropic Bimaterials," J. Elasticity, 26, 167-95 (1991).
16. R. M. McMeeking, "The Energy Release Rate for a Griffith Crack in a Piezoelectric Material," Eng. Fract. Mech., 71 [7-8] 1169-83 (2003).
17. T.-Y. Zhang, M. Zhao, and P. Tong, "Fracture of Piezoelectric Ceramics," Adv. Appl. Mech., 38, 147-289 (2001).
18. T. C. T. Ting, Anisotropic Elasticity. Oxford University Press, New York, 1996.
19. R. Moon, K. Bowman, K. Trumble, and J. Rödel, "Comparison of R-Curves from Single-Edge V-Notched Beam (SEVNB) and Surface-Crack-in-Flexure (SCF) Fracture-Toughness Tests Methods on Multilayer Alumina-Zirconia Composites," J. Am. Ceram. Soc., 83 [2] 445-7 (2000).
20. M. Stech and J. Rödel, "Method for Measuring Short-Crack R-Curves Without Calibration Parameters: Case Studies on Alumina and Alumina/Aluminum Composites," J. Am. Ceram. Soc., 79 [2] 291-7 (1996).
21. T. Nishida, G. Pezzoti, T. Mangialardi, and A. E. Paolini, "Fracture Mechanics Evaluation of Ceramics by Stable Crack Propagation in Bend Bar Specimens," Fract. Mech. Ceram., 11, 107-14 (1996).
22. J. Kübler, "Fracture Toughness of Ceramics Using the SEVNB Method: Preliminary Results," Ceram. Eng. Sci. Proc., 18 [4] 155-62 (1997).
23. G. R. Anstis, P. Chantikul, B. R. Lawn, and D. B. Marshall, "A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness: I, Direct Crack Measurements," J. Am. Ceram. Soc., 64 [9] 533-8 (1981).
24. L. M. Braun, S. J. Bennison, and B. R. Lawn, "Objective Evaluation of Short-Crack Toughness Curves Using Indentation Flaws: Case Study on Alumina-Based Ceramics," J. Am. Ceram. Soc., 75 [11] 3049-57 (1992).
25. B. Lawn, Fracture of Brittle Solids, p. 378 Cambridge University Press, Cambridge, UK, 1975.
26. W. Chen, D. C. Lupascu, J. Rödel, and C. S. Lynch, "Short Crack R-curves in Ferroelectric and Electrostrictive PLZT," J. Am. Ceram. Soc., 84 [3] 593-7 (2001).
27. T. Karastamatis, D. C. Lupascu, S. L. Lucato, J. Rödel, and C. S. Lynch, "R-Curves of Lead Zirconate Titanate (PZT)," J. Eur. Ceram. Soc., 23, 1401-8 (2002).
28. J. Seidel and J. Rödel, "Measurement of Crack Tip Toughness in Alumina as a Function of Grain Size," J. Am. Ceram. Soc., 80 [2] 433-8 (1997).
29. J. E. Srawley and B. Gross, "Side-Cracked Plates Subject to Combined Direct and Bending Forces," ASTM, STP601, 559-79 (1976).
30. M. Creager and P. C. Paris, "Elastic Field Equations for Blunt Cracks with Reference to Stress Corrosion Cracking," Int. J. Fract., 3, 247-52 (1967).
31. A. N. Stroh, "Dislocations and Cracks in Anisotropic Elasticity," Phil. Mag., 7, 625-46 (1958).
32. T. Liu, Unpublished Data.